Pengaruh Parameter Interlock Terhadap Kekuatan Tarik Produk 3D Print Berbahan Multimaterial Filamen PLA Dan Filamen TPU

AZIZ, MOCHAMAD (2024) Pengaruh Parameter Interlock Terhadap Kekuatan Tarik Produk 3D Print Berbahan Multimaterial Filamen PLA Dan Filamen TPU. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038221104-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2026. Download (5MB) | Request a copy

Abstract

Teknologi 3D Print yang mengalami perkembangan paling menarik adalah Multimaterial Additive Manufacturing (MAM), yang memungkinkan pencetakan objek dengan berbagai bahan secara bersamaan. MAM memungkinkan pencetakan obyek yang kompleks dengan material yang berbeda dalam satu proses cetak. Selain itu, penggabungan material yang berbeda memungkinkan pembuatan struktur hibrid yang memanfaatkan keunggulan masing-masing material, membuka pintu untuk inovasi yang lebih luas. Meskipun MAM menawarkan potensi besar, masih ada beberapa tantangan yang perlu diatasi, termasuk kesulitan dalam mengontrol berbagai parameter proses cetak, pemilihan material yang sesuai, kesesuaian desain dan kekuatan ikatan antar material yang salah satunya adalah material PLA dengan material TPU. Penelitian ini berupaya untuk mengetahui nilai kekuatan tarik dari produk MAM filamen PLA dan TPU yang diproduksi melalui parameter Interlock yang ada di Ultimaker Cura 5.4 dengan cara spesimen dicetak berdasarkan spesimen ASTM D638 dan untuk mengetahui pengaruh dari parameter interlock yang ada pada fitur tersebut. Hasil penelitian menunjukan kekuatan tarik yang diproduksi melalui parameter Interlock yang memiliki kekuatan tarik yang terbesar yaitu parameter Interlocking Depth 8 dan Interlock Structure Orientation 450 sebesar 7,08 MPa dan kekuatan tarik yang paling rendah yaitu parameter Interlocking Depth 2 dan Interlock Structure Orientation 450 sebesar 5,14 MPa. Dengan hasil tersebut dapat memberi tambahan pilihan untuk mempoduksi produk yang berbahan multimaterial filamen PLA dan filamen TPU melalui parameter Interlock yang ada pada Ultimaker Cura 5.4.
=============================================================================================================================
The most interesting development in 3D Printing technology is Multimaterial Additive Manufacturing (MAM), which allows for the printing of objects using various materials simultaneously. MAM enables the printing of complex objects with different materials in a single printing process. Furthermore, the combination of different materials allows for the creation of hybrid structures that leverage the advantages of each material, opening the door to broader innovation. Despite offering great potential, MAM still faces some challenges that need to be addressed, including difficulties in controlling various printing process parameters, selecting appropriate materials, design compatibility, and the bond strength between materials, one of which is between PLA and TPU materials. This research aims to determine the tensile strength values of MAM products made from PLA and TPU filaments produced through Interlock parameters in Ultimaker Cura 5.4. The specimens are printed based on ASTM D638 specifications to understand the influence of the Interlock parameters on the features. The research results show that the tensile strength produced through the Interlock parameters with the highest tensile strength is Interlocking Depth 8 and Interlock Structure Orientation 450 at 7,08 MPa, while the lowest tensile strength is with Interlocking Depth 2 and Interlock Structure Orientation 450 at 5,14 MPa. With these results, additional options are provided for producing products made of multimaterial PLA and TPU filaments through the Interlock parameters in Ultimaker Cura 5.4.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Multi-Material, 3D Print, Additive Manufacture, Kekuatan Tarik
Subjects:	T Technology > TS Manufactures > TS171 Product design T Technology > TS Manufactures > TS183 Manufacturing processes. Lean manufacturing.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Mochamad Aziz
Date Deposited:	15 Feb 2024 08:24
Last Modified:	15 Feb 2024 08:24
URI:	http://repository.its.ac.id/id/eprint/107164

Actions (login required)

View Item