Analisis Mekanisme Inhibisi Ekstrak Cengkeh Sebagai Inhibitor Organik Untuk Baja Api 5l Grade B Dengan Variasi Konsentrasi Dan Variasi Waktu Perendaman Di Lingkungan Asam

Alghifari, Robet (2025) Analisis Mekanisme Inhibisi Ekstrak Cengkeh Sebagai Inhibitor Organik Untuk Baja Api 5l Grade B Dengan Variasi Konsentrasi Dan Variasi Waktu Perendaman Di Lingkungan Asam. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038211061-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menganalisis mekanisme inhibisi ekstrak cengkeh sebagai inhibitor organik ramah lingkungan untuk baja API 5L Grade B. Fokus utama dari penelitian ini adalah untuk mengevaluasi efek variasi konsentrasi dan waktu perendaman ekstrak cengkeh dalam lingkungan asam terhadap laju korosi baja. Metodologi yang digunakan meliputi persiapan sampel baja, ekstraksi senyawa aktif dari cengkeh, dan pengujian korosi dengan menggunakan metode Polarisasi Potensiodinamik, Electrochemical Impedance Spectroscopy, Weight Loss, Fourier Transform Infra Red, Scanning Electron Microscopy.
Hasil penelitian menunjukkan bahwa ekstrak cengkeh mampu menghambat laju korosi secara efektif, dengan efisiensi tertinggi diperoleh pada konsentrasi 25 ppm dan waktu perendaman 12 jam. Pengujian menunjukkan bahwa efisiensi inhibisi mencapai 98,29% (Polarisasi Potensiodinamik), 89,92% (EIS), dan 97,18% (Weight Loss) pada kondisi tersebut. Mekanisme kerja inhibitor bersifat campuran, yaitu menghambat proses korosi baik pada reaksi anodik maupun katodik, yang didukung oleh analisis permukaan menggunakan FTIR dan SEM. Dengan demikian, ekstrak cengkeh terbukti sebagai inhibitor korosi yang potensial dan ramah lingkungan untuk perlindungan baja API 5L Grade B dalam lingkungan asam.
========================================================================================================================================
This study aims to analyze the inhibition mechanism of clove extract (Syzygium aromaticum) as an environmentally friendly organic inhibitor for API 5L Grade B steel. The main focus of the research is to evaluate the effect of varying concentrations and immersion times of clove extract in an acidic environment on the corrosion rate of steel. The methodology includes the preparation of steel samples, extraction of active compounds from clove, and corrosion testing using Potentiodynamic Polarization, Electrochemical Impedance Spectroscopy (EIS), Weight Loss, Fourier Transform Infrared Spectroscopy (FTIR), and Scanning Electron Microscopy (SEM). The results indicate that clove extract effectively reduces the corrosion rate, with the highest inhibition efficiency achieved at a concentration of 25 ppm and an immersion time of 12 hours. The efficiency values reached 98.29% (Potentiodynamic Polarization), 89.92% (EIS), and 97.18% (Weight Loss) under these conditions. The inhibition mechanism is classified as mixed-type, suppressing both anodic and cathodic reactions, as supported by surface analysis using FTIR and SEM. Therefore, clove extract is proven to be a promising and eco-friendly corrosion inhibitor for protecting API 5L Grade B steel in acidic environments.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Kata Kunci: Korosi, Inhibitor Organik, Cengkeh, Baja API 5L, HCl.
Subjects:	Q Science T Technology > T Technology (General)
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Muhammad Robet Alghifari
Date Deposited:	30 Jul 2025 04:19
Last Modified:	30 Jul 2025 04:19
URI:	http://repository.its.ac.id/id/eprint/123744

Actions (login required)

View Item