Pengaruh Orientasi Cetak dan Jenis Larutan Post-processing Terhadap Kekasaran Permukaan Dan Kekuatan Toroidal Propeller Pla Hasil Cetak 3D Fdm

Tuflihun, Panggih (2025) Pengaruh Orientasi Cetak dan Jenis Larutan Post-processing Terhadap Kekasaran Permukaan Dan Kekuatan Toroidal Propeller Pla Hasil Cetak 3D Fdm. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011211046_Undergraduate_Thesis.pdf Restricted to Repository staff only Download (5MB)

Abstract

Toroidal propeller merupakan jenis propeller dengan geometri kompleks yang memiliki keunggulan tingkat kebisingan yang rendah. Fabrikasi toroidal propeller dapat menggunakan metode additive manufacturing seperti fused deposition modelling atau FDM. Hasil fabrikasi menggunakan FDM memiliki tingkat kekasaran permukaan yang tinggi serta dapat mempengaruhi sifat mekanik pada toroidal propeller. Solusi yang digunakan pada masalah ini dengan melakukan pencelupan hasil cetak FDM ke dalam larutan kimia seperti chloroform dan dichloromethane. Tujuan dari penelitian ini adalah menganalisis pengaruh jenis larutan dan menganalisis pengaruh arah pencetakan terhadap kekasaran permukaan dan sifat mekanik toroidal propeller. Pada awal penelitian ini dilakukan pengujian karakterisasi seperti FTIR dan XRD untuk memvalidasi material yang digunakan yaitu PLA. Penelitian ini juga melakukan pengujian kekasaran permukaan dan tarik untuk mengetahui kekasaran dan kekuatan dari material sebelum post processing dan setelah post processing.. Pengujian akurasi dimensi dilakukan juga untuk mengukur kepresisian mesin FDM dalam fabrikasi objek yang kompleks. Hasil pengujian FTIR menandakan adanya peak baru pada spesimen chloroform dan dichloroform menandakan adanya gugus C-Cl yang terperangkap. Hasil pengujian XRD menandakan adanya peningkatan kristalinitas pada spesimen yang dilakukan post processing. Pada variasi orientasi cetak, kekuatan paling tinggi ada pada sudut 0° sebesar 50,7 MPa. Sedangkan kekasaran permukaan paling rendah pada sudut 90o sebesar 12,469 µm. Pada variasi jenis larutan post processing, kekuatan paling tinggi pada spesimen non treatment orientasi cetak 0° yaitu sebesar 50,7 MPa. Sedangkan kekasaran paling rendah pada spesimen dengan larutan dichloromethane orientasi cetak 0° yaitu sebesar 1,0628 µm.
===================================================================================================================================
Toroidal propellers, characterized by their complex geometry and low noise emissions, can be fabricated using Fused Deposition Modeling (FDM). However, the FDM process typically results in high surface roughness, which can compromise the mechanical properties of the propeller. This research investigates a chemical immersion post-processing method using chloroform and dichloromethane to mitigate these issues. The primary objective is to analyze the effects of different chemical solutions and print orientations on the surface roughness and mechanical properties of the propeller. The Polylactic Acid (PLA) material was first validated through FTIR and XRD characterization. The core of the research involves tensile tests to assess mechanical strength, alongside surface roughness measurements, comparing results before and after the post-processing treatment. Additionally, dimensional accuracy tests were conducted to evaluate the precision of the FDM fabrication for such complex geometries. The FTIR test results indicate the presence of new peaks in the chloroform and dichloroform specimens indicating the presence of trapped C-Cl groups. The XRD test results indicate an increase in crystallinity in the specimens that underwent post-processing. In the print orientation variation, the highest strength is at an angle of 0o at 50.7 MPa. While the lowest surface roughness is at an angle of 90o at 12.469 µm. In the variation of post-processing solution types, the highest strength is in the non-treatment specimen with a print orientation of 0° at 50.7 MPa. While the lowest roughness is in the specimen with a dichloromethane solution with a print orientation of 0° at 1.0628 µm.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Fused Depositiong Modelling, PLA, Proses Pasca Pencetakan, Toroidal Propeller, Post Processing
Subjects:	T Technology > T Technology (General) > TA404 Materials--Biodegradation T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL776 .N67 Quadrotor helicopters--Automatic control T Technology > TS Manufactures > TS2301.T7 Toys, etc
Depositing User:	Panggih Tuflihun
Date Deposited:	30 Jul 2025 10:25
Last Modified:	30 Jul 2025 10:25
URI:	http://repository.its.ac.id/id/eprint/124259