Pengaruh Logam Ca dan Zn Terhadap Kinerja Pelumas Pada Berbagai Grade

Nada, Alisa Khothrun (2025) Pengaruh Logam Ca dan Zn Terhadap Kinerja Pelumas Pada Berbagai Grade. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004201105-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2027. Download (687kB) | Request a copy

Abstract

Pelumas adalah zat kimia, biasanya berbentuk cairan, yang sangat penting untuk semua komponen mesin yang bergerak antara dua atau lebih permukaan guna mengurangi gesekan. Dengan demikian, komponen-komponen penting tersebut dapat beroperasi dengan optimal dan memiliki umur yang lebih panjang. Metode yang digunakan pada penelitian ini yaitu bahan pelumas dengan berbagai grade untuk melihat pengaruh logam Ca dan Zn terhadap kinerja pelumas. Karakterisasi yang digunakan pada penelitian ini yaitu FTIR dan XRF serta pengujian yang dilakukan meliputi densitas, kadar air, korosi, dan viskositas kinematik. Pada penelitian tugas akhir ini telah dilakukan pengujian pada produk pelumas A, B, C, dan D meliputi pengujian XRF, FTIR, densitas, kadar air, korosi, dan viskositas kinematik yang bertujuan untuk mengetahui pengaruh pelumas pada berbagai grade. Hasil pada penelitian ini menunjukkan bahwa produk pelumas B memiliki kualitas terbaik karena mengandung logam Ca paling banyak diantara produk pelumas lainnya yaitu sebesar 1,0869%. Selain itu, produk pelumas B juga unggul dalam parameter viskositas, densitas, dan kemampuan menahan korosi dibandingkan ketiga produk lainnya dengan nilai berturut-turut 140,438 mm2/s; 0,9032 g/cm3; 1a.
==============================================================================================================================
Lubricants are chemical substances, usually in liquid form, that are essential for all machine components that move between two or more surfaces to reduce friction. Thus, these important components can operate optimally and have a longer life. The method used in this research is lubricating materials with various grades to see the effect of Ca and Zn metals on lubricant performance. The characterization used in this research is FTIR and XRF and the tests carried out include density, water content, corrosion, and kinematic viscosity. In this final project research, tests have been carried out on lubricant products A, B, C, and D including XRF, FTIR, density, moisture content, corrosion, and kinematic viscosity testing which aims to determine the effect of lubricants on various grades. The results in this study show that lubricant product B has the best quality because it contains the most Ca metal among other lubricant products, which is 1.0869%. In addition, lubricant product B also excels in viscosity, density, and corrosion resistance parameters compared to the other three products with consecutive values of 140.438 mm2/s; 0.9032 g/cm3; 1a.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	FTIR, Korosi, Pelumas, Viskositas, XRF
Subjects:	Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Alisa Khothrun Nada
Date Deposited:	03 Feb 2025 21:49
Last Modified:	03 Feb 2025 21:49
URI:	http://repository.its.ac.id/id/eprint/118029