Analisis Metode Pengujian Four Point Bending Untuk Material Komposit Serat Sisal Dan Kenaf Dengan Standard D6272 Menggunakan Metode Elemen Hingga

Vikrant, Vikrant (2022) Analisis Metode Pengujian Four Point Bending Untuk Material Komposit Serat Sisal Dan Kenaf Dengan Standard D6272 Menggunakan Metode Elemen Hingga. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111840000169-Undergraduate Thesis.pdf Download (22MB)

Abstract

Polusi merupakan salah satu permasalahan penting yang ada didunia. Polusi dapat menimbulkan pencemaran pada lingkungan. Salah satu solusi dari permasalahan polusi adalah dengan menggunakan green material. Green material merupakan material ramah lingkungan yang tidak memberikan dampak buruk pada lingkungan. Salah satu contoh dari green material adalah komposit alami. Komposit alami merupakan komposit yang menggunakan serat dari alam. Serat alami yang digunakan pada penelitian ini adalah serat sisal dan serat kenaf. Pada penelitian ini, akan dilakukan analisa pengaruh dari fraksi volume dan variasi arah serat antara serat sisal dan serat kenaf untuk mengetahui flexural properties dengan menggunakan pengujian fourpoint bending. Penelitian yang dilakukan berupa simulasi pada software ANSYS untuk memperoleh nilai dari total deformasi, tegangan flexural, tegangan geser, regangan serta flexural modulus dari kedua jenis serat. Penelitian akan dimulai dengan mencari data mengenai kedua jenis serat lalu melakukan simulasi four point bending hingga material komposit mengalami kegagalan untuk mendapatkan nilai flexural properties dari setiap seratmenggunakan variasi fraksi volume dan arah serat. Hasil penelitian yang didapat adalah kombinasi material komposit terbaik yaitu fraksi volume sebesar 40% dengan orientasi arah serat [(0°)2/(45°)2/(90°)2/(-45°)2/(0°)2]. Flexural properties terbaik dari variasi yang ada dimiliki oleh Serat Sisal-Epoxy Resin dengan nilai flexural stress sebesar 185,73 MPa, shear stresssebesar 30,23 MPa, pure flexural stress sebesar 170,9 MPa, total deformasi sebesar 7,5424 mm, Flexural Strain sebesar 0,035522 dan flexural modulus sebesar 6164,185 MPa.
==================================================================================================================================
Pollution is one of the most important problems in the world. Pollution can be defined as a compound that causes damage to the environment. As a solution, green materials such as natural composites with natural fibers can be used to reduce pollution problems in the world. This study focuses on sisal and kenaf fiber as the natural fibers. This research analyzes the fiber directions and volume fractions between sisal and kenaf fibers in determining flexural properties through fourpoint bending testing. This research is conducted in the form of simulation on ANSYS software to obtain the total value of deformation, flexural stress, shear stress, and strain as well as flexural modulus from both fibers. The first step of the research is looking for the data of sisal and kenaf fibers, followed by conducting the fourpoint bending simulation and when the composite material breaks, the value of flexural properties from each fiber is obtained through fiber directions and volume fractions. The result of the simulation is the material combination of the best composites which are volume fractions of 40% with the orientation of fiber directions (0°)2/(45°)2/(90°)2/(-45°)2/(0°)2]. The best flexural properties were from Sisal Fiber-Epoxy Resin with the value of flexural stress of 185,73 MPa, shear stress of 30,23 MPa, pure flexural stress of 170,9 MPa, total deformasi of 7,5424 mm, Flexural Strain of 0,035522 and flexural modulus of 6164,185 MPa

Item Type:	Thesis (Other)
Additional Information:	RSM 620.118 Vik a-1 2022
Uncontrolled Keywords:	serat sisal, serat kenaf, arah serat, fraksi volume, fourpoint bending, ANSYS, sisal fiber, kenaf fiber, fiber orientation angle, volume fraction, fourpoint bending
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	25 Feb 2025 06:40
Last Modified:	25 Feb 2025 06:40
URI:	http://repository.its.ac.id/id/eprint/118881

Actions (login required)

View Item