Analisis Pengaruh Infill dan Sudut Pencetakan Terhadap Kekuatan Tarik Material PLA dan PETG yang Dimanufaktur dengan 3D Printer

Rachmawan, Nouvan Vitra (2024) Analisis Pengaruh Infill dan Sudut Pencetakan Terhadap Kekuatan Tarik Material PLA dan PETG yang Dimanufaktur dengan 3D Printer. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2038201032-Undergraduate_Thesis.pdf] Text
2038201032-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2026.

Download (11MB) | Request a copy

Abstract

Three dimensional (3D) printing menjadi salah satu mesin yang handal dan revolusioner pada teknik additive manufacturing (AM) untuk membuat objek tiga dimensi dengan struktur yang unik dan bermacam–macam. Proses riset dan penyempurnaan Fused Deposition Modelling 3D Printer, tentunya terdapat berbagai variabel dan parameter dengan tujuan menghasilkan objek tiga dimensi dengan hasil dan kekuatan yang baik serta dapat diaplikasikan seperti rancangan yang diharapkan. Pada penelitian ini akan dipelajari pengaruh infill pattern, infill density dan deposition angle terhadap kekuatan tarik pada material PLA dan PETG. Untuk mengetahui pengaruh infill pattern pada penelitian ini, digunakan pola pengisi rectilinear, triangle, dan honeycomb. Penggunaan variasi infill 33%, 66%, dan 99% digunakan untuk mengetahui pengaruh kepadatan infill yang mewakili dari tingkat rendah hingga tinggi. Variasi sudut pencetakan pada penelitian ini menggunakan sudut 45o dan 90 o. PLA dan PETG merupakan material yang banyak digunakan karena memiliki sifat mekanis yang baik, hasil cetak yang halus, serta terjangkau. Penelitian ini menggunakan pengujian uji tarik (tensile test) dengan pengolahan analisis statistik menggunakan Analysis Of Variance (ANNOVA).Hasil dari penelitian ini dapat mengetahui nilai ultimate tensile strenght yang terbaik dengen pengaruh dari infill pattern, infill density dan sudut pencetakan. Hasil perhitungan mendapatkan bahwa pengisian paling optimal pada filament PLA dengan variasi infill density 99% dan infill patern honeycomb. Dinyatakan parameter variasi yang memiliki pengaruh siginfikan yaitu infill density dengan nilai 99% pada filament PLA
===================================================================================================================================
Three-dimensional (3D) printing is one of the reliable and revolutionary machines in additive manufacturing (AM) techniques to create three-dimensional objects with unique and diverse structures. The research and refinement process of Fused Deposition Modeling 3D Printer, of course, there are various variables and parameters with the aim of producing three-dimensional objects with good results and strength and can be applied as expected design. In this study, the effect of infill pattern, infill density and deposition angle on tensile strength in PLA and PETG materials will be studied. To determine the effect of infill pattern in this study, rectilinear, triangle, and honeycomb filler patterns were used. The use of infill variations of 33%, 66%, and 99% was used to determine the effect of infill density representing from low to high levels. The printing angle variation in this study used angles of 45o and 90o. PLA and PETG are materials that are widely used because they have good mechanical properties, smooth print results, and are affordable. This study uses tensile test with statistical analysis processing using Analysis Of Variance (ANNOVA). The results of this study can determine the best ultimate tensile strength value with the influence of infill pattern, infill density and printing angle. The calculation results show that the most optimal filling on PLA filament with an infill density variation of 99% and a honeycomb infill pattern. It is stated that the variation parameter that has a significant influence is infill density with a value of 99% on PLA filament

Item Type: Thesis (Other)
Uncontrolled Keywords: 3D Printing, additive manufacturing (AM), FDM, Infill pattern, Infill density PLA,PETG
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User: Nouvan Vitra Rachmawan
Date Deposited: 01 Aug 2024 03:11
Last Modified: 12 Sep 2024 06:09
URI: http://repository.its.ac.id/id/eprint/110395

Actions (login required)

View Item View Item