Analisis Pengaruh Pwht Terhadap Susunan Struktur Mikro Pada Sambungan Las Dissimilar Material ASTM A-105 & A387 Gr5 Dengan Buttering Inconel 625

Sembiring, Immanuel Richart Piterson (2025) Analisis Pengaruh Pwht Terhadap Susunan Struktur Mikro Pada Sambungan Las Dissimilar Material ASTM A-105 & A387 Gr5 Dengan Buttering Inconel 625. Masters thesis, Institute Teknologi Sepuluh November.

Text 6011231003-Master_Thesis.pdf Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Jumlah minyak bumi yang dihasilkan di Indonesia menunjukan adanya penurunan dari sisi lifting sehingga hal ini menyebabkan belum terpenuhinya pasokan minyak bumi untuk kebutuhan dalam negeri. Untuk menutupi kebutuhan dalam negri Dibutuhkan kegiatan Import dari negara pengahsil minyak Bumi seperti Arab Saudi dan sejumlah negara kawasan Africa. Harga dari minyak bumi sangatdipengaruhi oleh kandungan dari Sulfur dan TAN. Semakin rendah kandungan TAN dan Sulfur, semakin tinggi dari harga minyak bumi (sweet crude) dan sebaliknya, semakin tinggi kandungan sulfur dan TAN (sour crude) maka semakin ekonomis nilai minyak bumi tersebut. Oleh karena itu, Indonesia harus mulai mengembangkan teknologi pengolahan minyak bumi untuk mengolah tipe sour crude tentunya dengan mengupgrade material pada Industri Pengolahan Minyak Bumi dalam negeri atau Refinery dengan material pipa yang tahan terhadap kandungan Sulfur dan TAN yang tinggi agar tidak terjadinya korosi material yang disebabkan tingginya kandungan asam dari minyak bumi yang di olah. Penggunaan material yang berbeda antara Column dan Pipa membutuhkan teknik khusus dengan penerapan PWHT dan Penggunaan Buttering pada sambungan lasan. Oleh karena itulah penelitian mengambil topik Analisa Dampak PWHT Terhadap KualitasSambungan Lasan dengan Buttering Inconel 625 di Nozzle Outlet Crude Destilation Unit. Penelitian ini diawal oleh kasus ditemukan adanya Crack dan Incomplete Fusion pada sambungan lasan di Nozzle Outlet (Bottom product) unit Destilasiminyak bumi akibat pergantian tipe material pada Nozzle Column dan Pipa. Peneletian ini dilakukan untuk melihat dampak dari penggunaan Inconel buttering dengan perlakukan PWHT material dibandingkan hasil analisa Ansys sehingga melalui penelitian ini dapat menjadi masukan untuk design sambungan dissimilar terhadap penggunaan Buttering yang umum di gunakan pada Industri pengolahan Minyak Bumi. Dari penelitian yang dilakukan maka cooling rate temperature pada PWHT untuk DMW dapat diketahui sesuai dengan hasil peneliatian pendekatan Roshental & Schaeffler dibanding hasil Simulasi Ansys.
=============================================================================================================================================
The amount of petroleum produced in Indonesia shows a decrease in lifting, which causes the supply of petroleum for domestic needs to be unfulfilled. To cover domestic needs, import activities are needed from oil-producing countries such as Saudi Arabia and several countries in the African region. The price of petroleum is greatly influenced by the content of Sulfur and TAN. The lower the TAN and Sulfur content, the higher the price of petroleum (sweet crude) and vice versa, the higher the sulfur and TAN content (sour crude) the more economical the value of the petroleum. Therefore, Indonesia must start developing petroleum processing technology to process sour crude types, of course by upgrading materials in the domestic Petroleum Processing Industry or Refinery with pipe materials that are resistant to high Sulfur and TAN content so that there is no material corrosion caused by the high acid content of the processed petroleum. The use of different materials between Column and Pipe requires special techniques with the application of PWHT and the Use of Buttering on welded joints. That is why the study took the topic of Analysis of the Impact of PWHT on the Quality of Welded Joints with Inconel 625 Buttering at the Nozzle Outlet Crude Distillation Unit. This study was initiated by a case where Cracks and Incomplete Fusion were found at the weld joints at the Nozzle Outlet (Bottom product) of the petroleum Distillation unit due to changes in the type of material in the Nozzle Column and Pipe. This study was conducted to see the impact of the use of Inconel buttering with PWHT material treatment compared to the results of the Ansys analysis so that through this study it can be input for the design of dissimilar joints to the use of Buttering which is commonly used in the Petroleum processing Industry. From the research conducted, the cooling rate temperature on PWHT for DMW can be known according to the results of the Roshental & Schaeffler approach compared to the results of the Ansys Simulation.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Total Acid Number, rasio corrosion allowance,Sulfur Content, Ansys, Buttering, :Total Acid Number, rasio corrosion allowance,Sulfur Content, Ansys, Buttering
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User:	Immanuel Richart Piterson Sembiring
Date Deposited:	17 Jul 2025 07:27
Last Modified:	17 Jul 2025 07:28
URI:	http://repository.its.ac.id/id/eprint/119665