Pengaruh Variasi Arus Pada Proses Pengelasan Dissimilar Baja Karbon Rendah ASTM A36 Dan Baja Karbon Menengah AISI 1045 Terhadap Kekerasan, Struktur Mikro, Dan Kekuatan Impak

Lumban Toruan, Feliks Agustinus Mulatua (2024) Pengaruh Variasi Arus Pada Proses Pengelasan Dissimilar Baja Karbon Rendah ASTM A36 Dan Baja Karbon Menengah AISI 1045 Terhadap Kekerasan, Struktur Mikro, Dan Kekuatan Impak. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 2038201054-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Baja karbon merupakan material yang banyak digunakan dalam industri perkapalan, konstruksi bangunan, serta dalam industri minyak dan gas. Dalam perkembangannya penyambungan antar material sudah dilakukan dengan jenis logam berbeda. Namun yang sangat sering dilakukan dalam dunia industri kapal dan migas yaitu pengelasan dissimilar antara baja karbon dengan grade material yang berbeda. Seperti pembuatan H beem, Sepatu es pada kapal, dan konstruksi jacket pada industri minyak dan gas.
Pada penelitian ini material yang digunakan pada proses pengelasan dissimilar adalah Baja karbon rendah ASTM A36 dan Baja karbon sedang AISI 1045 dengan variasi arus 80A, 100A, dan 120A menggunakan jenis pengelasan SMAW. Pengujian yang dilakukan adalah uji kekerasan, uji impak, dan uji metalografi untuk mengetahui nilai kekerasan, energi impak, dan struktur mikro akibat arus pengelasan.
Berdasarkan hasil pengujian diketahui bahwa dengan bertambahnya arus pengelasan memberikan dampak kepada naiknya nilai kekerasan pada area HAZ dan weld metal dengan nilai paling tinggi pada area weld metal dari arus 120A sebesar 59.6HRB, arus 100A 58.3HRB dan paling rendah terdapat pada arus 80A 55.6HRB. Arus pengelasan juga berdampak pada energi impak yang menurun seiring meningkatnya arus pengelasan 80A,100A, dan 120A secara beruturut (144,2J/ , 143,8J, 140,4J). Pada pengujian struktur mikro ukuran grain size pada area weld metal dari arus 80A, 100A, dan 120A masing-masing secara berturut yaitu 89 μm2 , 89 μm2, dan 126 μm2.
=================================================================
Carbon steel is a material that is widely used in the shipping industry, building construction, and in the oil and gas industry. In its development, the connection between materials has been carried out with different types of metal. However, what is very often done in the ship and oil and gas industry is dissimilar welding between carbon steel with different material grades. Such as the manufacture of H beems, ice shoes on ships, and jacket construction in the oil and gas industry.
In this study, the materials used in the dissimilar welding process are ASTM A36 low carbon steel and AISI 1045 medium carbon steel with a current variation of 80A, 100A, and 120A using the SMAW welding type. The tests carried out are hardness test, impact test, and metallographic test to determine the value of hardness, impact energy, and microstructure due to welding current.
Based on the test results, it is known that the increase in welding current has an impact on the increase in hardness values in the HAZ and weld metal areas with the highest value in the weld metal area of 120A current of 59.6HRB, 100A current 58.3HRB and the lowest is at 80A current 55.6HRB. The welding current also has an impact on impact energy which decreases as the welding current increases 80A, 100A, and 120A sequentially (144.2J/, 143.8J, 140.4J). In microstructure testing, the grain size in the weld metal area of the 80A, 100A, and 120A currents are 89 μm2, 89 μm2, and 126 μm2.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Baja Karbon, Dissimilar, SMAW, Kekerasan, Uji Impak, Metalografi, Carbon steel, Dissimilar, SMAW, Hardness, Impact Strength, Metalografi
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	FELIKS AGUSTINUS MULATUA LUMBAN TORUAN
Date Deposited:	08 Aug 2024 11:35
Last Modified:	08 Aug 2024 11:35
URI:	http://repository.its.ac.id/id/eprint/114780