Analisis Material Komposit Berbasis Serat Abaka Terhadap Isolasi Bunyi dan Sifat mekanik

Tanjung, Rafi' Anmara Habibie (2024) Analisis Material Komposit Berbasis Serat Abaka Terhadap Isolasi Bunyi dan Sifat mekanik. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201039-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Komposit merupakan material yang terdiri dari 2 penyusun yaitu matrik dan filler, pembuatan komposit ditujukan untuk meningkatkan nilai isolasi bunyi serta sifat mekanik dari serat abaka. Penelitian ini dilakukan pengujian serat abaka sebagai komposit untuk mengetahui pengaruh variasi fraksi matriks komposit serat abaka terhadap nilai TL, serta untuk mengetahui pengaruh porositas komposit serat abaka terhadap sifat mekanik. Variasi matriks dan serat yang digunakan untuk TL yaitu 80:20, 70:30, 60:40, dan 50:50. Adapun variasi ketebalan sampel untuk pengujian mekanik 6 mm, 5 mm, dan 4 mm. Pengujian TL dilakukan dengan metode tabung impedansi, sedangkan pengujian sifat mekanik dilakukan dengan metode three-point bending. Pengujian TL yang dilakukan pada frekuensi 80 – 4000 Hz 1/3 oktaf, dan didapatkan hasil terbaik pada sampel RA82 nilai TL tertinggi dan terendah berada pada frekuensi 3150 Hz dan 80 Hz dengan nilai 58 dB dan 56 dB. Adapun hasil terbaik dari pengujian mekanik pada sampel XA26 nilai beban maksimum, kekuatan kompresi, dan modulus lekuk berturut sebesar 226 N, 1,883 Mpa, dan 13,189 Mpa. Sehingga dari penelitian ini didapatkan bahwa pengaruh variasi fraksi matriks dan serat terhadap nilai TL memiliki hasil yang signifikan, dimana ketika fraksi matriks bertambah maka nilai dari TL akan semakin baik jika dibandingkan dengan fraksi matriks yang lebih rendah. Serta porositas pada sampel berpengaruh pada sifat mekanik sampel, dimana ketika porositas sampel semakin rendah maka sifat mekanik sampel akan menurun.
========================================================================================================================
Composite materials consist of two components the matrix and the filler. The development of composites aims to enhance the sound insulation and mechanical properties of abaca fiber. This research of abaca banana fiber as a composite to determine the effect of varying the composite matrix fraction on TL values, and to assess the impact of the porosity of the abaca fiber composite on its mechanical properties. The matrix and fiber variations used for TL are 80:20, 70:30, 60:40, and 50:50. The sample thickness variations for mechanical testing are 6 mm, 5 mm, and 4 mm. TL testing is conducted using the impedance tube method, while mechanical properties testing is performed using the three-point bending method. TL tests are conducted at frequencies ranging from 80 to 4000 Hz in 1/3 octave bands. The best results for TL are obtained from sample RA82, with the highest and lowest TL values at frequencies of 3150 Hz and 80 Hz are 58 dB and 56 dB, respectively. The best results from the mechanical testing on sample XA26 are a maximum load of 226 N, a bending strength of 1.883 MPa, and a bending modulus of 13.189 MPa. Thus, this study concludes that variations in matrix and fiber fractions significantly affect TL values, with higher matrix fractions resulting in better TL values compared to lower matrix fractions. Additionally, the porosity of the samples affects their mechanical properties, where lower sample porosity leads to a decrease in mechanical properties.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Abaca Banana Fiber, Mass Law, Mechanical, Mekanik, Serat abaka, Three Point Bending, Transmission Loss
Subjects:	Q Science > QC Physics Q Science > QC Physics > QC173.4.C63 Composite materials Q Science > QC Physics > QC221 Acoustics. Sound
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Rafi' Anmara Habibie Tanjung
Date Deposited:	05 Aug 2024 04:05
Last Modified:	05 Aug 2024 04:05
URI:	http://repository.its.ac.id/id/eprint/111146

Actions (login required)

View Item