Fadlurahman, Fauzan Abiyu (2025) Pengaruh Jumlah Membran dan Besar Tegangan Elektrolisis Terhadap Efektivitas Desorpsi-Recovery Emas berbasis Membran Nano-Kitosan Oligosakarida. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011211089-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Emas merupakan salah satu logam mulia yang sangat berharga yang nilainya tidak hanya dinilai dari aplikasi praktisnya. Metode untuk mengolah emas, pada umumnya menggunakan proses hidrometalurgi atau leaching. Sianida merupakan larutan leaching yang biasa digunakan namun sangat membahayakan lingkungan. Selain itu, proses recovery emas juga masih menggunakan kabon aktif sebagai adsorbennya juga tidak baik untuk lingkungan. Sehingga terdapat salah satu alternatif yang lebih rama yaitu penggunaan larutan klorida sebagai larutan leaching dan metode biosorpsi dengan nano chitosan oligosaccharides (nano COS) untuk recovery emas yang terbagi menjadi dua yaitu adsorpsi dan desorpsi. Pada penelitian ini terdapat beberapa parameter desorpsi emas, yaitu besar tegangan dan jumlah membran. Dengan besar tegangan 1.6 V, 1.8V, dan 2.1 V dengan 5 membran dan 10 membran. Tujuan penelitian ini adalah untuk mengetahui pengaruh besar tegangan dan jumlah membran terhadap efektivitas desorpsi recovery menggunakan membran nano chitosan oligosaccarides. Jenis nano COS yang digunakan adalah shrimp. Bahan yang digunakan adalah mineral emas yang berasal dari Gorontalo, Indonesia. Mineral emas terlebih dahulu dilakukan uji EDX, XRF, dan XRD untuk mengetahi konsentrasi emas didalam larutan. Kemudian mineral ini dilakukan proses pre-treatment yaitu crushing, grinding, panning, dan microwave separation dengan daya 800 W selama 8 jam. Kemudian ore dilanjutkan dengan proses acid baking dengan temperatur 150oC dengan agitasi 600 rpm selama 150 menit. Setelah itu, residu hasil acid baking dilakukan leaching menggunakan Aqua Regia 4M pada temperatur 55oC dengan agitasi 800 rpm selama 6 jam. Hasil leaching kemudian di lakukan uji AAS untuk menentukan konsentrasi emas didalamnya. Membran nano COS dibuat dengan kombinasi PVA dan glutaraldehida (GA) serta diuji menggunakan FTIR. Setelah itu dilakukan adsorpsi dengan fix parameter dengan tegangan 0.9 V, temperatur ruangan, selama 1 jam untuk 5 membran dan 10 membran. Kemudian larutan sebelum dan sesudah adsorpsi dilakukan uji AAS untuk mengetahui nilai Ter-Adsorpnya. Kemudian membran dilakukan desorpsi dengan metode seperti desorpsi, hanya saja memvariasikan besar tegangan 1.6 V, 1.8 V, dan 2.1 V dengan 5 membran dan 10 membran. Hasil desorpsi menunjukkan besar tegangan yang paling baik adalah 1.6 V dengan 10 membran yang dapat mencapai persen desorpsi hingga 95%. Sedangkan pada 5 membran pada voltase yang sama hanya mencapai 64.41%.
======================================================================================================================================
Gold is one of the most precious metals whose value is not only judged by its practical applications. Methods to process gold generally use hydrometallurgical or leaching processes. Cyanide is a commonly used leaching solution but is very harmful to the environment. In addition, the gold recovery process also still uses activated carbon as an adsorbent which is also not good for the environment. So there is one alternative that is more comfortable, namely the use of chloride solution as a leaching solution and biosorption method with nano chitosan oligosaccharides (nano COS) for gold recovery which is divided into two, namely adsorption and desorption. In this study, there are several parameters of gold desorption, namely the amount of voltage and the number of membranes. With a voltage of 1.6 V, 1.8V, and 2.1 V with 5 membranes and 10 membranes. The purpose of this study is to determine the effect of voltage and number of membranes on the effectiveness of desorption recovery using nano chitosan oligosaccarides membrane. The type of nano COS used is shrimp. The material used is gold mineral from Gorontalo, Indonesia. The gold mineral was first subjected to EDX, XRF, and XRD tests to determine the concentration of gold in the solution. Then the mineral is pre-treated by crushing, grinding, panning, and microwave separation with 800 W power for 8 hours. The ore was then subjected to acid baking at 150oC with 600 rpm agitation for 150 minutes. After that, the acid baking residue was leached using Aqua Regia 4M at 55oC with 800 rpm agitation for 6 hours. The leaching results were then subjected to AAS test to determine the concentration of gold in it. Nano COS membranes were made with a combination of PVA and glutaraldehyde (GA) and tested using FTIR. After that, adsorption was carried out with fixed parameters with a voltage of 0.9 V, room temperature, for 1 hour for 5 membranes and 10 membranes. Then the solution before and after adsorption is carried out AAS test to determine the value of Ter Adsorpnya. Then the membrane is desorbed with a method such as desorption, only varying the voltage of 1.6 V, 1.8 V, and 2.1 V with 5 membranes and 10 membranes. The desorption results show that the best voltage is 1.6 V with 10 membranes which can achieve a percent desorption of up to 95%. While the 5 membranes at the same voltage only reached 64.41%.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Desorpsi, Emas, Elektrolisis, Nano COS, Tegangan Elektrolisis, Desorption, Electrolysis, Gold, Nano COS, Voltage Electrolysis
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN688 Hydrometallurgy T Technology > TP Chemical technology > TP1140 Polymers T Technology > TS Manufactures > TS670 Electroplating
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Fauzan Abiyu Fadlurahman
Date Deposited:	30 Jul 2025 07:35
Last Modified:	30 Jul 2025 07:35
URI:	http://repository.its.ac.id/id/eprint/123853

Actions (login required)

View Item