Studi Eksperimental Pengaruh Ukuran Meshing Tempurung Kelapa pada Komposit Polypropylene Berpenguat Serat Sisal sebagai Pengganti ABS pada Cover Velg

Riandhani, Mirsha (2023) Studi Eksperimental Pengaruh Ukuran Meshing Tempurung Kelapa pada Komposit Polypropylene Berpenguat Serat Sisal sebagai Pengganti ABS pada Cover Velg. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111940000024-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (3MB) | Request a copy

Abstract

Inovasi dalam bidang otomotif terus berkembang khususnya pada material pembentuknya. Dewasa ini banyak digunakan material komposit alami yang mampu menghasilkan sifat spesifik sesuai kebutuhan dengan harga lebih murah. Penelitian ini menggunakan PP (polypropylene) sebagai matrik dan STK (Serbuk Tempurung Kelapa) sebagai reinforcement dengan penambahan serat sisal untuk membentuk sandwich dengan tujuan agar menjadi alternatif material pengganti plastik ABS (Acrylinotrile Butadiene Styrene). Studi eksperimen dilakukan dengan mencampur PP dan STK dengan variasi ukuran meshing 200-250, 250-300, dan 300-350 untuk membentuk plat komposit partikulat. Kemudian di antara dua plat komposit diberikan anyaman serat sisal dengan arah 90o. Pengujian dilakukan sesuai standar ASTM D638 untuk uji tarik dan ASTM D790 untuk uji bending. Penambahan STK pada komposit berpenguat serat sisal meningkatkan kekuatan tarik dan kekuatan bending dari polypropylene murni. Diperoleh hasil penambahan STK pada komposit berpenguat serat sisal tertinggi pada uji tarik adalah pada Variasi I dengan ukuran meshing 200-250 senilai 35,25 MPa dan modulus elastisitas tertinggi sebesar 2046,09 MPa pada Variasi III dengan ukuran meshing 300-350. Sedangkan, hasil kekuatan bending tertinggi terdapat pada Variasi III dengan ukuran meshing yaitu 201,51 MPa dan flexural modulus tertinggi diperoleh pada Variasi III atau ukuran meshing 300-350 dengan nilai 2854,29 MPa. Komposit STK berpenguat serat sisal berpotensi menggantikan plastik ABS sebagai aplikasi cover velg karena mechanical properties yang diperoleh telah sesuai dengan material cover velg yaitu plastik ABS.
=================================================================================================================================
Innovation in automotive is growing every day as well as its material. Nowadays, composite materials have been widely used, especially natural composite which are considered capable of producing specific properties required cheaper. This research use PP (polypropylene) as a matrix and CSP (Coconut Shell Powder) as reinforcement with additional of sisal fiber to form a sandwich. The goal is to be able to meet the specification of ABS (Acrylinotrile Butadiene Styrene) plastics so that it can be used as an alternative material to replace it. Experimental studies did by mixing PP and CSP with various meshing sizes of 200-250, 250-300, and 300-350 to form a particulate composite plate. Then between the two composite plates placed a 90o sisal fiber woven. The test is accorded to ASTM D638 standard for tensile test and ASTM D790 for bending test. The addition of CSP to sisal fiber reinforced composites increases the tensile strength and bending strength of pure polypropylene. The result of the addition of CSP to the sisal fiber reinforced composite in tensile test is in Variation I with a mesh size of 200-250 worth 35,25 MPa and the highest modulus of elasticity is 2046,09 MPa in Variation III with a mesh size of 300-350. Meanwhile, the highest bending strength results is found in Variation III with meshing size of 201,51 MPa and the highest flexural modulus is obtained in Variation III or meshing size of 200-250 with a value of 2854,29 MPa. The CSP composite reinforced with sisal fiber has the potential to replace ABS plastic as a cover velg application because the mechanical properties obtained are in accordance with the cover velg material which is ABS plastic.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Komposit, Polypropylene, Serat Sisal, Plastik ABS, Uji Tarik, Uji Bending, Composite, Sisal Fiber, ABS Plastic, Tensile Test, Bending Test
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Mirsha Riandhani
Date Deposited:	13 Sep 2023 07:51
Last Modified:	13 Sep 2023 07:51
URI:	http://repository.its.ac.id/id/eprint/104210

Actions (login required)

View Item