Studi Struktur CaO Pada Proses Penyerapan CO2 Melalui Variasi Penggilingan Untuk Meningkatkan Efisiensi Penangkapan Co2

Masdya, Yoga (2024) Studi Struktur CaO Pada Proses Penyerapan CO2 Melalui Variasi Penggilingan Untuk Meningkatkan Efisiensi Penangkapan Co2. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201001-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (2MB) | Request a copy

Abstract

Penelitian tugas akhir yang berjudul “STUDI STRUKTUR CaO PADA PROSES PENYERAPAN CO2 MELALUI VARIASI PENGGILINGAN UNTUK MENINGKATKAN EFISIENSI PENANGKAPAN CO2” bertujuan untuk mengungkap pengaruh durasi penggilingan terhadap struktur dan ukuran partikel CaO serta dampaknya pada penyerapan CO2 selama proses karbonasi dengan mengevaluasi perubahan karakteristik fisik CaO akibat variasi waktu Penggilingan, penelitian ini berusaha menentukan kondisi optimal untuk meningkatkan efisiensi penangkapan CO2. Penelitian dilaksanakan melalui dua tahapan utama: sintesis prekursor CaO melalui kalsinasi, aplikasi milling dengan variasi waktu (0 jam, 2 jam, 4 jam, dan 6 jam). Proses karbonasi dilakukan pada variasi suhu 700°C menggunakan tube-furnace. Karakterisasi hasil karbonasi yang mencakup identifikasi fasa terbentuk oleh X-Ray Diffraction (XRD) dengan sudut 10° - 70°. Fasa yang terbentuk dalam sampel berupa CaO, Ca(OH)₂, dan CaCO₃, dengan perubahan signifikan pada parameter kisi dan volume kristal. Ukuran kristal Ca(OH)₂ meningkat dari 14,75 nm menjadi 17,79 nm setelah hidrasi, menunjukkan pertumbuhan kristal yang signifikan. Penggilingan selama 4 jam menghasilkan penyerapan CO₂ tertinggi, mencerminkan efisiensi penyerapan optimal. Hasil penelitian menunjukkan bahwa penggilingan secara signifikan meningkatkan luas permukaan dan porositas sampel, yang memfasilitasi penyerapan CO₂ yang lebih efektif. Durasi penggilingan mempengaruhi aglomerasi partikel, di mana 4 jam merupakan durasi optimal untuk mencapai reaktivitas maksimal tanpa mengurangi efisiensi penyerapan. Dengan demikian, proses penggilingan yang tepat dapat meningkatkan potensi aplikasi kalsium oksida dalam berbagai industri, terutama dalam penyerapan gas CO2.
=================================================================================================================================
The final project research entitled "STUDY OF CaO STRUCTURE IN CO₂ ADSORPTION PROCESS THROUGH MILLING VARIATIONS TO ENHANCE CO₂ CAPTURE EFFICIENCY " aims to reveal the impact of milling duration on the structure and particle size of CaO and its effects on CO2 adsorption during the carbonation process by evaluating changes in the structural characteristics of CaO due to different milling durations, this study seeks to determine optimal conditions to enhance CO₂ capture efficiency. The research was conducted in two main stages: synthesis of CaO precursors through calcination, milling with time variations (0 hours, 2 hours, 4 hours, and 6 hours), and carbonation at 700°C using a tube furnace. Characterization of the carbonation results, including phase identification, was performed using X-Ray Diffraction (XRD) at angles between 10° and 70°. The phases formed in the samples included CaO, Ca(OH)₂, and CaCO₃, with significant changes in lattice parameters and crystal volume. The crystal size of Ca(OH)₂ increased from 14.75 nm to 17.79 nm after hydration, indicating significant crystal growth. Milling for 4 hours resulted in the highest CO₂ adsorption, reflecting optimal adsorption efficiency. The results show that milling significantly increases the surface area and porosity of the samples, facilitating more effective CO₂ adsorption. Milling duration influences particle agglomeration, with 4 hours being the optimal duration to achieve maximum reactivity without reducing adsorption efficiency. Therefore, appropriate milling processes can enhance the potential applications of calcium oxide in various industries, particularly in CO₂ gas adsorption.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	CaCO3, CaO, CO2 Capture, penangkapan CO2
Subjects:	Q Science > QC Physics > QC100 Crystals.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Yoga Masdya
Date Deposited:	18 Jul 2024 07:42
Last Modified:	18 Jul 2024 07:42
URI:	http://repository.its.ac.id/id/eprint/108452