Analisis Pengaruh Komposisi Ethyl Centralite dan Temperatur Curing terhadap Sifat Fisikokimia, Sifat Mekanik, dan Stabilitas Cast Double Base (CDB) Propelan

Syahroni, Aqsyal (2025) Analisis Pengaruh Komposisi Ethyl Centralite dan Temperatur Curing terhadap Sifat Fisikokimia, Sifat Mekanik, dan Stabilitas Cast Double Base (CDB) Propelan. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011211033 - Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (10MB) | Request a copy

Abstract

Propelan double base merupakan salah satu jenis propelan padat yang sedang dikembangkan di Indonesia karena memiliki keunggulan yaitu tidak menghasilkan asap saat pembakaran terjadi. Propelan jenis ini terdiri dari dua bahan utama yaitu Nitroselulosa (NC) dan Nitrogliserin (NG), untuk meningkatkan sifat mekanik dan stabilitas termalnya ditambahkan zat aditif tambahan seperti plasticizer dan stabilizer pada komposisinya. Mengingat bahwa propelan merupakan bahan sensitif dan mudah meledak, maka diperlukannya zat stabilizer sebagai penstabil dan menjamin keamanannya baik saat penyimpanan, produksi maupun transportasi. Etil sentralit merupakan senyawa organik yang mengandung gugus etil, gugus fenil dan gugus karbonil yang dapat bereaksi dengan gugus nitro (NO2) yang mana gugus tersebut merupakan produk dekomposisi dari propelan. Oleh karena itu penelitian ini bertujuan menganalisis pengaruh variasi penambahan etil sentralit sebagai stabilizer (2%, 5%, 8%) dan variasi temperatur curing (30 oC, 40 oC, 50 oC) terhadap sifat fisikokimia, sifat mekanik, dan stabilitas cast double base (CDB) propelan. Hasilnya menunjukkan temperatur curing yang optimum yakni pada temperatur curing dengan suhu 50 oC, dengan hasil morfologi yang lebih homogen, minim porositas, dan mempunyai kepadatan yang baik sesuai spesifikasi propelan yaitu diatas 1,5 gr/cm3. Temperatur curing yang optimum ini juga mendapatkan nilai kekerasan dan kekuatan luluh tekan yang paling baik diantara kedua variasi lainnya, dengan nilai kekerasan sebesar 74,67 shore A dan nilai kekuatan luluh tekan sebesar 3,86 MPa pada variasi SEC-2-50T. Pada variasi SEC-8-50T dengan penambahan etil entralit 8% dan temperatur curing 50 oC, menunjukkan hasil yang lebih stabil diantara variasi lainnya, dengan temperatur awal dekomposisi 163,17 oC, puncak dekomposisi pada 178,88 oC, dan residu sebesar 3,243%. Selain itu, pada variasi ini juga mendapatkan laju pengurangan massa sebesar 4,4921 mg per menitnya ketika berada pada temperatur nyalanya, serta membutuhkan waktu sebanyak 3,142 menit untuk dapat terdekomposisi sempurna dari temperatur nyala hingga ke temperatur puncaknya. Pada uji metil violet didapatkan lama waktu perubahan pada kertas uji selama 60 menit 44 detik.
======================================================================================================================================
Double base propellant is one type of solid propellant that is being developed in Indonesia because it has the advantage of not producing smoke when combustion occurs. This type of propellant consists of two main ingredients, Nitrocellulose (NC) and Nitroglycerin (NG), to improve its mechanical properties and thermal stability, additional additives such as plasticizers and stabilizers are added to its composition. Given that propellant is a sensitive and explosive material, it is necessary to use stabilizer as a stabilizer and ensure its safety both during storage, production and transportation. Ethyl centralite is an organic compound containing ethyl group, phenyl group and carbonyl group that can react with nitro group (NO2) which is the decomposition product of propellant. Therefore, this study aims to analyze the effect of variation of ethyl centralite addition as stabilizer (2%, 5%, 8%) and variation of curing temperature (30 oC, 40 oC, 50 oC) on physicochemical properties, mechanical properties, and stability of cast double base (CDB) propellant. The results show that the optimum curing temperature is at 50 oC, with more homogeneous morphology, minimal porosity, and good density according to propellant specifications which is above 1.5 gr/cm3 . This optimum curing temperature also obtained the best hardness and compressive yield strength values among the other two variations, with a hardness value of 74.67 shore A and a compressive yield strength value of 3.86 MPa in the SEC-2-50T variation. The SEC-8-50T variation with the addition of 8% ethyl centralite and a curing temperature of 50 oC, showed more stable results among other variations, with an initial decomposition temperature of 163.17 oC, peak decomposition at 178.88 oC, and a residue of 3.243%. In addition, this variation also obtained a mass reduction rate of 4.4921 mg per minute when it was at its flame temperature, and took 3.142 minutes to be completely decomposed from the flame temperature to its peak temperature. In the methyl violet test, the length of time for changes in the test paper was obtained for 60 minutes 44 seconds.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Cast Double Base, Double Base Propellant, Etil Sentralit, Stabilizer, Temperatur Curing, Cast Double Base, Double Base Propellant, Ethyl Centralite, Stabilizer, Temperatur Curing
Subjects:	T Technology > TP Chemical technology > TP1140 Polymers
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis