Adsorpsi Zat Warna Malasit Hijau Dengan Aluminosilikat Mesopori dari Lerak (Sapindus rarak) Sebagai Surfaktan Alami

Salsabila, Zahra (2024) Adsorpsi Zat Warna Malasit Hijau Dengan Aluminosilikat Mesopori dari Lerak (Sapindus rarak) Sebagai Surfaktan Alami. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 5004201088-Undergraduate_Thesis.pdf] Text
5004201088-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (4MB) | Request a copy

Abstract

Adsorben silika mesopori dengan surfaktan alami Sapindus rarak yang disintesis melalui metode sol-gel dan hidrotermal telah digunakan untuk adsorpsi malasit hijau. Sapindus rarak digunakan sebagai agen pengarah pori material yang ramah lingkungan. Dalam proses sintesis, digunakan HCl dengan variasi konsentrasi (0; 1; 1,5; 2; dan 3 M) untuk mengontrol karakteristik pori dan material hasil sintesis. Silika mesopori hasil sintesis dikarakterisasi dengan XRD, FTIR, FESEM, dan adsorpsi-desorpsi N2. Hasil XRD menunjukkan keberadaan silika amorf pada material pada 2θ sekitar 21-25°. Spektrum FTIR menunjukkan puncak serapan pada bilangan gelombang 1082 dan 960 cm-1 untuk mode vibrasi Si-O-Si sebagai spektra karakteristik material silika mesopori. Analisis dengan FESEM menunjukkan bahwa material silika mesopori memiliki morfologi awan cumulonimbus. Hasil fisisorpsi nitrogen sampel aluminosilikat mesopori konsentrasi HCl 0 M mempunyai luas permukaan eksternal sebesar 181,59 m2/g dengan diameter pori 3,78 nm. Penerapan material silika mesopori sebagai adsorben malasit hijau menunjukkan kapasitas adsorpsi sebesar 111,11 mg/g pada adsorben silika mesopori. Seluruh sampel menunjukkan kesesuaian terhadap kinetika orde dua semu. Isoterm Langmuir tepat untuk menggambarkan mekanisme adsorpsi monolayer.

Kata kunci: Adsorpsi, Aluminosilikat mesopori, HCl, Malasit hijau, Sapindus rarak
========================================================================================================================
Mesoporous silica adsorbent with natural surfactant Sapindus rarak synthesised by sol-gel and hydrothermal methods has been used for the adsorption of malachite green. Sapindus rarak is used as an eco-friendly pore-directing agent. In this synthesis process, HCl with varying concentrations (0; 1; 1.5; 2; and 3 M) is used to control the pore characteristics and properties of the synthesized material. The synthesised mesoporous silica was characterised by XRD, FTIR, FESEM, and N2 adsorption-desorption. The XRD results indicate the presence of amorphous silica in the material at 2θ around 21-25°. The FTIR spectrum shows absorption peaks at wavenumbers 1082 and 960 cm-1 for Si-O-Si vibration modes, characteristic of mesoporous silica material. FESEM analysis shows shows that the mesoporous silica material has a cumulonimbus cloud morphology. Nitrogen physisorption results of the mesoporous aluminosilicate sample with 0 M HCl concentration show an external surface area of 181.59 m²/g with a pore diameter of 3.78 nm. The application of mesoporous silica material as an adsorbent for malachite green shows an adsorption capacity of 111.11 mg/g for mesoporous silica adsorbent. All samples conform to pseudo-second-order kinetics. The Langmuir isotherm is suitable for describing the monolayer adsorption mechanism.

Keywords: Adsorption, Mesoporous aluminosilicate, HCl, Malachite green, Sapindus rarak

Item Type: Thesis (Other)
Uncontrolled Keywords: Adsorpsi, Aluminosilikat mesopori, HCl, Malasit hijau, Sapindus rarak Adsorption, Mesoporous aluminosilicate, HCl, Malachite green, Sapindus rarak
Subjects: Q Science > QD Chemistry > QD181.S6 A4 Aluminum silicates
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Zahra Salsabila
Date Deposited: 12 Aug 2024 03:27
Last Modified: 12 Aug 2024 03:27
URI: http://repository.its.ac.id/id/eprint/114747

Actions (login required)

View Item View Item