Sintesis dan Karakteristik Silika Mesopori Menggunakan Dual Cetakan P123-Gelatin Untuk Adorpsi Metilen biru

Safitri, Widiya Nur (2022) Sintesis dan Karakteristik Silika Mesopori Menggunakan Dual Cetakan P123-Gelatin Untuk Adorpsi Metilen biru. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6004201002-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2024. Download (4MB) | Request a copy

Abstract

Sintesis silika mesopori menggunakan dua kombinasi template P123 dan gelatin telah berhasil dilakukan dimana P123 menyebabkan terbentuknya silika mesopori dengan bentuk teratur, sedangkan gelatin berperan sebagai pore expander. Pada penelitian ini silika mesopori disintesis dengan metode sol-gel menggunakan prekusor TEOS dan katalis HCl pada suhu 100 °C selama 24 jam dengan variasi massa template P123:Gelatin 1:0; 1:0,2; 1:0,5; dan 1:1. Penerapan material silika mesopori pada penelitian ini adalah sebagai adsorben metilen biru. Silika mesopori hasil sintesis dikarakterisasi
menggunakan XRD, FTIR, SEM, EDX, adsorpsi-desorpsi N2 dan TEM. Hasil analisis XRD menunjukkan gundukan lebar pada 2θ sekitar 21-23,56° sebagai fase amorf. Spektrum FTIR menunjukkan puncak serapan pada bilangan gelombang 1082 dan 960 cm-1 untuk mode vibrasi Si-O-Si sebagai spektra karakteristik material silika mesopori. Morfologi dari SEM menunjukkan pembentukan rantai batang cacing dan lebih banyak
agregat seiring dengan peningkatan gelatin. Hasil TEM menunjukkan terbentuk struktur pori heksagonal. Sampel terbaik dalam penelitian ini adalah silika mesopori dengan rasio template 1:0,2 yang mempunyai luas permukaan sebesar 561,9 m2/g dengan diameter pori 10 nm. Silika mesopori 1:0,2 menunjukkan kapasitas adsorpsi sebesar 363,63 mg/g.
Adsorpsi metilen biru mengikuti kinetika orde dua semu dan model Langmuir. Desorpsi menggunakan aseton mencapai 81,4% dengan 4 kali penggunaan ulang.
=======================================================================================================================================
The synthesis of mesoporous silica using two combinations of templates between P123 and gelatin has been successfully carried out where P123 causes the formation of mesoporous silica with regular shape, while gelatin acts as a pore expander. In this study mesoporous silica was synthesized by the sol-gel method using TEOS as precursor and HCl catalyst at 100 ̊C for 24 hours using a mass variation of template P123: Gelatin 1:0; 1:0,2; 1:0.5; and 1:1. The application of mesoporous silica material in this study is as an adsorbent for methylene blue compounds. The synthesized mesoporous silica was characterized using XRD, FTIR, SEM, EDX, FTIR, N2 Adsorption-Desorption and TEM. XRD results show the peak of the board widening at 2θ around 21-23.56° as the amorphous phase. The FTIR spectrum shows absorption peaks at wave numbers 1100 and 950 cm-1 for the Si-O-Si vibrational mode as a characteristic spectra of mesoporous silica material. The morphology of the SEM showed the formation of rod chains and more aggregates with increasing gelatin. The TEM results showed a hexagonal structure was formed. The best sample in this study was mesoporous silica gelatin with a template ratio of 1:0.2 indicated by a surface area value of 561.9 m2 /g with a pore diameter of 10 nm. Mesoporous silica 1:0.2 showed an adsorption capacity of 363.63 mg/g. The adsorption of methylene blue followed pseudo-second-order kinetics and the Langmuir model. Desorption using acetone reached 84.3% with 4 times reusability.

Item Type:	Thesis (Masters)
Additional Information:	RTKi 546.683 Saf s-1 2022
Uncontrolled Keywords:	Gelatin, P123, silika mesopori, template, adsorpsi, metilen biru, mesoporous silica, template, adsorption, methylene blue
Subjects:	Q Science > QC Physics > QC585.75.S55 Silica
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	- Davi Wah
Date Deposited:	18 Oct 2023 08:17
Last Modified:	18 Oct 2023 08:17
URI:	http://repository.its.ac.id/id/eprint/104903

Actions (login required)

View Item