Studi Eksperimental Sifat Mekanis Material Campuran Komposit Polyester Berpenguat Fiberglass dan Bilah Bambu sebagai Material Pengganti pada Kapal Katamaran 10GT

Ferdian, Muhammad Arsy Robi (2023) Studi Eksperimental Sifat Mekanis Material Campuran Komposit Polyester Berpenguat Fiberglass dan Bilah Bambu sebagai Material Pengganti pada Kapal Katamaran 10GT. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111940000006-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (3MB) | Request a copy

Abstract

Kapal ikan tradisional fiberglass reinforced plastics (FRP)10 GT dengan metode hand lay-up pada umumnya memiliki sifat mekanik yang rendah karena tidak sesuai dengan standar BKI yakni tensile strength 98 MPa dengan MOE 6,86 GPa dan bending strength 150 MPa dengan MOE 6,86 GPa. Sementara itu, banyaknya produksi kapal di Indonesia berdampak kepada permintaan atas fiberglass yang semakin tinggi. Penciptaan fiberglass yang besar besaran dapat menghasilkan emisi gas karbon yang dapat menjadi polusi udara yang pada akhirnya menyebabkan global warming. Sehingga pada penelitian ini dilakukan pergantian sebagian lapisan fiberglass dengan menggunakan lapisan bambu tipis yang dianyam twill dengan lebar 5mm yang bahannya lebih ramah lingkungan daripada fiberglass itu sendiri. Pengujian tarik dan bending pada spesimen komposit campuran fiberglass dan bilah bambu dilakukan untuk mengetahui apakah komposit sesuai dengan standar BKI untuk berlayar. Standar uji tarik yang digunakan pada penelitian ini yaitu ASTM D638 dan standar untuk uji bending yaitu ASTM D790. Hasil pengujian uji tarik pada bambu dengan proses alkalisasi dan tanpa alkalisasi dan didapatkan hasil 111,718MPa bambu tanpa alkalisasi dan 221,692MPa untuk bambu dengan alkalisasi. Bilah bambu dengan alkalisasi digunakan sebagai campuran lapisan spesimen. Eksperimen ini melakukan pengujian FRP hand lay-up dengan dan tanpa press untuk mengetahui metode yang terbaik. Hasil pengujian tarik dan bending untuk spesimen dengan press yaitu 221,856MPa dan 229,856MPa sedangkan tanpa press yaitu 112,227MPa dan 228,476. Kemudian dilakukan pengujian spesimen hybrid composite empat lapis dengan variasi salah satu lapisan fiberglass digantikan oleh anyaman bambu yaitu di bagian WR 800 dan CSM 450. Untuk variasi penggantian WR 800 sebesar 106,316 MPa, dan 166,234 Mpa, sedanggan untuk penggantian CSM 450 sebesar 118,806 MPa dan 62,451 Mpa. Pada eksperimen ini didapatkan komposisi hybrid composite yang dapat memenuhi standar BKI untuk kapal 10GT yakni variasi anyaman bambu yang menggantikan layer fiberglass yaitu WR800 pada komposit FRP dengan press.
=================================================================================================================================
Traditional fiberglass reinforced plastics (FRP) 10 GT fishing boats with the hand lay-up method generally have low mechanical properties because they do not comply with BKI standards, namely tensile strength 98 MPa with MOE 6.86 GPa and bending strength 150 MPa with MOE 6.86 GPa. Meanwhile, the large number of ship production in Indonesia has an impact on the higher demand for fiberglass. The creation of large fiberglass can produce carbon gas emissions which can become air pollution which ultimately causes global warming. So in this study, a partial replacement of the fiberglass layer was carried out using a thin layer of bamboo woven twill with a width of 5mm which is a more environmentally friendly material than fiberglass itself. Tensile and bending tests on composite specimens of a mixture of fiberglass and bamboo slats were carried out to determine whether the composite complied with BKI standards for sailing. The tensile test standard used in this study is ASTM D638 and the standard for bending test is ASTM D790. The results of the tensile test on bamboo with an alkalization process and without alkalization and the results obtained were 111.718MPa for bamboo without alkalization and 221.692MPa for bamboo with alkalization. The alkalized bamboo slats were used as mixed layer specimens. This experiment conducted hand lay-up FRP testing with and without press to determine the best method. The tensile and bending test results for specimens with press are 221.856MPa and 229.856MPa while without press are 112.227MPa and 228.476. Then testing four-layer hybrid composite specimens with variations of one of the fiberglass layers replaced by woven bamboo, namely in the WR 800 and CSM 450 parts. For the WR 800 replacement variation of 106.316 MPa, and 166.234 Mpa, while for the replacement of CSM 450 of 118.806 MPa and 62.451 Mpa. In this experiment, a hybrid composite composition that can meet the BKI standard for 10GT vessels is obtained, namely the variation of woven bamboo which replaces the fiberglass layer, namely WR800 in FRP composites with press.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Fiberglass Reinforced Plastic (FRP), Anyaman Bilah Bambu, Kapal Ikan, Woven Bamboo Blades, fishing boats
Subjects:	H Social Sciences > HD Industries. Land use. Labor > HD9999.C715-.C7154 Composite materials Q Science > QC Physics > QC173.4.C63 Composite materials T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Arsy Roby Ferdian
Date Deposited:	18 Sep 2023 01:52
Last Modified:	18 Sep 2023 01:52
URI:	http://repository.its.ac.id/id/eprint/104439

Actions (login required)

View Item