Sintesis Nano-Superabsorbent Polymer Berbasis Kitosan-Pektin Sebagai Absorben Logam Berat

Aditya, M Daffa (2024) Sintesis Nano-Superabsorbent Polymer Berbasis Kitosan-Pektin Sebagai Absorben Logam Berat. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004201104-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (5MB) | Request a copy

Abstract

Pencemaran logam berat merupakan salah satu masalah lingkungan yang serius akibat penggunaan zat beracun dalam industri, yang berdampak buruk pada ekosistem akuatik dan kesehatan manusia. Penanggulangan pencemaran logam berat dengan metode efektif dan ramah lingkungan diperlukan, salah satunya adalah dengan metode absorpsi menggunakan superabsorben polimer. Salah satu material yang potensial digunakan sebagai superabsorben polimer adalah kitosan. Namun, penggunaan kitosan untuk tujuan absorpsi logam tidak bisa digunakan dalam bentuk murninya. Maka dari itu, superabsorben polimer berbasis kitosan perlu dimodifikasi, salah satunya menggunakan pektin atau alginat untuk meningkatkan kemampuan absorpsi terhadap logam berat. Kemampuan absorpsi logam berat dapat ditingkatkan lagi dengan membuat superabsorben polimer dalam bentuk nano. Diharapkan dengan luas permukaan yang lebih besar membuat kemampuan absorpsinya lebih baik lagi. Penelitian ini bertujuan mensintesis dan Nano-SAP berbasis kitosan, termodifikasi oleh pektin dan alginat serta karakterisasi dan evaluasi swelling. Metode penelitian meliputi tahap sintesis Nano-SAP, karakterisasi menggunakan FTIR dan SEM, dan uji swelling. Nano-SAP berbasis kitosan termodifikasi pektin dan alginat berhasil disintesis. Hasil karakterisasi FT-IR mengkonfirmasi terjadi perubahan bilangan gelombang pada gugus O-H, C-H, C≡N, C=O, COO-, N-H, dan C-O, yang mengindikasikan bahwa Nano-SAP terbentuk. Hasil karakterisasi dengan SEM menunjukan bahwa Nano-SAP memiliki ukuran nano. Evaluasi kapasitas penyerapan dari Nano-SAP menunjukan hasil swelling terhadap ion Ni2+ optimum pada waktu 15 menit perendaman. Penelitian ini diharapkan dapat menjadi alternatif untuk penanggulangan logam berat yang lebih ekonomis dan ramah lingkungan.
================================================================================================================================
Heavy metal pollution is one of a serious environmental problems due to the use of toxic substances in industry, which heavily affects aquatic ecosystems and human health. Treatment of heavy metal pollution requires effective and environmentally friendly methods, one of which is absorption using superabsorbent polymers. A potential material used as an absorbent is chitosan. However, the use of chitosan for metal absorption purposes cannot be used in its pure form. Therefore, chitosanbased superabsorbent polymers should be modified with pectin or alginate to enhance the absorption ability of heavy metals. Absorption of heavy metals can be further enhanced by making the superabsorbent polymer in nano form. It is expected that the larger surface area can make the absorption ability even better. This study aims to synthesize Nano-SAP based on chitosan, modified by pectin and alginate as well as characterization and evaluation of its swelling ability. The research method includes the synthesis of Nano-SAP, characterization using FTIR and SEM, and swelling test. Nano-SAPs based on chitosan modified by pectin and alginate were successfully synthesized. FT-IR characterization results confirmed the shifts in the wavenumbers of O-H, C-H, C≡N, C=O, COO-, N-H, and C-O groups, indicating that Nano-SAP was formed. SEM characterization results showed that Nano-SAP has a nano size scale. Evaluation of the sorption capacity of Nano-SAP showed optimum swelling result of Ni2+ ions at 15 minutes of immersion. This research is expected to be an alternative for heavy metal treatment that is more economical and environmentally friendly.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Absorben, Pektin, Kitosan, Logam Berat, Nano-SAP, Absorbent, Pectin, Chitosan, Heavy Metals
Subjects:	Q Science > QD Chemistry T Technology > TP Chemical technology > TP1140 Polymers T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles. T Technology > TP Chemical technology > TP248.65.C55 Chitosan--Biotechnology.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	M Daffa Aditya
Date Deposited:	20 Aug 2024 04:02
Last Modified:	27 Aug 2024 08:19
URI:	http://repository.its.ac.id/id/eprint/113628

Actions (login required)

View Item