Studi Eksperimen Pengaruh Konsentrasi Hcl Dan Waktu Imersi Terhadap Laju Korosi Pada Material Baja Paduan

Fathofani, Aziiz (2025) Studi Eksperimen Pengaruh Konsentrasi Hcl Dan Waktu Imersi Terhadap Laju Korosi Pada Material Baja Paduan. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 10211810010037-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2027. Download (3MB) | Request a copy

Abstract

Korosi adalah terjadinya perusakan material khususnya logam akibat lingkunganya. Korosi pada logam diakibatkan karena terjadinya reaksi kimia yaitu pada temperatur tinggi antara logam dan gas ataupun bisa terjadi korosi elektrokimia dalam lingkungan air atau udara yang lembab. Penyebab dari korosi yang dipengaruhi oleh senyawa larutan tertentu akan mengakibatkan nilai laju korosi serta pengaruh yang berbeda. Pemilihan dari larutan tersebut untuk mengetahui dari tingkatan korosi yang berpengaruh pada material baja yang dapat digunakan sebagai acuan untuk penggunaan material tersebut dalam sistem industri. Permasalahan korosi dapat mengakibatkan bertambahnya potensi pencemaran oleh gas terhadap lingkungan akibat kegiatan eksplorasi dan eksploitasi berlangsung, seringkali terjadi kerusakan pada pipa yang bisa jadi diindikasikan karena bahan pipa penyalur itu sendiri, kerusakan tersebut antara lain akibat korosi. Berdasarkan pengamatan visual jenis korosi yang terjadi dari pengujian weight loss dan polarisasi potensio dinamik siklik adalah korosi sumuran. Hasil dari penelitian ini didapatkan nilai laju korosi terendah pada spesimen dengan nilai keasaman 0,5 M dan waktu imersi selama 90 menit dengan menghasilkan nilai laju korosi sebesar 22,915 mmpy, kemudian untuk nilai laju korosi tertinggi terletak pada pengujian dengan nilai keasaman 2,5M Molar dengan waktu imersi selama 30 menit yang menghasilkan nilai laju korosi sebesar 198,19 mmpy. Dan juga perbesaran dari kondisi visual dan pengujian SEM perbesaran 200x hingga 2000x
====================================================================================================================================
Corrosion is the destruction of materials, especially metals, due to their environment. Corrosion of metals is caused by chemical reactions, namely at high temperatures between metals and gases or electrochemical corrosion can occur in humid water or air environments. The cause of corrosion influenced by certain solution compounds will result in different corrosion rate values and effects. The selection of the solution is to determine the level of corrosion that affects the steel material which can be used as a reference for the use of the material in industrial systems. Corrosion problems can result in increased potential for gas pollution to the environment due to ongoing exploration and exploitation activities, often there is damage to the pipe which can be indicated because of the pipe material itself, the damage is due to corrosion, among others. Based on visual observations, the type of corrosion that occurs from the weight loss test and cyclic dynamic potentiometer polarization is pitting corrosion. The results of this study obtained the lowest corrosion rate value in specimens with an acidity value of 0.5 M and an immersion time of 90 minutes by producing a corrosion rate value of 22.915 mmpy, then for the highest corrosion rate value is in the test with an acidity value of 2.5M Molar with an immersion time of 30 minutes which produces a corrosion rate value of 198.19 mmpy. And also the magnification of the visual conditions and SEM testing magnification of 200x to 2000x

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Korosi, Weight Loss, Imersi, Konsentrasi Larutan, Baja Paduan
Subjects:	Q Science > QD Chemistry > QD251.2 Chemistry, Organic. Biochemistry Q Science > QD Chemistry > QD471 Chemical compounds - Structure and formulas V Naval Science > V Naval Science (General)
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Aziiz Fathofani
Date Deposited:	04 Feb 2025 01:34
Last Modified:	04 Feb 2025 01:34
URI:	http://repository.its.ac.id/id/eprint/118057

Actions (login required)

View Item