Pengaruh Variasi Konsentrasi Ekstrak Kulit Jagung (Zea Mays L.) terhadap Laju Korosi sebagai Inhibitor Organik pada Baja API 5L Grade B dalam Larutan H2SO4 1M dengan Variasi Waktu Perendaman

Putri, Adinda (2025) Pengaruh Variasi Konsentrasi Ekstrak Kulit Jagung (Zea Mays L.) terhadap Laju Korosi sebagai Inhibitor Organik pada Baja API 5L Grade B dalam Larutan H2SO4 1M dengan Variasi Waktu Perendaman. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038211081-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (26MB) | Request a copy

Abstract

Baja API 5L Grade B banyak digunakan dalam industri minyak dan gas karena kekuatan mekaniknya yang tinggi, namun material ini rentan mengalami korosi, khususnya pada lingkungan asam. Penelitian ini bertujuan untuk mengevaluasi efektivitas ekstrak kulit jagung (Zea mays L.) sebagai inhibitor korosi ramah lingkungan terhadap baja API 5L Grade
B dalam larutan H₂SO₄ 1 M. Pengujian dilakukan menggunakan variasi konsentrasi inhibitor sebesar 0, 100, 200, 300, 400, dan 500 ppm dengan waktu perendaman selama 3, 4, dan 5 jam. Pengujian yang dilakukan yaitu FTIR, Polarisasi Potensiodinamik, EIS, Weight Loss, dan SEM. Pembuatan ekstrak dengan menggunakan metode maserasi. Hasil pengujian menunjukkan bahwa ekstrak kulit jagung memiliki kemampuan menghambat laju korosi secara efektif. Konsentrasi optimum diperoleh pada 500 ppm dengan efisiensi inhibisi maksimum mencapai 95,59% pada waktu perendaman 5 jam berdasarkan hasil pengujian PDP. Sedangkan pengujian EIS dengan efisiensi tertinggi berada pada konsentrasi 500 ppm
waktu perendaman 5 jam sebesar 98,28%. Dari pengujian Weight Loss di ambil dari sampel hasil terbaik pengujian polarisasi dan didapat hasil dengan efisiensi tertinggi sebesar 95,19%. Hasil SEM menunjukkan permukaan spesimen yang lebih halus dan minim kerusakan pada sampel dengan inhibitor dibandingkan tanpa inhibitor, mendukung peran adsorpsi senyawa aktif dalam membentuk lapisan protektif. Dengan demikian, ekstrak kulit jagung terbukti dapat bertindak sebagai inhibitor tipe campuran.
=======================================================================================================================================
API 5L Grade B steel is widely used in the oil and gas industry due to It’s high mechanical strength, but this material is susceptible to corrosion, especially in acidic environments. This study aim’s to evaluate the effectiveness of corn husk extract (Zea Mays L.) as an environmentally friendly corrosion inhibitor for API 5L Grade B steel in 1 M H₂SO₄ solution. Test’s were carried out using variations in inhibitor concentrations of 0, 100, 200, 300, 400, and 500 ppm with immersion times of 3, 4, and 5 hours. The tests carried out were FTIR, Potentiodynamic Polarization, EIS, Weight Loss, and SEM. Preparation of extracts using maceration method. The test results show that corn husk extract has the ability to inhibit the corrosion rate effectively. The optimum concentration was obtained at 500 ppm with maximum inhibition efficiency reaching 95,59% at 5 hours immersion time based on
PDP test results. While EIS testing with the highest efficiency is at a concentration of 500 ppm 5 hours immersion time of 98,28%. Weight loss test was taken from the best sample results of polarization testing and obtained results with the highest efficiency of 95,19%. SEM results show a smoother specimen surface and minimal damage to samples with inhibitors than without inhibitors, supporting the role of adsorption of active compounds in forming a protective layer. Thus, corn husk extract was shown to act as a mixed-type inhibitor.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Korosi, Inhibitor Organik, Kulit Jagung, Baja API 5L Grade B, H2SO4 1 M. Corrosion, Organic Inhibitor, Corn Husk, API 5L Grade B Steel, 1 M H2SO4
Subjects:	Q Science > QD Chemistry > QD115 Electrochemical analysis T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Adinda Putri
Date Deposited:	30 Jul 2025 08:06
Last Modified:	30 Jul 2025 08:06
URI:	http://repository.its.ac.id/id/eprint/124389