Pengembangan Komposit Bone Graft Berbasis Kitosan-Pmma-Hidroksiapatit Scaffold Pada Properties

Livanrio, Edric (2022) Pengembangan Komposit Bone Graft Berbasis Kitosan-Pmma-Hidroksiapatit Scaffold Pada Properties. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000049-Undergraduate_Thesis.pdf Download (2MB)

Abstract

Bone graft scaffold merupakan salah satu solusi yang digunakan untuk penyembuhan tulang dari fraktur yang disebabkan kecelakaan ataupun dari osteoporosis. Selain itu, scaffold sekarang telah menjadi salah satu pemasukan besar pada pasar global dan banyak dikembangkan dengan bahan-bahan alami. Bahan scaffold yang digunakan berupa hidroksiapatit tulang sapi yang difabrikasi sendiri menggunakan microwave dengan daya 800 watt selama 70 menit, kitosan dan PMMA, dimana setiap bahan yang memiliki keunggulan masing – masing. Tujuan dilakukan penelitian ini adalah untuk mengetahui dampak penambahan dari PMMA serta HAp terhadap sifat dari scaffold. Dari hasil pengujian yang dilakukan diketahui bahwa teknik solvent casting particulate leaching dapat digunakan dalam pembuatan scaffold berpori yang dapat dilihat pada hasil pengamatan pada mikroskop stereotype, yang mana terbentuk pori dengan menggunakan porogen NaCl. Pori – pori yang terbentuk ini kemudian diukur porositasnya dengan menggunakan metode liquid displacement test, dimana seiring dengan kenaikan PMMA menyebabkan penurunan pada nilai porositas. Penurunan nilai porositas ini juga mempengaruhi sifat tekan dari scaffold. Dengan penurunan nilai porositas ini akan menyebabkan kenaikkan pada nilai kekuatan tekan dari scaffold, yang secara berurut dengan rasio scaffold HAp:PMMA:kitosan 56:40:4; 61:35:4; 66:30:4 menghasilkan kekuatan tekan sebesar 38,39; 37,61; 35,61 N/mm2. Walaupun sifat mekanik dari scaffold menurun seiring dengan penurunan Hidroksiapatit, tetapi sifat antibakteri dari scaffold meningkat seiring dengan kenaikan hidroksiapatit, dan juga dengan penambahan dari HAp ini dapat memberikan peningkatan nilai viabilitas dari scaffold, yang didapatkan rasio scaffold HAp:PMMA:kitosan 66:30:4 memiliki nilai viabilitas tertinggi yaitu 64,18%.
================================================================================================================================
Bone graft scaffold is one of the solutions used for healing bones from fractures caused by accidents. In addition, scaffold has now become one of the largest revenues in the global market and is widely developed with natural materials. The scaffold material used are consist of self�fabricated bovine hydroxyapatite using a microwave with a power of 800 watts for 70 minutes, chitosan and PMMA, where each material has its own advantages. The purpose of this research was to determine the impact of the addition of PMMA and HAp on the nature of the scaffold From the results of the tests carried out, it is known that the solvent casting particulate leaching technique can be used in the manufacture of porous scaffolds which can be seen in the results of observations on stereotype microscopes, which form pores using porogen NaCl. The pores formed are then measured by porosity using the liquid displacement test method, which along with the increase in PMMA causes a decrease in the porosity value. This decrease in porosity value also affects the compressive properties of the scaffold. With a decrease in the value of porosity this will cause an increase in the value of the compressive strength of the scaffold, which is in order with the ratio of the scaffold HAp:PMMA:chitosan 56:40:4; 61:35:4; 66:30:4 yielded a compressive density of 38.39; 37,61; 35.61 N/mm2. Although the mechanical properties of the scaffold decrease along with the decrease in hydroxyapatite, the antibacterial properties of the scaffold increase along with the increase in hydroxyapatite, and also with the addition of this HAp can provide an increase in the viability value of the scaffold, which obtained the ratio of scaffold HAp: PMMA: chitosan 66: 30: 4 has the highest viability value of 64.18%.

Item Type:	Thesis (Other)
Additional Information:	RSMt 620.118 Liv p-1 2022
Uncontrolled Keywords:	Hidroksiapatit, kitosan, PMMA, Scaffold, Solvent casting/Particulate Leaching
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	16 Dec 2024 05:46
Last Modified:	16 Dec 2024 05:46
URI:	http://repository.its.ac.id/id/eprint/115984