Sintesis dan Karakterisasi Alumina Mesopori dengan Pendekatan Dual Templat P123 dan Ekstrak Lerak (Sapindus rarak DC.)

Mauliddika, Naura Ariella (2025) Sintesis dan Karakterisasi Alumina Mesopori dengan Pendekatan Dual Templat P123 dan Ekstrak Lerak (Sapindus rarak DC.). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004211085-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Sintesis alumina mesopori dengan pendekatan dual templat P123 dan ekstrak lerak (Sapindus rarak DC.) bertujuan untuk mengetahui pengaruh penambahan surfaktan alami terhadap karakteristik material hasil sintesis. Aluminium klorida heksahidrat (AlCl3·6H2O) dan natrium aluminat (NaAlO2) digunakan sebagai sumber alumina. Ekstrak lerak diperoleh melalui metode maserasi, kemudian dicampur dengan P123 dalam rasio berat 1:1. Sintesis dilakukan dengan metode hidrotermal pada suhu 150℃. Hasil karakterisasi XRD menunjukkan adanya puncak difraksi pada 2θ = 19,52°, 32,98°, 36,46°, 39,2°, 45,5°, 59,96°, dan 66,48° yang mengindikasikan terbentuknya struktur γ-Al2O3. Analisis adsorpsi-desorpsi N2 menghasilkan isoterm tipe IV dengan loop histeresis tipe H3, yang menunjukkan keberadaan pori meso pada seluruh sampel. Penggunaan dual templat mampu meningkatkan luas permukaan spesifik hingga 262,24 m2/g dan menghasilkan distribusi ukuran pori yang sempit. Karakterisasi FESEM menunjukkan bahwa alumina mesopori yang disintesis dengan dual templat P123 dan ekstrak lerak memiliki rata-rata distribusi ukuran partikel terbesar dibandingkan dengan sampel lainnya. Hasil ini menunjukkan bahwa penambahan surfaktan alami dalam sistem dual templat dapat memengaruhi ukuran partikel, morfologi, dan sifat tekstural dari alumina mesopori.
========================================================================================================================================
Mesoporous alumina was synthesized using a dual-template approach involving P123 and lerak extract (Sapindus rarak DC.) to investigate the effect of natural surfactant addition on the characteristics of the resulting material. Aluminum chloride hexahydrate (AlCl3·6H2O) and sodium aluminate (NaAlO2) were used as alumina precursors. Lerak extract was obtained through maceration and subsequently mixed with P123 in a 1:1 weight ratio. The synthesis was carried out via a hydrothermal method at 150°C. XRD results showed diffraction peaks at 2θ = 19,52°, 32,98°, 36,46°, 39,2°, 45,5°, 59,96°, and 66,48°, indicating the formation of γ-Al2O3. Nitrogen adsorption-desorption analysis showed type IV isotherms with H3 hysteresis loops, confirming the presence of mesopores. The dual-template system increased the specific surface area up to 262,24 m2/g and produced a narrow pore size distribution. FESEM analysis revealed that the sample synthesized with the P123 and lerak extract combination had the largest average particle size among all samples. These results indicate that the addition of a natural surfactant in the dual-template system affects the particle size, morphology, and textural properties of mesoporous alumina.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Alumina mesopori, Hidrotermal, Templat, Lerak, Kalsinasi Mesoporous alumina, Hydrothermal, Template, Lerak, Calcination
Subjects:	Q Science > QD Chemistry > QD905.2 Crystals.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry
Depositing User:	Naura Ariella Mauliddika
Date Deposited:	06 Aug 2025 02:11
Last Modified:	06 Aug 2025 02:11
URI:	http://repository.its.ac.id/id/eprint/127664