Analisa Pengaruh Frekuensi dan Resonansi pada 3D Printing Kotak Musik dengan Material PLA+ ABS dan PETG

Arifin, Zainal (2024) Analisa Pengaruh Frekuensi dan Resonansi pada 3D Printing Kotak Musik dengan Material PLA+ ABS dan PETG. Other thesis, Sepuluh Nopember Institute of Technology.

Text 2038211014-Undergraduate-Thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menganalisis pengaruh material PLA+, ABS, dan PETG terhadap karakteristik akustik kotak musik hasil pencetakan 3D. Penggunaan teknologi 3D printing dalam bidang seni dan musik menawarkan efisiensi serta fleksibilitas desain, namun tiap material memiliki sifat mekanik yang berbeda sehingga mempengaruhi resonansi dan frekuensi suara yang dihasilkan. Pengujian dilakukan dengan merekam suara dari kotak musik yang dicetak menggunakan ketiga jenis filamen, lalu dianalisis menggunakan Audacity dan perangkat lunak SPSS. Hasil analisis menunjukkan bahwa tidak terdapat perbedaan signifikan pada frekuensi antar material, namun terdapat perbedaan yang signifikan pada intensitas suara. Material PETG menunjukkan penyimpangan paling tinggi terhadap material acuan (Zinc Zamac), sedangkan ABS memberikan hasil yang paling mendekati dari sisi intensitas dan frekuensi suara. Kesimpulan dari penelitian ini menunjukkan bahwa ABS merupakan material paling sesuai sebagai pengganti material logam dalam pembuatan kotak musik berbasis 3D printing.
===============================================================================================================================
This study aims to analyse the effect of PLA+, ABS, and PETG materials on the acoustic characteristics of 3D-printed music boxes. The use of 3D printing technology in the fields of art and music offers efficiency and design flexibility, but each material has different mechanical properties that affect resonance and sound frequency. The testing was conducted by recording the sound from music boxes printed using the three types of filaments, then analysed using Audacity and SPSS software. The analysis results showed that there were no significant differences in frequency between materials, but there were significant differences in sound intensity. PETG showed the highest deviation from the reference material (Zinc-Zamac), while ABS provided results closest to the reference in terms of sound intensity and frequency. The conclusion of this study indicates that ABS is the most suitable material as a substitute for metal in the production of 3D-printed music boxes.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	ABS, Frekuensi, Kotak Musik, Manufaktur Aditif, PETG, PLA+, Resonansi
Subjects:	T Technology > TS Manufactures > TS161 Materials management. T Technology > TS Manufactures > TS170 New products. Product Development
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Zainal Arifin
Date Deposited:	20 Jan 2026 04:37
Last Modified:	20 Jan 2026 04:37
URI:	http://repository.its.ac.id/id/eprint/128070

Actions (login required)

View Item