PENGARUH VARIASI TEMPERATUR KALSINASI PADA SINTESA LITHIUM MANGAN OKSIDA DENGAN RASIO MOL Li/Mn 0,8 TERHADAP KEMAMPUAN ADSORPSI LITHIUM LUMPUR SIDOARJO

KISTIYANTO, WAHYU PERDANA (2016) PENGARUH VARIASI TEMPERATUR KALSINASI PADA SINTESA LITHIUM MANGAN OKSIDA DENGAN RASIO MOL Li/Mn 0,8 TERHADAP KEMAMPUAN ADSORPSI LITHIUM LUMPUR SIDOARJO. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2712100075-Undergraduate_Theses.pdf]
Preview
Text
2712100075-Undergraduate_Theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Indonesia kaya dengan sumber daya mineral dan
alamnya. Di Indonesia terdapat geothermal fluid yaitu Lumpur
Sidoarjo, yang menurut ilmuwan dari Jepang, Prof. Wataru
Tanikawa, Lumpur Sidoarjo mengandung unsur Lithium yang
besar dan dapat dimanfaatkan sebagai baterai. Dari berbagai
macam metode ekstraksi yang ada dipilih ialah metode adsorpsi
dengan Lithium Mangan Oksida Spinel sebagai adsorben. Proses
sintesis lithium mangan oksida dengan metode solid state reaction
dengan ratio mol Li/Mn adalah 0,8. Serbuk adsorben dikompaksi
dengan tekanan 4,358 kN/mm untuk membentuk pellet LMO.
Kemudian pellet LMO dikalsinasi dengan variasi temperatur
500ºC, 600 ºC dan 700 ºC. untuk mengeluarkan Lithium dari
adsorben dilakukan acid treatment didalam 1Liter HCL 0,5M
selama 24jam. Setelah itu untuk proses adsorpsi Lithium,
adsorben LMO dimasukkan ke 1Liter Lumpur Sidoarjo selama
24jam. Karakterisasi yang dilakukan meliputi; XRD, SEM dan
ICP. Morfologi yang terbentuk pada pellet adsorben dengan
variasi temperatur kalsinasi 500 ºC, 600 ºC dan 700 ºC adalah
irregular dan semakin tinggi temperatur kalsinasi maka semakin
besar ukuran rata-rata butirnya serta semakin kristalin. LMO 700
mempunyai kemampuan adsorpsi Lithium Lumpur Sidoarjo yang
paling baik dibanding adsorben lain, yaitu 29,8 mg/g.
=========
Indonesia is rich in mineral and natural resources. In
Indonesia there are Lumpur Sidoarjo geothermal fluid, which
according to scientists from Japan, Prof. Wataru Tanikawa,
Sidoarjo Mud contains large Lithium element and can be used as
batteries. From the various methods of extraction that is chosen is
the adsorption method with Lithium Manganese Oxide Spinel as
adsorbent.The synthesis of lithium manganese oxide by solid state
reaction method with a mole ratio Li / Mn was 0.8. Adsorbent
powder compacted with a pressure of 4.358 kN / mm to form
pellets LMO. LMO pellets then calcined at 500ºC temperature
variation, 600 ºC and 700 ºC. Lithium from the adsorbent to
remove the acid treatment done in 1liter 0.5M HCL for 24 hours.
After that for Lithium adsorption process, the adsorbent LMO put
1liter Lumpur Sidoarjo for 24 hours. Characterization performed
included; XRD, SEM and ICP. Morfologi formed in pellet
adsorbent with variation of calcination temperature of 500 ºC,
600 ºC and 700 ºC is irregular and the higher the calcination
temperature, the greater the average size of the grain as well as
the more crystalline. LMO 700 having adsorption capacity
Lithium Lumpur Sidoarjo most well compared to other adsorbent,
which is 2.98 mg/g.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Adsorpsi, Reaksi Solid State, Topotastis, Lithium Mangan Oksida Spinel, Lumpur Sidoarjo, Adsorption, Solid State Reaction, Topotactic,Lithium Mangan Oxide Spinel, Sidoarjo Mud.
Subjects: Q Science > QC Physics > QC271 Temperature measurements
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: - Davi Wah
Date Deposited: 27 Dec 2016 08:24
Last Modified: 27 Dec 2018 02:04