Optimasi Sintesis Perak Nanopartikel dengan Response Surface Methodology (RSM) Dan Aplikasinya Sebagai Anti Bakteri

Devian, Gabriel Denis (2024) Optimasi Sintesis Perak Nanopartikel dengan Response Surface Methodology (RSM) Dan Aplikasinya Sebagai Anti Bakteri. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6004212003-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2026. Download (2MB) | Request a copy

Abstract

Perak nanopartikel (AgNP) telah berhasil dioptimasi dengan melibatkan tiga jenis faktor yang mempengaruhi hasil sintesisnya. Faktor tersebut adalah konsentrasi prekursor (AgNO3), konsentrasi reduktor (glukosa), serta waktu sonikasi, dengan masing-masing faktor menggunakan tiga tingkatan variasi. Variasi yang digunakan yakni pada AgNO3 dengan konsentrasi ssebesar 0,001 ; 0,005 ; 0,010 M, konsentrasi glukosa sebesar 0,01 ; 0,05 ; 0,10 M, serta waktu sonikasi selama 0, 10, dan 20 menit. Proses optimasi data dilakukan dengan Response Surface Methodology (RSM) : Face Centered – Central Composite Design (F-CCD), sehingga didapati data optimum yang dipengaruhi oleh ketiga variabel. Kondisi optimum yang didapatkan yakni dengan konsentrasi AgNO3 sebesar 0,010 M, konsentrasi glukosa sebesar 0,065 M, serta waktu sonikasi selama 20 menit. Studi lebih lanjut dilakukan pada AgNP hasil optimasi untuk melihat distribusi dan ukuran partikel, yakni dengan Particle Size Analyzer (PSA) dan Transmission Electron Microscope (TEM). Hasil pengujian menunjukkan partikel berbentuk spherical berukuran 18,40 nm dengan puncak tunggal serta distribusi partikel yang tersebar merata secara monodisperse. Pengujian anti bakteri juga dilakukan dengan metode difusi cakram pada bakteri Gram negatif (Escherichia coli) dan Gram positif (Staphylococcus aureus). Hasil menunjukkan didapati zona inhibisi sebesar 6,5 mm dan 4,8 mm masing-masing untuk bakteri Gram negatif dan positif.
=============================================================================================================================
Silver nanoparticles (AgNPs) have been successfully optimized by involving three types of factors that influence the synthesis results. These factors are precursor concentration (AgNO3), reductant concentration (glucose), and sonication time, with each factor using three levels of variation. The variation used is AgNO3 with a concentration of 0.001; 0.005 ; 0.010 M, glucose concentration of 0.01; 0.05 ; 0.10 M, and sonication times of 0, 10, and 20 minutes. The optimization process of the data was conducted using Response Surface Methodology (RSM): Face Centered - Central Composite Design (F-CCD), resulting in optimum data influenced by all three variables. The obtained optimum conditions are AgNO3 concentration of 0.010 M, glucose concentration of 0.065 M, and sonication time of 20 minutes. Further studies were conducted on the optimized AgNPs to observe the particle distribution and size using Particle Size Analyzer (PSA) and Transmission Electron Microscope (TEM). The test results showed spherical particles with a size of 18.40 nm, with a single peak and a uniformly distributed monodisperse particle size. Antibacterial testing was also conducted using the disk diffusion method on Gram-negative bacteria (Escherichia coli) and Gram-positive bacteria (Staphylococcus aureus). The results showed inhibition zones of 6.5 mm and 4.8 mm for Gram-negative and Gram-positive bacteria, respectively.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Perak Nanopartikel (AgNP), RSM, Sonikasi, Anti Bakteri, Silver Nanoparticles (AgNP), Sonication, Anti Bacterial
Subjects:	Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Gabriel Denis Devian
Date Deposited:	15 Feb 2024 19:17
Last Modified:	15 Feb 2024 19:17
URI:	http://repository.its.ac.id/id/eprint/107176

Actions (login required)

View Item