Perancangan Sistem Proteksi Katodik Anoda Korban Aluminium (SACP) Pada Pipa Baja Api 5l Grade B Dengan Variasi Coating Dan Penempatan Anoda Di Lingkungan Danau Statis

Gultom, Pernando (2023) Perancangan Sistem Proteksi Katodik Anoda Korban Aluminium (SACP) Pada Pipa Baja Api 5l Grade B Dengan Variasi Coating Dan Penempatan Anoda Di Lingkungan Danau Statis. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511940000072-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (9MB) | Request a copy

Abstract

Korosi merupakan degradasi material yang umum terjadi pada permukaan logam secara alami, peristiwa tersebut dipengaruhi oleh lingkungan dan pasti akan terjadi pada logam apabila pada kondisi memenuhi syarat terjadinya korosi. Korosi sering merusak peralatan di dunia industri yang dapat menyebabkan kerugian karena alat menjadi tidak bekerja dengan baik sebagaimana mestinya. Dalam menanggulangi peristiwa korosi tersebut, terdapat banyak metode yang dapat digunakan, salah satunya adalah metode SACP, metode tersebut menjadi topik dalam penelitian ini. Percobaan ini untuk menganalisis pengaruh anoda pada proteksi katodik berdasarkan penempatan anoda dan bagaimana pengaruh lapisan coating terhadap perlindungan korosi. Pada penelitian ini, dilakukan pengujian pada pipa dengan panjang 1,5 m dengan variasi coating (tanpa coating, coating primer, coating primer + sekunder) dan variasi penempatan anoda yaitu penempatan satu anoda ditengah pipa dan penempatan dua anoda pada pipa dengan jarak 0,5 m dari kedua ujung pipa. Pipa yang diuji memiliki luas permukaan sebesar 0,12576 m2 sehingga membutuhkan arus proteksi sebesar 0,00314175 A untuk pipa tanpa coating, dan 0,0009432 A untuk pipa dengan coating primer serta membutuhkan 0,0003458 A untuk memproteksi pipa dengan coating primer dan sekunder. Diketahui juga rata-rata potensial proteksi terukur sebesar – 696,13 mV sampai dengan – 665,15mV.
======================================================================================================================================
Corrosion is a common natural degradation of metals that occurs on the surface due to environmental factors and will inevitably happen to metals under certain conditions. Corrosion often damages equipment in the industrial world, leading to losses as the tools no longer function properly. In addressing this corrosion issue, there are many methods that can be used, one of which is the Sacrificial Anode Cathodic Protection (SACP) method, which is the topic of this research. The experiment aims to analyze the influence of anodes on cathodic protection based on the placement of the anode and the effect of coating layers on corrosion protection. In this research, testing was conducted on a 1.5-meter-long pipe with variations in coating (no coating, primer coating, primer + secondary coating) and variations in anode placement, either a single anode placed in the middle of the pipe or two anodes placed with a distance of 0,5 m from both ends of pipe. The tested pipe has a surface area of 0.12576 m2, requiring a protective current of 0.00314175 A for the uncoated pipe, 0.0009432 A for the pipe with primer coating, and 0.0003458 A to protect the pipe with primer and secondary coating. It is also known that the average measured protection potential ranges from -696.13 mV to -665.15 mV.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	SACP, Korosi, Potensial, Coating SACP, Corrosion, Potential, Coating.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Pernando Gultom
Date Deposited:	16 Aug 2023 03:28
Last Modified:	16 Aug 2023 03:28
URI:	http://repository.its.ac.id/id/eprint/100020