Uji In Vitro Fotosensitizer Riboflavin Dikonjugasikan dengan Green Synthesis Nanopartikel Perak Pada Terapi Fotodinamika Sel Kanker Paru-paru A549

Arafani, Nadja Haliza (2024) Uji In Vitro Fotosensitizer Riboflavin Dikonjugasikan dengan Green Synthesis Nanopartikel Perak Pada Terapi Fotodinamika Sel Kanker Paru-paru A549. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201117-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (6MB) | Request a copy

Abstract

Nanopartikel perak (AgNPs) telah menjadi salah satu bahan nano yang digunakan dalam kemajuan bidang biomedis. Salah satu penggunaannya dalam bidang biomedis adalah sebagai fotosensitizer dalam terapi sel kanker. Penelitian kali ini dilakukan untuk mengevaluasi efektivitas dari larutan konjugat RF-AgNPs dalam terapi fotodinamika pada sel kanker paru-paru A549. Sintesis menggunakan bahan alam dilakukan untuk menghasilkan AgNPs yang menunjukkan puncak serapan pada rentang 422-428 nm. Analisis difraksi sinar-X menunjukkan struktur fasa kristal dari AgNPs adalah FCC. Dalam analisis SEM-EDX menunjukkan ukuran dari partikel berkisar antara 200-350 nm dan elemen lainnya yang terkandung dalam sampel. Analisis pada uji PSA diperoleh distribusi rata-rata ukuran partikel sebesar 419,6 nm dengan PdI 0,3711. Terapi fotodinamika dilakukan menggunakan LED sebagai sumber cahaya dengan panjang gelombang 440-445 nm. Dilakukan pengukuran viabilitas sel menggunakan metode reduksi resazurin. Hasil simulasi menunjukkan bahwa konjugat RF-AgNPs secara signifikan menurunkan viabilitas sel kanker. Diperoleh nilai IC50 sebesar 69,91 µM, yang menunjukkan adanya penuruna vaibilitas sel sebanyak 50%. Analisis mikroskopis menunjukkan adanya perubahan morfologi sel seperti penyusutan dan pembengkakan sel kanker. Konsentrasi RF-AgNPs yang lebih tinggi meningkatkan efek toksisitas yang ditunjukkan dengan penurunan kepadatan sel dan perubahan moroflogi yang signifikan. Penelitian ini mengindikasikan bahwa RF-AgNPs dapat menjadi salah satu agen fotosensitizer alternatif dalam terapi kanker paru-paru A549.
=======================================================================================================================================

Silver nanoparticles (AgNPs) have become one of the nanomaterials used in advancements in the biomedical field. One of their uses in biomedicine is as a photosensitizer in cancer cell therapy. This study aims to evaluate the effectiveness of RF-AgNP conjugate solution in photodynamic therapy on A549 lung cancer cells. The synthesis using natural materials was carried out to produce AgNPs, which showed an absorption peak at 422-428 nm. X-ray diffraction analysis showed that the crystal phase structure of the AgNPs is FCC. SEM-EDX analysis showed that the particle sizes ranged from 200 to 350 nm and identified other elements contained in the sample. Analysis of the PSA test obtained an average particle size distribution of 419.6 nm with a PdI of 0,3711. Photodynamic therapy was conducted using an LED light source with a wavelength of 440-445 nm. Cell viability measurements were peRFormed using the resazurin reduction method. The simulation results showed that RF-AgNP conjugates significantly reduced cancer cell viability. An IC50 value of 69,91 µM was obtained, indicating a 50% reduction in cell viability. Microscopic analysis showed morphological changes in cells such as shrinkage and swelling of cancer cells. Higher concentrations of RF-AgNPs increased the toxic effect, indicated by a decrease in cell density and significant morphological changes. This study indicates that RF-AgNPs can be an alternative photosensitizer agent in A549 lung cancer therapy.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	AgNPs, Reduksi Resazurin, SEM-EDX, UV-Vis, XRD ============================================================ AgNPs, Resazurin Reduction, SEM-EDX, UV-Vis, XRD
Subjects:	Q Science Q Science > QC Physics
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Nadja Haliza Arafani
Date Deposited:	07 Aug 2024 07:18
Last Modified:	07 Aug 2024 07:18
URI:	http://repository.its.ac.id/id/eprint/111685