Pengaruh Loading Kobalt Terhadap Karakteristik Morfologi, Kristalinitas, dan Distribusi Kobalt Pada Katalis Co/γAl2O3 yang Disintesis Melalui Metode Impregnasi

Pradana, Revaldo Anugerah Putra (2023) Pengaruh Loading Kobalt Terhadap Karakteristik Morfologi, Kristalinitas, dan Distribusi Kobalt Pada Katalis Co/γAl2O3 yang Disintesis Melalui Metode Impregnasi. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211040000010-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (4MB) | Request a copy

Abstract

Katalis heterogen Co/γAl2O3 telah disintesis menggunakan metode impregnasi yang dilanjutkan dengan pengeringan dan kalsinasi. Co(NO3)2•6H2O digunakan sebagai prekursor logam dan γAl2O3 sebagai support.Variabel bebas yang diamati pada penelitian ini berupa %berat penambahan logam aktif Co sebesar 2,5%; 5,0%; 10,0%; 15,0%. Pengaruh loading kobalt pada karakteristik katalis dipelajari dengan menggunakan beberapa instrumen yaitu SEM-EDX, XRD, AAS dan XRF. Hasil analisis SEM menunjukkan variasi 2,5% Co/γAl2O3 memiliki distribusi kobalt paling merata dan tidak terdapat aglomerasi; 5,0% Co/γAl2O3 terdapat sedikit aglomerasi; 10,0% dan 15,0% teraglomerasi. Sedangkan jumlah unsur yang terkandung hasil analisis kuantifikasi kobalt pada karakterisasi SEM-EDX maping menunjukkan kenaikan pada variasi 5,0%-15,0% yang menunjukkan kepresisian seiring dengan kenaikan loading dan mengonfirmasi distribusi kobalt yang telah. Hasil analisis karakteristik katalis dengan XRD menunjukkan terdapat puncak-puncak difraktogram tajam yang menunjukkan sifat material yang kristalin. Puncak yang didapatkan pada 31,32; 36,88; 44,98; 59,50 dan 65,38 yang merupakan fasa CoAl2O4 dan Co3O4. Hasil karakterisasi AAS menunjukkan kenaikan massa kobalt yang terkandung dengan nilai regresi sebesar 0,9094 menunjukkan adanya kepresisian pada nilai kuantifikasi kobalt terdeteksi. Karakterisasi XRF menunjukkan peningkatan %berat seiring dengan peningkatan variasi loading hasil plotting menunjukkan nilai regresi sebesar 0,9722 yang berarti memiliki tingkat kepresisian tinggi. Hasil keseluruhan karakterisasi tersebut menunjukkan bahwa penambahan loading kobalt mempengaruhi jumlah kobalt yang terimpregnasi sebagai sisi aktif katalis beserta karakteristik seperti distribusi kobalt, morfologi, dan kristalinitas.
================================================================================================================================
The heterogeneous catalyst Co/γAl2O3 was synthesized using wetness impregnation method, followed by drying and calcination. The Co(NO3)2•6H2O was used as metal precursor and γAl2O3 was applied as catalyst support. The independent variables observed in this study were Cobalt loading of of 2.5 wt%; 5.0 wt%; 10.0 wt%; and 15.0 wt%. The effect of cobalt loading on the catalyst was studied through several instruments such as SEM-EDX, XRD, AAS and XRF. The SEM analysis showed that the 2.5% Co/γAl2O3 exhibited well distributed cobalt and the 5,0% Co/γAl2O3 demonstrated low agglomeration. The 10,0% Co/γAl2O3 and 15,0% Co/γAl2O3 showed many agglomerated cobalt particles. The cobalt quantification by SEM-EDX showed an increase of cobalt content with the incline of cobalt loading. XRD confirmed the presence of Alumina, CoAl2O4 and Co3O4 phases. Alumina was inferred by the peaks at 32,80; 37,50; 39,32; 45,90 dan 67,12. The peaks at 31.32; 36.88; 44.98; 59.50 and 65.38 inferred the availability of CoAl2O4 and Co3O4 phases. The results of the AAS characterization showed an increase in the mass of contained cobalt with a regression value of 0.9094, indicating precision in the quantification of detected cobalt. XRF characterization revealed an increase in weight percentage with increasing loading variations. The plotted results showed a regression value of 0.9722, indicating a high level of precision. The overall results of this characterization show that the addition of cobalt loading affects the amount of impregnated cobalt as the active side of the catalyst as well as its properties including cobalt distribution, morphology, and crystallinity.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Katalis Co/γAl2O3, Impregnasi, Karakterisasi, Impregenation, Characterization, Catalytic Activity
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Revaldo Anugerah Putra Pradana
Date Deposited:	23 Aug 2023 04:55
Last Modified:	23 Aug 2023 04:55
URI:	http://repository.its.ac.id/id/eprint/104424