Komparasi Karakteristik Permukaan Material Pada Limbah Pemesinan Menggunakan Menggunakan Metode Metalurgi Serbuk

Raharjo, Yoga Kartiko (2024) Komparasi Karakteristik Permukaan Material Pada Limbah Pemesinan Menggunakan Menggunakan Metode Metalurgi Serbuk. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038201028-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (4MB) | Request a copy

Abstract

Saat menghasilkan produk melalui proses pemesinan, pasti akan terbentuk limbah berupa serbuk sisa yang belum dapat diproses kembali secara optimal. Dengan tujuan mengurangi volume limbah, serbuk sisa pemesinan dapat dimanfaatkan kembali melalui proses pengolahan. Tujuan utama dari penelitian ini adalah untuk mengevaluasi potensi penggunaan
ulang serbuk logam sisa pemesinan dalam produksi produk jadi. Hasil penelitian diharapkan dapat memberikan informasi yang berharga mengenai sifat mekanik dan struktur mikro yang
terbentuk dari serbuk logam tersebut, terutama dalam konteks variasi temperatur sintering. Perbandingan struktur mikro antara baja ST60 dan ketiga spesimen menunjukkan kesamaan dalam pembentukan pearlite dan ferrite, semakin tinggi temperatur sintering fasa yang terbentuk semakin ferrite. Dalam hal sifat mekanik, nilai kekerasan dan kekuatan tekan
baja ST60 lebih unggul dibandingkan ketiga spesimen dengan variasi temperatur sintering. Dari hasil perbandingan kekerasan material Baja ST60 dengan ketiga spesimen nilai
kekerasan tertingi terdapat pada spesimen dengan temperatur 1100℃ sebesar 65,1 HRB nilai ini mendekati nilai kekerasan dari Baja ST60 yang memiliki nilai kekerasan sebesar 80,6
HRB. . Dari hasil perbandingan kekuatan tekan material Baja ST60 dengan ketiga spesimen nilai kekuatan tekan tertingi terdapat pada spesimen dengan temperatur 1100℃ sebesar
73,293 N/mm2 nilai ini mendekati nilai kekuatan tekan dari Baja ST60 yang memiliki nilai kekuatan tekan sebesar 156,157 N/mm2. Dari hasil perbandingan kekasaran material Baja
ST60 antara dengan ketiga spesimen nilai kekasaran terendah terdapat pada spesimen dengan temperatur 1200℃ sebesar 7,058 Ra nilai ini mendekati nilai kekasaran dari Baja
ST60 yang memiliki nilai kekasaran sebesar 2,003 Ra

============================================================
If a product is produced through a machining process, waste will definitely form in the form of powder residue which cannot be reprocessed optimally. With the aim of reducing
the volume of waste, remaining machine powder can be reused through processing. The main aim of this research is to highlight the potential for reuse of machining waste metal powder in the production of finished products. The research results are expected to provide valuable information regarding the mechanical properties and microstructure
formed from metal powders, especially in the context of variations in sintering temperature. A comparison of the microstructure between ST60 steel and the three specimens
shows similarities in the formation of pearlite and ferrite. The higher the sintering
temperature, the more ferrite phase is formed. In terms of mechanical properties, the
hardness and compressive strength values of ST60 steel are superior to the three specimens
with varying sintering temperatures. From the hardness comparison results of ST60 steel
with the three specimens, the highest hardness value is found in the specimen with a
temperature of 1100℃ at 65.1 HRB, which is close to the hardness value of ST60 steel which
has a hardness value of 80.6 HRB. From the compressive strength comparison results of
ST60 steel with the three specimens, the highest compressive strength value is found in the
specimen with a temperature of 1100℃ at 73.293 N/mm2, which is close to the compressive
strength value of ST60 steel which has a compressive strength value of 156.157 N/mm2.
From the surface roughness comparison results of ST60 steel with the three specimens, the
lowest roughness value is found in the specimen with a temperature of 1200℃ at 7.058 Ra,
which is close to the roughness value of ST60 steel which has a roughness value of 2.003

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Limbah Sisa Pemesinan, Metalurgi Serbuk, Kompaksi, Sintering, Machining Waste, Powder Metallurgy, Compaction, Sintering
Subjects:	T Technology > T Technology (General) T Technology > TS Manufactures T Technology > TS Manufactures > TS205 Metals--Heat treatment.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Yoga Kartiko Raharjo
Date Deposited:	03 Aug 2024 02:43
Last Modified:	03 Aug 2024 02:46
URI:	http://repository.its.ac.id/id/eprint/112276

Actions (login required)

View Item