Fabrikasi Elektroda Emas Termodifikasi Tungsten Trioksida/Tinta Karbon (WO3/C/Au) sebagai Sensor Elektrokimia untuk Deteksi Ion Nitrit

Sari, Niken Puspita (2024) Fabrikasi Elektroda Emas Termodifikasi Tungsten Trioksida/Tinta Karbon (WO3/C/Au) sebagai Sensor Elektrokimia untuk Deteksi Ion Nitrit. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6004212006-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2026. Download (1MB) | Request a copy

Abstract

Pada penelitian ini, elektroda emas termodifikasi tungsten trioksida/tinta karbon (WO3/C/Au) difabrikasi untuk deteksi ion nitrit yang sensitif. WO3 disintesis dari logam tungsten melalui teknik pengendapan selektif. Material hasil sintesis dikarakterisasi dengan pengamatan visual, FE-SEM/EDS, dan XRD. Elektroda emas dimodifikasi dengan teknik dip immersion dalam campuran WO3 / tinta karbon (agen pengikat). Elektroda termodifikasi dievaluasi dengan teknik voltammetri siklik dan amperometri. Hasil pengukuran luas area elektroaktif menunjukkan bahwa Elektroda WO3/C/Au memiliki luas area elektroaktif terbesar dibandingkan dengan elektroda emas termodifikasi tinta karbon (C/Au) dan elektroda emas tanpa modifikasi (Au). Elektroda WO3/C/Au bekerja dengan baik pada pH 7 untuk mendeteksi ion nitrit dan memberi puncak arus tertinggi dibanding elektroda C/Au dan elektroda Au. Nilai batas deteksi dan sensitivitas elektroda diperoleh dari pengujian amperometri dengan nilai masing-masing sebesar 0,80 µg/L dan 8,86 μA L mg-1cm-2 pada rentang linear 1-11 mg/L. Elektroda WO3/C/Au menunjukkan selektivitas yang baik dalam mendeteksi nitrit pada larutan yang mengandung NO3-, SO42-, Zn2+, Fe2+, Pb2+, Cl-, Ca2+, dan NH4+. Uji repeatability dan reproducibility dari elektroda WO3/C/Au menghasilkan nilai RSD masing-masing sebesar 0,87% dan 1,34% yang menunjukkan stabilitas arus dan presisi elektroda yang baik. Secara keseluruhan, elektroda WO3/C/Au merupakan kandidat yang menjanjikan sebagai elektroda alternatif untuk deteksi nitrit.
===================================================================================================================================
In this work, tungsten trioxide/carbon paint modified gold electrode was fabricated for sensitive nitrite ion detection. The WO3 was synthesized from tungsten metal through selective precipitation technique. The shynthesized material was characterized by visual observation, FE-SEM/EDS, and XRD. Gold electrode was modified by dip immersion technique in a mixture of WO3 - carbon paint (binder). The modified electrode was evaluated by cyclic voltammetry and amperometry techniques. The measurement of electroactive surface area shows that WO3/C/Au has the highest surface area compared to unmodified Au (Au) and carbon modified Au electrodes (C/Au). The WO3/C/Au electrode works well at pH 7 for the detection of nitrite ions and gives the highest peack current campared to Au and C/Au electrodes. The limit of detection (LOD) and sensitivity acquired from amperommetry measurements were 0,80 µg/L dan 8,86 μA L mg-1cm-2, respectively in linear range of 1-11 mg/L. The WO3/C/Au electrode reveals good selectivity for nitrite ion detection in the presence of NO3-, SO42-, Zn2+, Fe2+, Pb2+, Cl-, Ca2+, and NH4+. The repeatability and reproducibility measurements of WO3/C/Au with low RSDs of 0,87% and 1,34%, respectively indicated good electrode stability and precision. All of this performace indicates that WO3/C/Au modified gold electrode is a promising candidate for nitrite ion detection.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Tungsten Trixide, Sensor, Selective, nitrite ion, Tungsten Trioksida, Sensor, Selektif, Ion Nitrit
Subjects:	Q Science > QD Chemistry > QD115 Electrochemical analysis
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Niken Puspita Sari
Date Deposited:	14 Feb 2024 14:10
Last Modified:	14 Feb 2024 14:10
URI:	http://repository.its.ac.id/id/eprint/107038

Actions (login required)

View Item