Analisis Pengaruh Penggunaan Spent Bleaching Earth Terproses dengan Semen OPC dan PCC Terhadap Sifat Karakteristik Mortar

Tambunan, Marvel Hotleif (2025) Analisis Pengaruh Penggunaan Spent Bleaching Earth Terproses dengan Semen OPC dan PCC Terhadap Sifat Karakteristik Mortar. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5012201177-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2027. Download (23MB) | Request a copy

Abstract

Menurut lembaga penelitian Chatham House, semen adalah sumber dari sekitar 8% emisi karbon dioksida (CO2) yang ikut terlibat dalam terjadinya efek rumah kaca. Laporan terbaru Status Global 2022 menemukan sektor Bangunan dan Konstruksi menyumbang lebih dari 34 persen dari permintaan energi dan sekitar 37 persen dari energi dan emisi CO2 terkait proses tersebut pada tahun 2021. Emisi CO2 terkait energi operasional sektor ini mencapai sepuluh gigaton setara CO2 – lima persen di atas tingkat tahun 2020 dan dua persen di atas puncak pra-pandemi pada tahun 2019. Oleh karena keterlibatan konstruksi yang besar terjadinya efek rumah kaca. Dalam perkembangannya, berbagai penelitian telah dilakukan untuk menginovasikan pembuatan bahan baku konstruksi yang lebih ramah lingkungan. Salah satunya adalah pemanfaatan limbah yang tidak terpakai atau limbah yang dapat diolah menjadi bahan pembuatan alat dan bahan konstruksi. Dalam penelitian ini dilakukan replacement bahan baku semen dengan limbah terproses yang disebut Spent Bleaching Earth dengan persentase tertentu yang dapat dipakai kembali menjadi bahan baku konstruksi, juga mengurangi dampak konstruksi pada kondisi lingkungan. Tipe semen yang akan dilakukan pengetesan yaitu menggunakan tipe semen Ordinary Portland Cement (OPC) dan Portland Composite Cement (PCC). Metode yang dipakai adalah menggunakan treatment terdahulu pada SBE menjadi PSBE (Post-treated Spent Bleaching Earth). Sampel yang digunakan untuk pengetesan yaitu mortar beton. Lalu dilanjutkan pengetesan dengan acuan American Society for Testing and Materials (ASTM). Variabel yang ditentukan yaitu persentase replacement SBE dan umur pengetesan mortar beton. Hasil dari pengetesan tersebut menunjukkan bahwa kekuatan mortar semen yang diberikan campuran PSBE cenderung akan memiliki penurunan kekuatan dibandingkan dengan mortar semen OPC dan PCC pada umumnya. Namun dari hasil tersebut masih dapat dikategorikan dalam mortar yang dapat diaplikasikan dalam klasemen mortar tertentu.
==============================================================================================================================
Cement is the source of around 8% of carbon dioxide (CO2) emissions which are involved in the greenhouse effect according to the Chatham House research institute. The latest Global Status 2022 report found the Building and Construction sector accounted for more than 34 percent of energy demand and around 37 percent of energy and process related CO2 emissions in 2021. The sector's operational energy-related CO2 emissions reached ten gigatons of CO2 equivalent – five percent in above 2020 levels and two percent above the pre-pandemic peak in 2019. Due to the large construction involvement there is a greenhouse effect. In its development, various research has been carried out to innovate the manufacture of construction raw materials that are more environmentally friendly. One of them is the use of unused waste or waste that can be processed into tools and construction materials. In this research, cement raw materials were replaced with processed waste called Spent Bleaching Earth with a certain percentage which can be reused as construction raw materials, also reducing the impact of construction on environmental conditions. The type of cement that will be tested is Ordinary Portland Cement (OPC) dan Portland Composite Cement (PCC).cement types. The method used is to use the previous treatment on SBE to become PSBE (Post-treated Spent Bleaching Earth). The sample used for testing was concrete mortar. Then testing continued with American Society for Testing and Materials (ASTM) references and limits, namely measuring compressive strength, hydration temperature and setting time of concrete mortar. The variables determined are the percentage of SBE replacement and the age of concrete mortar testing. The results of these tests show that the strength of the cement mortar given the PSBE mixture tends to have a decrease in strength compared to OPC and PCC cement mortars in general. However, these results can still be categorized into mortars that can be applied in certain mortar classifications.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	SBE, PSBE, Mortar, Quality, Percentage, Kualitas, Persentase
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) T Technology > TA Engineering (General). Civil engineering (General) > TA433 Strength of materials.
Divisions:	Faculty of Civil, Planning, and Geo Engineering (CIVPLAN) > Civil Engineering > 22201-(S1) Undergraduate Thesis
Depositing User:	Marvel Hotleif Tambunan
Date Deposited:	03 Feb 2025 05:42
Last Modified:	03 Feb 2025 05:42
URI:	http://repository.its.ac.id/id/eprint/117798

Actions (login required)

View Item