Pengaruh Pemanasan Rendah Lapisan Komposit PANI/TiO₂ Pada Substrat Kaca ITO Sebagai Elektroda Kerja Terhadap Efisiensi DSSC

Zahira, Nasywa (2024) Pengaruh Pemanasan Rendah Lapisan Komposit PANI/TiO₂ Pada Substrat Kaca ITO Sebagai Elektroda Kerja Terhadap Efisiensi DSSC. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201145-Non_Degree.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (2MB) | Request a copy

Abstract

Pengembangan DSSC dalam pemanfaatan tenaga surya terus menjadi perhatian. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan polianilin dan pemanasan elektroda terhadap efisiensi DSSC. Penelitian dilakukan dengan menyintesis nanokomposit PANI/TiO₂ secara oksidatif kimia in situ. Elektroda kerja dideposisi pada substrat ITO menggunakan metode spray pyrolysis dengan larutan yang terdiri atas variasi komposit yang dilarutkan pada isopropanol. Substrat kemudian dipanaskan pada suhu 80 ᵒC sebelum direndam ke dalam pewarna sintesis alfalfa. Lapisan DSSC disusun dengan elektrolit diinjeksikan ke substrat elektroda kerja sebelum direkatkan dengan substrat elektroda balik yang dibuat dari karbon aktif. Pengujian solar simulator dilakukan untuk menilai efisiensi sel surya yang telah dibuat. Dari pengujian yang telah dilakukan, diperoleh nilai efisiensi untuk masing-masing elektroda kerja TiO₂, P/T (1/8), P/T (1/10), P/T (1/12) berturut-turut adalah 0,066%, 0,040%, 0,035% dan 0,023%. Hasil tersebut menunjukkan efisiensi menurun seiring bertambahnya jumlah polianilin. Melihat TiO₂ memiliki efisiensi tertinggi, pengujian dengan memanaskan elektroda kerja yang sama pada suhu yang berbeda dilakukan. Dari pengujian didapatkan bahwa nilai efisiensi DSSC dengan pemanasan 200 ᵒC sebesar 0,064%, sedangkan nilai efisiensi DSSC dengan pemanasan 80 ᵒC sebesar 0,066%. Hal ini membuktikan bahwa pemanasan pada elektroda kerja TiO₂ tidak memiliki pengaruh yang signifikan.
========================================================================================================================
The development of DSSC in utilizing solar energy had been an interest. The purpose of this research is to observe the effect of adding polyaniline and heating the electrode on the efficiency of DSSC. The research was carried out by synthesizing PANI/TiO₂ nanocomposites through in-situ oxidative chemical polymerization. The deposition of working electrode was done on the conductive surface of ITO substrate through the spray pyrolysis method using a solution consisted of composites variations dissolved in isopropanol. The substrate was then heated at 80 ᵒC before being soaked in alfalfa chlorophyll dye. The sandwich layer of DSSC is assembled by injecting electrolyte into the working electrode substrate before being sealed with a counter electrode substrate made of activated carbon. Solar simulator characterization is carried out to evaluate the efficiency of the solar cells. Based on the result analysis, the efficiency obtained for each variations of working electrode TiO₂, P/T (1/8), P/T (1/10), P/T (1/12) are 0.066%, 0.040%, 0.035% and 0.023% respectively. These results show that the efficiency decreases as the amount of polyaniline increases. As TiO₂ has the highest efficiency, using the same working electrode, characterization using different temperatures were carried out. Based on the result analysis, the efficiency of DSSC heated at 200 ᵒC was 0.064%, while the efficiency of DSSC heated at 80 ᵒC was 0.066%. This proves that heating the working electrode TiO₂ does not have a significant effect

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Celah pita, DSSC, Elektroda Kerja, Substrat ITO, Titanium Dioksida. Band Gap, DSSC, ITO Substrate, Titanium Dioxide, Working Electrode.
Subjects:	Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Nasywa Zahira
Date Deposited:	09 Aug 2024 06:23
Last Modified:	09 Aug 2024 06:23
URI:	http://repository.its.ac.id/id/eprint/112105