Pengaruh Heat Input Terhadap Porositas Hasil Pengelasan Sambungan Dengan Gmaw/Mig Untuk Aluminium 5083 H116

Irsyah, Rasheed Siddiq (2025) Pengaruh Heat Input Terhadap Porositas Hasil Pengelasan Sambungan Dengan Gmaw/Mig Untuk Aluminium 5083 H116. Other thesis, Institut Teknologi Sepuluh Nopember Surabaya.

Text 5046211025-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menyelidiki bagaimana variasi heat input mempengaruhi tingkat porositas dalam pengelasan aluminium 5083 H116 yang dilakukan dengan teknik Gas Metal Arc Welding (GMAW) atau Metal Inert Gas (MIG). Aluminium 5083 H116 banyak dimanfaatkan dalam berbagai aplikasi struktural, termasuk pembuatan kapal dan infrastruktur lepas pantai, berkat sifat tahan korosi dan kekuatannya. Namun, salah satu tantangan utama dalam pengelasan aluminium adalah masalah porositas, yang berpotensi melemahkan karakteristik mekanik dari sambungan yang dihasilkan. Variasi input panas sangat krusial dalam pembentukan porositas, di mana tingkat yang terlalu rendah atau tinggi dapat meningkatkan kemungkinan terbentuknya gas yang terperangkap di dalam logam cair. Metodologi penelitian ini menggunakan pendekatan experimental yang meliputi pengelasan plat aluminium 5083 H116 dengan melakukan variasi pada parameter heat input yang diatur melalui tegangan, arus, dan kecepatan pengelasan yang digunakan. Hasil pengelasan kemudian dianalisis menggunakan metode radiografi untuk mendeteksi adanya porositas, serta menggunakan metalografi optik untuk mempelajari struktur mikro dan makro dari sambungan tersebut. Uji mekanik seperti pengujian Tarik juga dilaksanakan untuk menilai karakteristik mekanik dari sambungan tersebut. Analisis statistik diterapkan untuk mengidentifikasi hubungan antara input panas dan tingkat porositas yang teramati. Diharapkan bahwa temuan penelitian ini dapat memberikan pemahaman mengenai parameter heat input yang optimal untuk mengurangi porositas, sehingga kualitas dan keandalan sambungan pengelasan aluminium 5083 H116 dapat meningkat. Penelitian ini juga bertujuan untuk memberikan sumbangsih terhadap pengembangan proses pengelasan yang lebih efektif dan efisien dalam konteks industri.
========================================================================================================================
This study aims to investigate how variations in heat input affect the level of porosity in 5083H116 aluminum welding performed using Gas Metal Arc Welding (GMAW) or Metal Inert Gas (MIG) techniques. 5083 H116 aluminum is widely used in various structural applications, including shipbuilding and offshore infrastructure, due to its corrosion resistance and strength. However, one of the main challenges in aluminum welding is the issue of porosity, which has the potential to weaken the mechanical characteristics of the resulting joint. Variations in heat input are crucial in the formation of porosity, where too low or high levels can increase the possibility of trapped gas in the molten metal. The methodology of this study is an experimental approach which includes welding 5083 H116 aluminum plates by varying the heat input parameters controlled by the voltage, current, and welding speed used. The welding results were then analyzed using radiography methods to detect porosity, and using optical metallography to study the micro and macro structures of the joint. Mechanical tests such as tensile testing were also carried out to assess the mechanical characteristics of the joint. Statistical analysis was applied to identify the relationship between heat input and the observed porosity levels. It is expected that the findings of this study can provide an understanding of the optimal heat input parameters to reduce porosity, so that the quality and reliability of aluminum 5083 H116 welding joints can be increased. This study also aims to contribute to the development of more effective and efficient welding processes in an industrial context.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	GMAW, Alumunium 5083 , Heat Input, Porositas, MIG, Aluminium 5083, Heat Input, Porosity
Subjects:	T Technology > T Technology (General) T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing. T Technology > TA Engineering (General). Civil engineering (General) > TA433 Strength of materials. T Technology > TA Engineering (General). Civil engineering (General) > TA480.A6 Aluminum alloys. T Technology > TA Engineering (General). Civil engineering (General) > TA492.W4 Welded joints
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Rasheed Siddiq Irsyah
Date Deposited:	23 Jul 2025 02:00
Last Modified:	23 Jul 2025 02:00
URI:	http://repository.its.ac.id/id/eprint/120651

Actions (login required)

View Item