Efektivitas Jenis Kitosan dan Temperatur Pada Proses Adsorpsi Logam Emas Menggunakan Adsorben Berbasis Biopolimer Nano COS

Febriyanti, Vira Nur Afifah (2024) Efektivitas Jenis Kitosan dan Temperatur Pada Proses Adsorpsi Logam Emas Menggunakan Adsorben Berbasis Biopolimer Nano COS. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 5011201024-Undergraduate_Thesis.pdf] Text
5011201024-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2026.

Download (6MB) | Request a copy

Abstract

Emas adalah salah satu logam yang berharga. Metode untuk mengolah emas pada umumnya melalui proses hidrometalurgi atau leaching. Sianida yang digunakan sebagai larutan leaching sangat membahayakan lingkungan. Selain itu, proses recovery emas yang masih menggunakan karbon aktif sebagai adsorbennya juga menimbulkan polusi udara. Salah satu metode ekstraksi emas yang lebih ramah lingkungan adalah menggunakan larutan klorida sebagai larutan leaching dan metode biosorpsi menggunakan nano chitosan oligosaccharides (nano COS) untuk recovery emas. Proses recovery emas dibagi menjadi dua yaitu adsorpsi dan desorpsi. Terdapat beberapa parameter adsorpsi emas, yaitu temperatur dan jenis adsorben. Tujuan dari penelitian ini adalah untuk menganalisis pengaruh jenis kitosan dan temperatur pada proses adsorpsi menggunakan biopolimer nano COS, serta menganalisis tingkat konsentrasi logam emas yang dapat diadsorp menggunakan biopolimer nano COS. Variasi yang digunakan untuk jenis nano COS adalah udang dan kepiting, sedangkan temperatur yang digunakan adalah 35°C, 45°C, dan 55°C. Bahan yang digunakan adalah mineral emas yang berasal dari Gorontalo, Indonesia. Mineral emas terlebih dahulu dilakukan pengujian EDX dan XRD untuk mengetahui unsur dan senyawanya. Tahapan sebelum adsorpsi adalah adalah grinding, panning, roasting, dan leaching. Larutan leaching dilakukan pengujian AAS dan UVVis untuk mengetahui konsentrasi emas di dalam larutan. Kemudian, larutan leaching dilanjutkan untuk proses adsorpsi menggunakan jenis nano COS yang berbeda yaitu shrimp dan crab. Pada proses desorpsi dilakukan menggunakan larutan EDTA 0,1 M. Berdasarkan tahapan penelitian yang telah dilakukan, hasil roasting variasi daya 800 W menunjukkan persentase unsur emas lebih tinggi yaitu 3,73%. Kemudian pada agen leaching, larutan yang digunakan adalah HCl + HNO3 4 M 100°C dengan dasar absorbansi UV-Vis terbaik. Adapun hasil penelitian diketahui jenis nano COS yang lebih efektif pada proses adsorpsi adalah nano COS shrimp karena gugus amine yang bekerja lebih baik daripada gugus amide pada nano COS crab. Adapun temperatur adsorpsi berbanding lurus dengan kapasitas adsorpsi membran. Selain itu, temperatur adsorpsi mempengaruhi mekanisme adsorpsi Dimana temperatur 45°C, mekanisme adsorpsi terjadi secara elektrostatis. Sedangkan temperatur 55°C, mekanisme yang terjadi adalah chelation. Variasi membran nano COS shrimp mampu mengadsorpsi logam emas paling banyak pada temperatur 55°C yaitu 102,48 ppm dengan efisiensi 12,7%. Sedangkan kapasitas adsorpsi paling rendah adalah pada membran nano COS crab temperatur 35°C yaitu 7,23 ppm dengan efisiensi 0,9%.
======================================================================================================================================
Gold is one of the most valuable metals. Methods to process gold are generally through hydrometallurgical or leaching processes. The cyanide used as a leaching solution is very harmful to the environment. In addition, the gold recovery process that still uses activated carbon as an adsorbent also causes air pollution. One of the more environmentally friendly gold extraction methods is to use chloride solution as a leaching solution and biosorption method using nano chitosan oligosaccharides for gold recovery. The gold recovery process is divided into two, namely adsorption and desorption. There are several gold adsorption parameters, namely temperature and adsorbent type. The purpose of this study is to analyze the effect of chitosan type and temperature on the adsorption process using COS nano biopolymers, and to analyze the level of gold metal concentration that can be adsorbed using COS nano biopolymers. The variations used for the type of nano COS are shrimp and crab, while the temperatures used are 25°C, 35°C, and 45°C. The material used was gold mineral from Gorontalo, Indonesia. Gold minerals were first subjected to EDX and XRD testing to determine the elements and compounds. Stages before adsorption are grinding, panning, roasting, and leaching. The leaching solution was subjected to ICP-OES and UV-Vis testing to determine the concentration of gold in the solution. Then, the leaching solution was continued for the adsorption process using different types of nano COS, namely shrimp and crab. The desorption process was carried out using 0.1 M EDTA solution. Based on the stages of research carried out, the results of roasting variations of 800 W power show a higher percentage of gold elements, namely 3.73%. Then, in the leaching agent, the solution HCl + HNO3 4 M 100°C was used on the basis of the best UV-Vis absorbance. From the results, it is known that the type of nano-COS that is more effective in the adsorption process is nano-COS shrimp, because the amine group works better than the amide group on nano-COS shrimp. The adsorption temperature is directly proportional to the adsorption capacity of the membrane. In addition, the adsorption temperature affects the adsorption mechanism, where the temperature is 45 °C, the adsorption mechanism occurs electrostatically. While at 55°C, the mechanism that occurs is chelation. The COS shrimp nanomembrane variant was able to adsorb the most gold metal at 55°C, namely 102.48 ppm with an efficiency of 12.7%. While the lowest adsorption capacity is on the 35°C COS shrimp nanomembrane, which is 7.23 ppm with an efficiency of 0.9%.

Item Type: Thesis (Other)
Uncontrolled Keywords: Adsorpsi, Adsorben, Emas, Nano COS, Temperatur Adsorption, Adsorbent, Gold, Nano COS, Temperature
Subjects: T Technology > TN Mining engineering. Metallurgy > TN688 Hydrometallurgy
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Vira Nur Afifah Febriyanti
Date Deposited: 02 Aug 2024 03:07
Last Modified: 24 Sep 2024 02:22
URI: http://repository.its.ac.id/id/eprint/111064