Analisis Pengaruh Penambahan Filler Nanoselulosa Terhadap Morfologi, Sifat Mekanik Dan Sifat Absorpsi Suara Pada Komposit Polypropylene Berpenguat Nanoselulosa

Perkasa, Nugraha Wahyu (2022) Analisis Pengaruh Penambahan Filler Nanoselulosa Terhadap Morfologi, Sifat Mekanik Dan Sifat Absorpsi Suara Pada Komposit Polypropylene Berpenguat Nanoselulosa. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000113-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (2MB) | Request a copy

Abstract

Penyerapan suara dapat didefinisikan sebagai ukuran jumlah energi yang dilepaskan dari gelombang suara saat gelombang tersebut melewati ketebalan pada suatu material tertentu. Penyerapan suara merupakan hal yang sangat penting dalam proses peredaman suara. Dalam penelitian kali ini bahan yang digunakan untuk menguji suatu peredaman suara berasal dari bahan serat alam dengan matriks Polypropylene. Salah satu cara untuk meningkatkan sifat mekanik pada komposit kayu dengan matriks Polypropylene yaitu dengan menambahkan filler nanoselulosa. Sehingga, penelitian ini dibuat bertujuan untuk menganalisis pengaruh penambahan filler nanoselulosa terhadap morfologi, sifat mekanik, sifat thermal, dan sifat absorpsi suara pada komposit bermatriks polypropylene dengan filler nanoselulosa. Variasi fraksi massa yang digunakan pada nanoselulosa sebesar 10%wt, 15%wt, dan 20%wt. Dalam pengujian yang dilakukan meliputi Pengujian Mikroskop Digital, Pengujian Absorbsi Suara (α), Pengujian Fourier Transform Infrared (FTIR), Pengujian Densitas, Pengujian Hardness dan Pengujian Flame Retardant. Hasil yang didapatkan dalam pengujian absorbsi suara, yang efisien untuk digunakan sebagai aplikasi otomotif jok mobil adalah penambahan 15% Nanoselulosa. Untuk hasil pengujian pada Flame Retardant dengan percobaan Polypropylene Murni didapatkan waktu pembakaran sebesar 198,6 detik. Pada hasil pengujian Hardness untuk tingkat kekerasan yang paling tinggi adalah PP2M yaitu sebesar 24,3 D. Pada hasil pengujian densitas untuk nilai porositas meningkat, namun, untuk nilai densitas nya menurun seiring dengan bertambahnya %Nanoselulosa pada sampel. Untuk nilai densitas yang paling tinggi adalah PP2M sebesar 0,8582 gr/cm3 dan terkecil adalah PP20N2M sebesar 0,8148 gr/cm3. Pengujian Absorbsi Suara dengan nilai (a) memiliki nilai koefisien serap suara yang paling tinggi adalah PP2M.

===================================================================================================================================

Sound absorption can be defined as a measure of the amount of energy released from sound waves when they pass through a certain thickness of a material. Sound absorption is very important in the sound suppression process. In this study, the material used to test a sound attenuation comes from natural fiber with a Polypropylene matrix. One way to improve the mechanical properties of wood composites with Polypropylene matrix is by adding nanocellulose filler. Thus, this study aimed to analyze the effect of adding nanocellulose filler to the morphology, mechanical properties, thermal properties, and sound absorption properties of the polypropylene matrix composite with nanocellulose filler. Variations in the mass fraction used in nanocellulose are 10% wt, 15% wt, and 20% wt. The tests carried out include Digital Microscope Testing, Sound Absorption Testing (α), Fourier Transform Infrared (FTIR) Testing, Density Testing, Hardness Testing and Flame Retardant Testing. The results obtained in the sound absorption test, which is efficient for use as an automotive car seat application, is the addition of 15% nanocellulose. For the test results on Flame Retardant with Pure Polypropylene experiments, the combustion time was 198.6 seconds. The Hardness test results for the highest hardness level is PP2M, which is 24.3 D. In the results of the density test, the porosity value increases, however, the density value decreases along with the increase in % nanocellulose in the sample. For the highest density value is PP2M of 0.8582 gr/cm3 and the smallest is PP20N2M of 0.8148 gr/cm3. Sound Absorption Test with a value or the highest sound absorption coefficient value is PP2M.

Keywords: Filler, Mechanical Properties, Nanocellulose, Polypropylene, Sound Absorption

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Absorpsi Suara,Filler,Nanoselulosa, Polypropylene, Sifat Mekanik, Filler, Mechanical Properties, Nanocellulose, Polypropylene, Sound Absorption
Subjects:	T Technology > TP Chemical technology > TP1140 Polymers
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Nugraha Wahyu Perkasa
Date Deposited:	30 Jul 2023 14:47
Last Modified:	30 Jul 2023 14:47
URI:	http://repository.its.ac.id/id/eprint/100543

Actions (login required)

View Item