Modifikasi Elektroda Kerja Emas Dengan Polianilin - Enzim Invertase - Partikel Nano Emas Sebagai Biosensor Sukrosa

Fitriyana, Fitriyana (2014) Modifikasi Elektroda Kerja Emas Dengan Polianilin - Enzim Invertase - Partikel Nano Emas Sebagai Biosensor Sukrosa. Masters thesis, Insititut Teknologi Sepuluh Nopember.

Text 1410201004_Master_Thesis.pdf Download (2MB)

Abstract

Elekroda kerja emas telah dimodifikasi dengan polianilin, enzim invertase dan partikel nano emas dan diujikan pada larutan sukrosa. Modifikasi elektroda emas dengan polianilin (PANI) dan enzim invertase dilakukan dengan teknik voltammetri siklik menggunakan potensiostat, sedangkan pengendapan partikel nano emas pada permukaannya dilakukan dengan teknik lapis demi lapis. Permukaan elektroda termodifikasi diamati perubahannya menggunakan mikroskop optik. Elektroda termodifikasi kemudian digunakan untuk mendeteksi sukrosa dengan teknik voltammetri siklik dalam larutan buffer fosfat pada pH 6,78. Respon arus oksidasi pada potensial 328 mV merupakan arus oksidasi glukosa sebagai hasil hidrolisis sukrosa, sehingga elektroda modifikasi memberikan respon terhadap sukrosa dan glukosa dengan 174,0, =amp jik . Nilai arus oksidasi naik seiring dengan naiknya konsentrasi sukrosa hingga sinyal arus yang dihasilkan menjadi konstan pada konsentrasi sukrosa 45 hingga 50 mM. Kurva kalibrasi yang dihasilkan adalah kurva hiperbo lik khas enzim R = 0,9983. Hasil perhitungan menunjukan bahwa sensitivitas elektroda emas termodifikasi polianilin, enzim invertase dan partikel nano emas sebesar 0,4657 μA. mm-2 . mM-1 dengan limit deteksi sebesar 9 μM.
=============================================================================================================================
A modified working electrode fabricated with polyaniline, the enzyme invertase and gold nano particles has been successfully tested to sucrose solution. The modification was performed through cyclic voltammetry technique by using potentiostat. Gold nano particles were coated to the electrode surface layer by layer and simultaneously observed the gradation of surface formation using optical microscope. Sucrose was tested in buffer phospat solution with acidity level at 6.78. The potential current oxidation respond at 328 mV was identified as current oxidation of glucose yielded from hidrolisis process of sucrose. Selectivity coefficient of this modified electrode to glucose was 0,174k amp ji, = . The oxidation current and sucrose concentration showed a positive linear relationship but limited to maximum 45-50 mM of sucrose concentration. Experimental callibration curve which figure out electrode respond to different sucrose concentration followed a typical enzyme hyperbolic trend line with R = 0,9983. Therefor e, it suggested that the new modified working electrode has sensitivity to the sucrose at 0,4657 μA. mm- 2 . mM- 1 with limit detection at 9 μM.

Item Type:	Thesis (Masters)
Additional Information:	RTKi 541.372 4 Fit m-1, 2014
Uncontrolled Keywords:	Biosensor sukrosa, PANI, invertase, partikel nano emas, voltammetri siklik, Sucrose biosensor, invertase, gold nanoparticles, cyclic voltammetry.
Subjects:	Q Science > QD Chemistry > QD115 Electrochemical analysis
Divisions:	Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	10 Jan 2024 02:53
Last Modified:	10 Jan 2024 02:53
URI:	http://repository.its.ac.id/id/eprint/105433

Actions (login required)

View Item