Pengaruh Variasi Temperatur Dan Media Pendingin Step Quench Pada Proses Solution Treatment Paduan Cu-15,9Zn-6,89Al Terhadap Struktur Mikro Dan Kekerasan

Akbar, Marzuki (2022) Pengaruh Variasi Temperatur Dan Media Pendingin Step Quench Pada Proses Solution Treatment Paduan Cu-15,9Zn-6,89Al Terhadap Struktur Mikro Dan Kekerasan. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000108_UndergraduateThesis.pdf Download (5MB)

Abstract

Paduan Cu-Zn-Al merupakan salah satu paduan shape memory alloy yang memiliki kemampuan untuk kembali ke bentuk semula setelah mengalami deformasi dengan proses pemanasan hingga melewati temperatur transformasinya. Paduan yang digunakan dalam penelitian ini adalah Cu-15,9Zn-6,89Al. Paduan didapat dengan proses pengecoran yang kemudian diikuti dengan perlakuan panas homogenizing, annealing, dan solution treatment selama 10 menit dengan variasi temperatur 750oC, 800oC, dan 850oC. Proses quench yang dilakukan setelah solution treatment menggunakan metode step quench dengan variasi media pendingin oli dan air pada temperatur 100oC selama 10 menit. Selanjutnya dianalisis terkait perlakuan tersebut terhadap struktur mikro dan kekerasan dari paduan Cu-15,9Zn-6,89Al. Struktur mikro yang terbentuk pada seluruh spesimen adalah α, β, dan  tanpa adanya fasa martensit (β’). Tidak terbentuknya β’ (martensit) dikarenakan temperatur martensite start (Ms) berada di bawah temperatur ruang. Diameter ukuran butir terbesar adalah 163,49 μm yang terdapat pada spesimen SQWB 850 dan terkecil adalah 112,41 μm yang terdapat pada spesimen SQWB 750. Hal tersebut terjadi dikarenakan semakin tinggi temperatur solution treatment yang digunakan membuat ukuran butir semakin besar. Nilai kekerasan tertinggi adalah 271,33 ± 2,08 HVN yang terdapat pada spesimen SQOB 750 dan terendah adalah 257,67 ± 3,06 HVN yang terdapat pada spesimen SQWB 850. Media pendingin air memiliki laju pendinginan yang lebih lambat jika dibandingkan dengan oli pada step quench menggunakan temperatur 100oC selama 10 menit. Laju pendinginan yang lambat dan diameter butir yang besar membuat kekerasan semakin rendah.
====================================================================================================================================
The Cu-Zn-Al alloy is one of the shape memory alloys which can return to its original shape after being deformed by heating until it passes the transformation temperature. The alloy used in this study was Cu-15,9Zn-6,89Al. The alloy is obtained by casting process which is then followed by heat treatment of homogenizing, annealing, and solution treatment for 10 minutes with temperature variations of 750oC, 800oC, and 850oC. The quenching process is carried out after the solution treatment using the step quench method with variations of oil and water cooling media at a temperature of 100oC for 10 minutes. Furthermore, it was analyzed related to the treatment of the microstructure and hardness of the Cu-15,9Zn-6,89Al alloy. The microstructures formed in all specimens are α, β, and  without the presence of martensite phase (β'). No formation of β' (martensite) because the martensite start temperature (Ms) is below room temperature. The diameter of the largest grain size is 163.49 m in the SQWB 850 specimen and the smallest is 112.41 m in the SQWB 750 specimen. This is because the higher the solution treatment temperature used, the larger the grain size. The highest hardness value is 271.33 ± 2.08 HVN found in the SQOB 750 specimen and the lowest is 257.67 ± 3.06 HVN found in the SQWB 850 specimen. Water cooling media has a slower cooling rate when compared to oil in step quench using a temperature of 100oC for 10 minutes. The slow cooling rate and large grain diameter make the hardness lower

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Cu-Zn-Al, Solution Treatment, Step-Quench, Variasi Temperatur, Media Pendingin, Struktur Mikro, Kekerasan, Solution Treatment, Step-Quench, Temperature Variation, Cooling Media, Microstructure, Hardness
Subjects:	T Technology > TS Manufactures > TS205 Metals--Heat treatment.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	10 Feb 2025 04:38
Last Modified:	10 Feb 2025 04:38
URI:	http://repository.its.ac.id/id/eprint/118588