Pengukuran Konduktivitas Panas Pada Aspal Hotmix Dengan Campuran Getah Pinus Dan Styrofoam

Fiqrulhaq, Naufaldy (2022) Pengukuran Konduktivitas Panas Pada Aspal Hotmix Dengan Campuran Getah Pinus Dan Styrofoam. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000053-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 September 2024. Download (3MB)

Abstract

Penelitian pengukuran konduktivitas panas pada aspal hotmix dengan campuran getah pinus dan styrofoam sebagai refrensi aspal pada landasan pacu bertujuan untuk mengetahui pengaruh perbedaan jenis aspal pada konduktivitas termal dan persebaran panas, mengetahui pengaruh perbedaan konsentrasi aspal pada konduktivitas termal dan persebaran panas. Variasi aspal dan filler yang digunakan dalam modifikasi I adalah 92% Styrofoam 5% dan pinus 3% dan modifikasi II adalah 90% Styrofoam 7% dan pinus 3%, dengan variasi komposisi aspal didalam spesimen sebesar 4%, 5%, dan 6%. Metode untuk mencari nilai konduktivitas panas adalah metode komparatif dan mencari persebaran titik panas dalam spesimen. Tatanan tempat pada uji komparatif ini adalah termokopel pertama untuk mengetahui nilai T1 di paling atas, lalu aluminium, kemudian termokopel ke-2 untuk mengetahui nilai T2 yang diukur dari kontak antara aluminium dengan sampel aspal, dan T3 diukur dari kontak antara sampel aspal dengan pendingin. Pengambilan data suhu ini dilakukan pada suhu 30ºC, 50ºC, 70ºC dan 100ºC. Berdasarkan penelitian yang telah dilakukan, diperoleh hasil sebagai berikut pada aspal pertamina nilai konduktivitas termalnya adalah 114,06; 94,39; 66,57; dan 47,17 W / (m.K). Sementara itu pada aspal modifikasi I 101,13; 22,15; 13,07; 12,83 W / (m.K). Dan pada aspal modifikasi II 113,675; 32,06; 13,02; 11,35 W / (m.K). Dari hasil diatas aspal modifikasi I dan II mampu menurunkan konduktivitas termalnya sebesar 82% hingga 88%. Dari hasil pengukuran tiap titik imenunjukan bahwa aspal modifikasi II lebih tahan terhadap panas dikarenakan nilai ∆Ta dan ∆Tb memiliki nilai yang paling jauh, yaitu 60,67 ℃ dan 13,93 ℃ , yang membuatnya lebih tahan terhadap deformasi.
================================================================================================================================
Research on measuring the thermal conductivity of hot mix asphalt with a mixture of pine resin and styrofoam as a reference for asphalt on the runway aims to determine the effect of different types of asphalt on thermal conductivity and heat distribution, and to determine the effect of differences in asphalt concentration on thermal conductivity and heat distribution. The variation of asphalt and filler used in modification I was 92% Styrofoam 5% and 3% pine and modification II was 90% Styrofoam 7% and pine 3%, with variations in the composition of asphalt in the specimen by 4%, 5%, and 6%. The method to find the value of thermal conductivity is a comparative method and looks for the distribution of hot spots in the specimen. The order of place in this comparative test is the first thermocouple to determine the T1 value at the top, then aluminum, then the 2nd thermocouple to determine the T2 value measured from the contact between the aluminum and the asphalt sample, and T3 measured from the contact between the asphalt sample and the coolant. The temperatur data were collected at 30ºC, 50ºC, 70ºC and 100ºC. Based on the research that has been done, the following results were obtained for Pertamina's asphalt, the thermal conductivity value was 114.06; 94.39; 66.57; and 47.17. Meanwhile on the asphalt modification I 101.13; 22.15; 13.07; 12.83. And on the modified asphalt II 113.675; 32.06; 13.02; 11.35. From the results above, the modified asphalt I and II are able to reduce their thermal conductivity by 82% to 88%. However, the values of Ta and Tb belonging to modified asphalt II are higher, namely 60.67 and 13.93 . These results indicate that the modified asphalt II is more resistant to heat, which in turn makes this asphalt more resistant to deformation.

Item Type:	Thesis (Other)
Additional Information:	RSFi 536.2 Fiq p-1
Uncontrolled Keywords:	Aspal, Konduktivitas termal, Landasan pacu, Persebaran Panas
Subjects:	Q Science > QC Physics > QC320 Heat transfer
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Tondo Indra Nyata
Date Deposited:	27 Feb 2024 03:27
Last Modified:	27 Feb 2024 03:27
URI:	http://repository.its.ac.id/id/eprint/107716

Actions (login required)

View Item