Efektivitas Konsentrasi Agen Desorpsi Ethylenediaminetetraacetic (EDTA) Dan Waktu Desorpsi Terhadap Ekstraksi Platinum Pada Proses Hidrometalurgi Menggunakan Membran Nano-Chitosan Oligo Saccharide

Budiono, Bintan Jorgi (2024) Efektivitas Konsentrasi Agen Desorpsi Ethylenediaminetetraacetic (EDTA) Dan Waktu Desorpsi Terhadap Ekstraksi Platinum Pada Proses Hidrometalurgi Menggunakan Membran Nano-Chitosan Oligo Saccharide. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011201085-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (6MB) | Request a copy

Abstract

Studi dan pemanfaatan logam platinum telah cukup lama dilakukan serta memberikan manfaat bagi manusia. Dependensi manusia terhadap logam platinum membuat industri pengolahan logam Platinum Group Metals (PGMs) berkembang pesat dengan dominasi pirometalurgi sebagai metode pemrosesannya. Pemrosesan secara pirometalurgi ini masih membutuhkan energi yang besar serta meninggalkan emisi yang besar bagi lingkungan. Maka dari itu penelitian ini akan berfokus pada ektraksi ion platinum secara hidrometalurgi dengan bantuan metode biosorpsi. Metode leaching adalah proses hidrometalurgi yang akan digunakan untuk kemudian menggunakan membran nano-chitosan oligosakarida pada proses adsorpsi dan desorpsi. Proses leaching ditetapkan pada temperatur 300°C, agitasi 200 rpm, dan larutannya adalah HCl : HNO3 4M. Kemudian proses adsorpsi ditetapkan pada pH 1,5 dengan temperatur 35°C selama 4 jam. Penelitian ini akan difokuskan pada proses desorpsi variasi konsentrasi etilendiaminetetraacetic (EDTA) 0,01; 0,05; dan 0,1 M. Kemudian variasi waktu yaitu 4, 6, 8, 10, 12 jam yang kemudian dilakukan analisis menggunakan pengujian UV-Vis, FTIR, dan SEM EDX untuk dapat menentukan hasil penelitian ekstraksi ion PtCl62- pada aqueous solution. Hasil pada penelitian menunjukkan bahwa pengaruh waktu desorpsi memiliki titik maksimum pada 4 jam yang kemudian turun pada waktu 6 jam dan mengalami kejenuhan pada waktu 8 jam. Desorpsi pada 10 jam dan 12 jam mengalami kenaikan kembali. Hasil penelitian ini juga menunjukkan bahwa pengaruh konsentrasi memiliki ketentuan yang tidak stabil pada proses desorpsi ion PtCl62- . Konsentrasi 0,01 dan 0,05 M akan optimal pada waktu 4 jam, sedangkan konsentrasi 0,1 M akan optimal pada waktu 12 jam.
========================================================================================================================
The study and utilization of platinum metals have been carried out for a long time and provide benefits to humans. Human dependence on platinum metals has led to the rapid growth of the Platinum Group Metals (PGMs) processing industry with pyrometallurgy dominating as the processing method. Pyrometallurgical processing still requires a lot of energy and leaves large emissions for the environment. Therefore, this research will focus on the hydrometallurgical extraction of platinum ions with the help of biosorption method. The leaching method is a hydrometallurgical process that will be used to then use nano-chitosan oligosaccharide membranes in the adsorption and desorption process. The leaching process was set at 300°C, 200 rpm agitation, and the solution was HCl: HNO3 4M. Then the adsorption process was set at pH 1.5 with a temperature of 35°C for 4 hours. This research will focus on the desorption variation of ethylenediaminetetraacetic (EDTA) concentrations of 0.01; 0.05; and 0.1M. Then the time variation is 4, 6, 8, 10, 12 hours which is then analyzed using UV-Vis, FTIR, and SEM EDX testing to determine the results of PtCl62- ion extraction research in aqueous solution. The results showed that the effect of desorption time had a maximum point at 4 hours which then dropped at 6 hours and experienced saturation at 8 hours. Desorption at 10 hours and 12 hours increased again. The results of this study also show that the effect of concentration has unstable provisions on the desorption process of PtCl62- ions. The concentration of 0.01 and 0.05 M will be optimal at 4 hours, while the concentration of 0.1 M will be optimal at 12 hours.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Biosorpsi, Desorpsi, Kitosan, Konsentrasi EDTA, Platinum, Waktu desorp, Biosorption, Chitosan, Desorption, Desorption time, EDTA Concentration, Platinum
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN688 Hydrometallurgy T Technology > TP Chemical technology > TP248.65.C55 Chitosan--Biotechnology.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Bintan Jorgi Budiono
Date Deposited:	02 Aug 2024 01:35
Last Modified:	02 Aug 2024 01:35
URI:	http://repository.its.ac.id/id/eprint/110566

Actions (login required)

View Item