Analisis Pengaruh Waktu Elektrodeposisi Terhadap Peningkatan Kinerja Baterai- Superkapasitor Hybrid Berbahan Komposit NiOH2/NiMoO4 Pada Template rGO Nickel Foam

Vikranta, Ida Ayu Gayatri Alycia (2024) Analisis Pengaruh Waktu Elektrodeposisi Terhadap Peningkatan Kinerja Baterai- Superkapasitor Hybrid Berbahan Komposit NiOH2/NiMoO4 Pada Template rGO Nickel Foam. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011201118-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2026. Download (4MB) | Request a copy

Abstract

Fabrikasi elektroda hybrid baterai-superkapasitor berbahan Ni(OH)2/NiMoO4/ rGO/NF diharapkan mampu membentuk struktur nano yang efektif untuk meningkatkan kinerja elektrokimia dari elektroda jenis hybrid baterai-superkapasitor. Komposit Ni(OH)2/NiMoO4 ditumbuhkan pada rGO/NF melalui metode hidrotermal dan elektrodeposisi potensiostatik. Dengan kombinasi sifat-sifat yang baik dari Ni(OH)2 dan NiMoO4, serta penggunaan substrat Ni foam, komposit Ni(OH)2/NiMoO4 untuk perangkat hybrid baterai-superkapasitor dapat memberikan kinerja elektrokimia yang unggul dengan kapasitas penyimpanan energi yang tinggi, stabilitas siklus yang baik, dan transfer muatan yang efisien diperlukan adanya penelitian terbaru yang akan fokus terhadap sintesis elektroda berbahan dasar komposit NiOH2/NiMoO4/rGO/NF dengan variasi penambahan waktu elektrodeposisi sebesar 60, 120, dan 180 detik. Adapun beberapa pengujian karakterisasi yang digunakan adalah SEM-EDX, XRD, dan FTIR untuk melakukan analisa morfologi dan struktur komposit. Sedangkan pengujian CV, EIS, dan GCD dilakukan agar dapat mengetahui nilai kapasitansi dan konduktivitas listrik dari komposit NiOH2/NiMoO4/rGO/NF. Penambahan waktu elektrodeposisi pada semua variasi komposit NiOH2/NiMoO4/rGO/NF berpengaruh terhadap presentase kandungan dari NiOH2 yang semakin banyak pada komposit NiOH2/NiMoO4/rGO/NF. Kemudian dari pengujian EDX didapatkan presentase komposisi C dan Ni tertinggi pada material N5(E3) sebesar 01.73 wt% C dan 70.32% wt% Ni. Kemudian untuk pengujian elektrokimia variasi waktu elektrodeposisi yang memiliki nilai kapasitansi yang paling tinggi dan sifat kapasitif yang baik adalah 3 menit N5(E3) berdasarkan hasil pengujian CV sebesar 576.584 F/g pada scan rate 5 mV/s, untuk hasil pengujian EIS dengan nilai konduktivitas 1.044 Sm-1, sedangkan hasil pengujian GCD sebesar 68.011 F/g pada current density 0.25 A/g.
=================================================================================================================================
Fabrication of battery-supercapacitor hybrid electrodes made from Ni(OH)2/NiMoO4/rGO/NF is expected to form effective nanostructures to improve the electrochemical performance of battery-supercapacitor hybrid electrodes. Ni(OH)2/NiMoO4 composites are grown on rGO/NF through hydrothermal methods and potentiostatic electrodeposition. With the combination of good properties of Ni(OH)2 and NiMoO4, as well as the use of Ni foam substrates, Ni(OH)2/NiMoO4 composites for battery-supercapacitor hybrid devices can provide superior electrochemical performance with high energy storage capacity, good cycle stability, and efficient charge transfer, new research is needed that will focus on the synthesis of NiOH2 composite-based electrodes/NiMoO4/rGO/NF with increased electrodeposition times of 60, 120, and 180 seconds. Some of the characterization tests used are SEM-EDX, XRD, and FTIR to perform morphological analysis and composite structures. Meanwhile, CV, EIS, and GCD tests are carried out in order to determine the capacitance and electrical conductivity values of NiOH2 / NiMoO4 / rGO/NF composites. The addition of electrodeposition time in all variations of NiOH2/NiMoO4/rGO/NF composites affects the increasing percentage of NiOH2 content in NiOH2/NiMoO4/rGO/NF composites. Then from EDX testing, the highest percentage of C and Ni composition in N5 (E3) material was 01.73 wt% C and 70.32% wt% Ni. Then for electrochemical testing, the electrodeposition time variation that has the highest capacitance value and good capacitive properties is 3 minutes N5 (E3) based on CV test results of 576.584 F/g at a scan rate of 5 mV / s, based on EIS test results with a conductivity value of 1.044 Sm-1, and based on GCD test results of 68.011 F / g at a current density of 0.25 A/g.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Baterai Superkapasitor Hybrid, Elektrodeposisi, Nickel foam, NiOH2/NiMoO4, rGO, Electrodeposition, Hybrid Supercapacitor Battery
Subjects:	T Technology > T Technology (General)
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Ida Ayu Gayatri Alycia Vikranta
Date Deposited:	05 Feb 2024 05:01
Last Modified:	05 Feb 2024 05:01
URI:	http://repository.its.ac.id/id/eprint/106058

Actions (login required)

View Item