Studi Pengaruh Silanisasi Sonikasi Dalam Pembentukan Monolayer 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) Pada Silika (SiO2)

Assidiqiah, Citra and Putri, Lintang Laxitna (2025) Studi Pengaruh Silanisasi Sonikasi Dalam Pembentukan Monolayer 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) Pada Silika (SiO2). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2041211022_2041211039-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Dental amalgam adalah salah satu bahan restorasi yang paling umum digunakan dalam kedokteran gigi. Amalgam mengandung sekitar 43-50% merkuri (berdasarkan berat), yang dikombinasikan dengan logam-logam seperti perak, timah, dan tembaga. Sebagai alternatif, resin komposit kini mulai digunakan sebagai pengganti amalgam dalam prosedur penambalan gigi. Komponen pada resin komposit terdiri dari matriks dan filler. Salah satu filler yang sering digunakan yaitu SiO2. Silika (SiO2) sebagai pengisi penguat untuk meningkatkan sifat mekanis bahan restorasi seperti memiliki ketahanan yang cukup terhadap gigitan dan kunyahan setelah diaplikasikan pada gigi. Oleh karena itu, penelitian ini bertujuan untuk mengetahui pengaruh waktu silanisasi dengan larutan 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) terhadap sifat hidrofobisitas dengan uji FTIR dan Water Contact Angle (WCA). Untuk mengetahui pengaruh silanisasi terhadap jumlah 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) pada SiO2 dengan uji TGA. Untuk mengetahui pengaruh waktu silanisasi dengan 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) terhadap karakterisasi SiO2 dengan uji SEM-EDX. Untuk mengetahui kinetika attachment pada proses silanisasi hingga membentuk monolayer/lapisan sebagai filler restorasi gigi. Penelitian ini dimulai dengan melakukan sonikasi menggunakan ultrasonik probe atau pre-treatment SiO2 dengan pelarut cyclohexane, kemudian melakukan silanisasi dengan ultrasonik bath yang ditambahkan 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM). Silika atau SiO2 yang telah disilanisasi kemudian diuji menggunakan FTIR (Fourier transform infrared spectroscopy), TGA (Thermogravimetric Analysis), SEM-EDX, Uji Water Contact Angle (WCA).
======================================================================================================================================
Dental amalgam is one of the most used restorative materials in dentistry. Amalgam contains approximately 43-50% mercury (by weight), combined with metals such as silver, tin, and copper. As an alternative, composite resins are now being used as a substitute for amalgam in dental filling procedures. The components of composite resin consist of a matrix and filler. One frequently used filler is SiO2. Silica (SiO2) acts as a reinforcing filler to improve the mechanical properties of restorative materials, such as providing sufficient resistance to biting and chewing after application to teeth. Therefore, this study aims to determine the effect of silanization time with 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) solution on hydrophobicity properties using FTIR and Water Contact Angle (WCA) tests. To determine the effect of silanization on the amount of 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) in SiO2 using TGA tests. To determine the effect of silanization time with 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM) on the characterization of SiO2 using SEM-EDX test. To determine the attachment kinetics in the silanization process to form a monolayer/layer as a dental restoration filler. This study began with sonication using an ultrasonic probe or pre-treatment of SiO2 with cyclohexane solvent, then silanization with an ultrasonic bath added with 3-(Trimethoxysilyl)Propyl Methacrylate (TMSPM). Silica or SiO2 that has been silanized was then tested using FTIR (Fourier transform infrared spectroscopy), TGA (Thermogravimetric Analysis), SEM-EDX, Water Contact Angle (WCA) test.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Silanisasi, Silika Nanopartikel, Ultrasonikasi
Subjects:	T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Vocational > Industrial Chemical Engineering
Depositing User:	Lintang Laxitna Putri
Date Deposited:	01 Aug 2025 06:31
Last Modified:	01 Aug 2025 06:31
URI:	http://repository.its.ac.id/id/eprint/124639

Actions (login required)

View Item