Sintesis Ag-Nanopartikel dengan Apis Florea Sebagai Capping Agent dan Analisis Potensi Antioksidan: Optimasi Menggunakan Desain Box-Behnken

Sabilla, Wardatus (2025) Sintesis Ag-Nanopartikel dengan Apis Florea Sebagai Capping Agent dan Analisis Potensi Antioksidan: Optimasi Menggunakan Desain Box-Behnken. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004211120_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Apis florea merupakan sumber antioksidan yang dapat mencegah radikal bebas yang dapat merusak sel tubuh. Penelitian ini Apis florea digunakan sebagai capping agent dalam sintesis nanopartikel perak untuk mencegah agregrasi. Tujuan dari penelitian ini adalah untuk mensintesis nanopartikel perak menggunakan metode reduksi kimia berbantuan iradiasi ultrasonik. Sintesis dilakukan menggunakan AgNO3 sebagai sumber ion Ag+, NaBH4 sebagai agen pereduksi, dan MAF sebagai capping agent, optimasi sintesis diteliti menggunakan RSM berbasis Box-Behnken Design (BBD) dengan tiga faktor dan tiga level yang berbeda meliputi suhu (40; 60; 80℃), waktu sonikasi (30; 60; 90 menit), dan konsentrasi MAF (5; 10; 15 ppm). Nanopartikel perak yang terbentuk dikarakterisasi dengan Spektrofotometer UV-Vis, Particle Size Analyzer (PSA), dan Transmission Electron Microscope (TEM). Spektra UV-Vis menunjukkan bahwa nanopartikel perak telah terbentuk pada panjang gelombang 410 nm, PSA menunjukkan bahwa hasil sintesis telah menunjukkan hasil yang nano dengan rata-rata ukuran partikel yang didapatkan sebesar 36,48 nm, FTIR menghasilkan peak pada 3198 cm-1 (O-H) dan 1631 cm-1 (C=O). TEM menunjukkan bahwa AgNPs berbentuk bulat dengan ukuran rata-rata 19,01 nm. BBD-RSM yang digunakan telah berhasil mengindikasikan hasil optimum suhu 70℃, waktu 90 menit, dan konsentrasi MAF 10 ppm yang dihasilkan serta menghasilkan model statistik dengan signifikansi yang baik. Hasil optimum nanopartikel perak diuji aktivitas antioksidan untuk mengevaluasi kemampuannya dan menunjukkan hasil nilai IC50 ditemukan sebesar 4,72 ppm. Nanopartikel perak menunjukkan kemampuan yang baik dalam menangkal radikal.
=================================================================================================================================
Apis florea is a source of antioxidants that can prevent free radicals that can damage body cells. In this study, Apis florea was used as a capping agent in the synthesis of silver nanoparticles to prevent agregation. The purpose of this study was to synthesis silver nanoparticles using a chemical reduction method assisted by ultrasonic irradiation. Synthesis was carried out using AgNO3 as a source of Ag+ ions, NaBH4 as a reducing agent, and MAF as a capping agent, synthesis optimization was studied using RSM based on Box-Behnken Design (BBD) with three factors and three different levels including temperature (40; 60; 80℃), sonication time (30; 60; 90 minutes), and MAF concentration (5; 10; 15 ppm). The formed silver nanoparticles were characterized by a UV-Vis Spectrophotometer, Particle Size Analyzer (PSA), and Transmission Electron Microscope (TEM). The UV-Vis spectrum shows that silver nanoparticles have been formed at a wavelength of 410 nm, PSA shows that the synthesis results have shown nano results with an average particle size of 36.48 nm, FTIR produces peaks at 3198 cm-1 (O-H) and 1631 cm-1 (C=O). TEM shows that the AgNPs are spherical with an average size of 19.01 nm. The BBD-RSM used has successfully indicated the optimum temperature of 70 ℃, time of 90 minutes, and MAF concentration of 10 ppm and produced a statistical model with good significance. The optimum results of silver nanoparticles were tested for antioxidant activity to evaluate their ability and showed the IC50 value was found to be 4.72 ppm. Silver nanoparticles show good ability to ward off radicals.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Nanopartikel perak, Ultrasonikasi, Apis Florea, RSM, Antioksidan. ======================================================== Silver nanoparticle, Ultrasonication, Apis Florea, RSM, Antioxidant
Subjects:	Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Wardatus Sabilla
Date Deposited:	29 Jul 2025 07:27
Last Modified:	29 Jul 2025 07:27
URI:	http://repository.its.ac.id/id/eprint/122643

Actions (login required)

View Item