Shobah, Fatimah Nurus (2024) Sintesis Nanopartikel Tembaga menggunakan Tanaman Manjakani sebagai Agen Pereduksi. Other thesis, Institut Teknologi Sepuluh Nopember.
Text
5004201099-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (3MB) | Request a copy |
Abstract
Nanopartikel tembaga (CuNPs) telah banyak disintesis menggunakan tanaman sebagai agen pereduksi, namun umumnya CuNPs yang dihasilkan berbentuk bulat (spherical) atau berdimensi nol dimensi (0-D). CuNPs dengan bentuk selain bulat (spherical) perlu dikembangkan lagi karena memiliki luas permukaan yang lebih luas sehingga dapat memiliki potensi lebih besar untuk diaplikasikan dalam berbagai bidang. Pada penelitian ini CuNPs disintesis menggunakan Quercus infectoria Gall (QIG) sebagai agen pereduksi. Proses sintesis dilakukan dengan variasi rasio logam (Cu(NO3)2.3H2O) terhadap QIG 1:1, 2:1, 4:1, 8:1 dan variasi pH 5, 7, 9, 11 untuk mengetahui kondisi paling optimal dalam sintesis CuNPs menggunakan QIG. CuNPs hasil sintesis dikarakterisasi menggunakan Spektrofotometer UV-Vis. Hasil spektra UV-Vis menunjukkan adanya puncak pada panjang gelombang maksimum 320-325 nm, yang menunjukkan CuNPs telah berhasil terbentuk. Berdasarkan analisis spektra UV-Vis variasi paling optimal untuk pembentukan CuNPs adalah 2:1 dan pH 7 karena memiliki absorbansi paling tinggi dan tidak ada puncak QIG yang muncul. CuNPs variasi 2:1 pH 7 selanjutnya dikarakterisasi menggunakan PSA-Zeta, XRD dan FESEM-EDX. Hasil analisis PSA-Zeta menunjukkan CuNPs memiliki ukuran rata-rata 149,4 nm dengan nilai potensial zeta -22,46 mV. Hasil analisis XRD menunjukkan bahwa tembaga yang terbentuk adalah CuO. Sementara itu, hasil pengamatan dengan FESEM-EDX menunjukkan bahwa partikel CuNPs memiliki bentuk batang dengan persebaran QIG dipermukaannya. Namun, hasil XRD yang mengkonfirmasi pembentukan CuO mengindikasikan bahwa partikel tembaga tidak terlingkupi seluruhnya oleh QIG sehingga dapat teroksidasi oleh udara.
=================================================================================================================================
Copper nanoparticles (CuNPs) have been widely synthesized using plant as reducing agents, but generally the CuNPs produced is spherical or zero-dimensional (0-D). CuNPs with a shape other than spherical needs to be developed again because it has a wider surface area so that it can have greater potential to be applied in various fields. In this study, CuNPs were synthesized using Quercus infectoria Gall (QIG) as a reducing agent. The synthesis process was carried out with variations ratio of copper solution (Cu(NO3)2.3H2O) with QIG 1:1, 2:1, 4:1, 8:1 and pH variations of 5, 7, 9,11 to determine the most optimal conditions in CuNPs synthesis using QIG. The synthesized CuNPs was characterized using a UV-Vis Spectrophotometer. The results of the UV-Vis spectra show the presence of a peak at a maximum wavelength of 320-325 nm, which indicates that CuNPs has successfully formed. Based on UV-Vis spectral analysis, the most optimal variation for CuNPs formation is 2:1 and pH 7 because it has the highest absorbance and no QIG peaks appear. The 2:1 pH 7 variation CuNPs was further characterized using PSA-Zeta, XRD and FESEM-EDX. The results of PSA-Zeta analysis showed that CuNPs had an average size of 149.4 nm with a zeta potential value of -22.46 mV. The results of XRD analysis show that the copper formed is CuO. Meanwhile, the results of observations with FESEM-EDX show that CuNPs particles have a bar shape with a distribution of QIG on their surface. However, XRD results confirming the formation of CuO indicate that copper particles are not completely covered by QIG and can be oxidized by air.
Item Type: | Thesis (Other) |
---|---|
Uncontrolled Keywords: | Manjakani, Nanopartikel, Tembaga, Copper, Nanoparticle, Quercus infectoria Gall |
Subjects: | Q Science > QD Chemistry |
Divisions: | Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis |
Depositing User: | Fatimah Nurus Shobah |
Date Deposited: | 14 Aug 2024 02:02 |
Last Modified: | 14 Aug 2024 02:02 |
URI: | http://repository.its.ac.id/id/eprint/114793 |
Actions (login required)
View Item |