Sintesa Nanokomposit Tio2/Cus/Gqds Dengan Drop Casting Untuk Aplikasi Fotokatalis Dalam Degradasi Senyawa Organik Sianida Pada Limbah

Dewanto, Javier Nur Dewanto (2024) Sintesa Nanokomposit Tio2/Cus/Gqds Dengan Drop Casting Untuk Aplikasi Fotokatalis Dalam Degradasi Senyawa Organik Sianida Pada Limbah. Other thesis, Institute Teknologi Sepuluh Nopember.

Text 5011201158_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (6MB) | Request a copy

Abstract

Metode hidrotermal digunakan untuk mengolah tembaga klorida (CuCl) dan Tiourea dalam rangka menghasilkan CuS, yang kemudian dipasangkan dengan semikonduktor TiO2. CuS memiliki energi band gap yang rendah, sehingga dianggap efektif dalam meningkatkan kinerja fotokatalis saat berinteraksi dengan energi foton rendah, seperti cahaya tampak. Graphene Quantum Dots (GQDs) diperoleh dari Graphene Oxide (GO) melalui metode top-down basa, dan GQDs memiliki luas permukaan yang besar, yang memperbaiki interaksi antara fotokatalis TiO2 dan senyawa sianida, serta meningkatkan degradasi sianida berkat transfer elektron yang cepat. Penelitian ini bertujuan untuk menganalisis efek penambahan GQDs dan CuS sebagai material yang dipasangkan dengan TiO2 terhadap karakteristik dan sifat TiO2, serta dampak kombinasi TiO2/CuS/GQDs terhadap degradasi senyawa organik sianida. Penelitian ini melibatkan berbagai eksperimen, termasuk sintesis TiO2, GQDs, CuS, dan nanokomposit TiO2/CuS/GQDs dengan variasi metode fabrikasi menggunakan drop casting. Hasil dari pengujian XRD nanokomposit TiO2/CuS/GQDs terdapat pada peak 26,79o, 25,44o, 27,70o, 29,49o, 31,92o, 32,94o. Hasil uji FTIR menunjukkan adanya gugus fungsi pada material komposit yaitu C-S, Ti-O-Ti, Ti-O-C yang mengindikasikan material nanokomposit TiO2/CuS/GQDs. Pada hasil uji SEM menunjukkan bahwa komposit TiO2/CuS/GQDs melekat pada nikel foam. Lalu pada hasil EDX menunjukkan unsur-unsur seperti Ti, O, C, Cu, S yang mengindikasikan komposit TiO2/CuS/GQDs. Hasil pengujian Uv-Vis pada variasi komposisi menghasilkan energy band gap 2,91 eV, 2,51 eV, 3,05 eV yang menandakan material CuS berhasil menurunkan bandgap dari material TiO2. Hasil pengujian fotokatalitik di dapatkan variasi komposisi 1;0,5;0,2 memiliki hasil degradasi optimal yaitu 91,83% pada larutan sianida.
=================================================================================================================================
Hydrothermal method is used to process copper chloride (CuCl) and Thiourea to produce CuS, which is then coupled with TiO2 semiconductor. CuS has a low band gap energy, so it is considered effective in improving the performance of photocatalysts when interacting with low photon energy, such as visible light. Graphene Quantum Dots (GQDs) are obtained from Graphene Oxide (GO) through a basic top-down method, and GQDs have a large surface area, which improves the interaction between TiO2 photocatalysts and cyanide compounds, and enhances cyanide degradation due to fast electron transfer. This study aims to analyze the effects of adding GQDs and CuS as materials coupled with TiO2 on the characteristics and properties of TiO2, as well as the impact of the TiO2/CuS/GQDs combination on the degradation of organic cyanide compounds. This study involves various experiments, including the synthesis of TiO2, GQDs, CuS, and TiO2/CuS/GQDs nanocomposites with various fabrication methods using drop casting. The results of the XRD test of TiO2/CuS/GQDs nanocomposites are found at peaks 26.79o, 25.44o, 27.70o, 29.49o, 31.92o, 32.94o. The results of the FTIR test indicate the presence of functional groups in the composite material, namely C-S, Ti-O-Ti, Ti-O-C which indicate TiO2/CuS/GQDs nanocomposite material. The SEM test results show that the TiO2/CuS/GQDs composite is attached to nickel foam. Then the EDX results show elements such as Ti, O, C, Cu, S which indicate the TiO2/CuS/GQDs composite. The results of the Uv-Vis test on the composition variations produce an energy band gap of 2.91 eV, 2.51 eV, 3.05 eV which indicates that the CuS material has succeeded in reducing the band gap of the TiO2 material. The results of the photocatalytic test showed that the composition variation of 1;0.5;0.2 had an optimal degradation result of 91.83% in cyanide solution.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	CuS; Fotokatalis; GQDs; Sianida; TiO2 CuS; Cyanide; Photocatalytic; GQDs; TiO2
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure. Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Javier Nur Dewanto
Date Deposited:	06 Aug 2024 03:59
Last Modified:	06 Aug 2024 03:59
URI:	http://repository.its.ac.id/id/eprint/111152

Actions (login required)

View Item