Pemanfaatan Tanaman Manjakani (Quercus infectoria Gall) sebagai Reduktor pada Sintesis Nanopartikel Emas

Muslih, Zulfa Syaifana (2024) Pemanfaatan Tanaman Manjakani (Quercus infectoria Gall) sebagai Reduktor pada Sintesis Nanopartikel Emas. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004201138-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (5MB) | Request a copy

Abstract

Nanopartikel emas (AuNP) berhasil disintesis dengan menggunakan tanaman manjakani atau Quercus infectoria Gall (QIG) sebagai agen pereduksi. Sintesis AuNP dilakukan dengan memvariasikan perbandingan larutan ion Au/ QIG sebesar 1:1, 2:1, 4:1, dan 8:1 serta pada variasi pH 1, 3, 5, 7, dan 9 untuk mengetahui pengaruhnya terhadap pembentukan dan morfologi AuNP. Pembentukan AuNP diidentifikasi dengan spektrofotometer UV-Vis, particle size analyzer (PSA), pengukur zeta, XRD, dan FESEM-EDX. Analisis UV-Vis menunjukkan bahwa AuNP memiliki absorbansi maksimum pada panjang gelombang 535 nm hingga 539 nm. Di antara variasi tersebut, pembentukan AuNP yang paling optimal diamati pada rasio 1:1 pH=7 yang ditandai dengan intensitas absorbansi AuNP yang tinggi disertai penurunan panjang gelombang yang berkorelasi dengan QIG. Hasil analisis PSA menunjukkan bahwa AuNP yang dihasilkan memiliki ukuran diameter rata-rata 94,97 nm yang juga dikonfirmasi oleh pengamatan FESEM-EDX. Pencitraan FESEM memverifikasi pembentukan morfologi cenderung bulat dan batang serta dihasilkan rata-rata diameter partikel sebesar 82,44 nm, sedangkan EDX memberikan validasi bahwa struktur tersebut merupakan unsur Au. Karakterisasi menggunakan XRD juga menunjukkan adanya kristal Au yang menjadi tanda keberhasilan terbentuknya AuNP pada hasil sintesis dengan bidang kristalnya yaitu FCC (1 1 1). AuNP memiliki zeta potensial -20,77 mV yang menunjukkan stabilitas nanopartikel. Penelitian ini terbukti dapat memberikan sintesis AuNP yang mudah dengan menggunakan agen pereduksi berupa QIG yang berasal dari bahan alam dan tidak berbahaya.
===================================================================================================================================
Gold nanoparticles (AuNPs) were successfully synthesized using manjakani plant or Quercus infectoria Gall (QIG) as a reducing agent. Synthesis of AuNPs was carried out by varying the volume ratio of Au ion/QIG solution by 1:1, 2:1, 4:1, and 8:1 and at pH variations of 1, 3, 5, 7, and 9 to determine the effect on the formation and morphology of AuNPs. The formation of AuNPs was identified by UV-Vis spectrophotometer, particle size analyzer (PSA), zeta meter, XRD, and FESEM-EDX. UV-Vis analysis shows that AuNPs have maximum absorbance at wavelengths of 535 nm to 539 nm. Among these variations, the most optimal formation of AuNPs was observed at 1:1 ratio pH=7 which was characterized by high absorbance intensity of AuNPs accompanied by a decrease in wavelength that correlated with QIG . PSA analysis results showed that the resulting AuNPs had an average diameter size of 94.97 nm which was also confirmed by FESEM-EDX observation. FESEM imaging verified the formation of spherical and rod morphology, and an average particle diameter is 82.44 nm. While EDX validates that the structure is Au elements. Characterization using XRD also showed the presence of Au crystals, which is a sign of the successful formation of AuNPs in the synthesis results with the Au crystal plane is FCC (1 1 1). AuNPs have a zeta potential of -20.77 mV which indicates the stability of nanoparticles. This research can provide a facile synthesis of AuNPs using a reducing agent in the form of QIG which is derived from natural and harmless materials.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Emas, Manjakani, Nanopartikel, Quercus infectoria Gall, Sintesis
Subjects:	Q Science > QD Chemistry
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Zulfa Syaifana Muslih
Date Deposited:	12 Aug 2024 08:37
Last Modified:	27 Aug 2024 07:14
URI:	http://repository.its.ac.id/id/eprint/114699

Actions (login required)

View Item