Pengaruh Temperatur Pada Proses Perlakuan Panas Baja Tahan Karat Martensitik Aisi 431 Terhadap Laju Korosi Dan Struktur Mikro

Setiawan, Medwin (2008) Pengaruh Temperatur Pada Proses Perlakuan Panas Baja Tahan Karat Martensitik Aisi 431 Terhadap Laju Korosi Dan Struktur Mikro. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 2104030006-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (47MB) | Request a copy

Abstract

Suatu permukaan logam yang berinteraksi langsung dengan lingkungan korosif dengan adanya keadaan ketidakseragaman akan terjadi perbedaan potensial efektif lokal, sehubungan dengan itu maka akan terjadi korosi pada daerah yang lebih anodik daripada permukaan lain disebabkan oleh perlakuan yang dilakukan pada material tersebut, misalnya adalah proses heat treatment. Dalam tugas akhir ini obyek yang diteliti adalah baja tahan karat martensitic stainless steel AISI dengan kadar karbon 17%, 0,2%, karbon, 1,6 nickel. Pada penelitian kali ini akan dilakukan suatu penelitian terhadap pengaruh variasi temperatur pemanasan pada proses keat treatment terhadap laju korosi.Proses heat treatment disini adalah menggunakan temperatur pemanasan ; 750°C, 850°C, 950°C, ditahan 30 menit dan diquenching dengan media pendingin air. Dari proses heat treatment tersebut akan dilakukan pengujian kekerasan, struktur mikro dan uji laju korosi, dimana metode yang digunakan adalah metode immersi (media korosif HCL ). Dari hasil pengujian tersebut diatas didapatkan hasil sebagai berikut : baja tanpa laku panas mengalami laju korosi sebesar 51,8 mpy, untuk baja mengalami laku panas 7500C dengan .holding time 30 menit laju korosi specimen] adala.h 50 mpy, specimen2 adalah 30 mpy, specimen3 adalah 76 mpy specimen4 adalah 68 mpy, specimenS adalah 67 mpy. Untuk 850°C laju korosi specimen] adalah 43 mpy, specimen2 adalah 61 mpy, specimen3 adalah 46 mpy, specimen4 adalah 29 mpy, specimen5 adalah 27 mpy. Untuk 9500C laju korosi specimen] adalah 82 mpy, specimen2 adalah 84 mpy, specimen3 adalah 78 mpy, specimen4 adalah 75 mpy, specimen5 adalah 77 mpy
====================================================================================================================================
A metal surface that interacts directly with a corrosive environment with a state of non-uniformity will result in a local effective potential difference, in connection with which corrosion will occur in areas that are more anodic than other surfaces due to the treatment carried out on the material, for example the heat treatment process. In this final project the object studied is martensitic stainless steel AISI with a carbon content of 17%, 0.2%, carbon, 1.6 nickel. In this study, a study will be conducted on the effect of variations in heating temperature in the heat treatment process on the corrosion rate. The heat treatment process here is using a heating temperature; 750°C, 850°C, 950°C, held for 30 minutes and quenched with water cooling media. From the heat treatment process, hardness testing, microstructure and corrosion rate testing will be carried out, where the method used is the immersion method (corrosive media HCL). From the test results above, the following results were obtained: steel without heat treatment experienced a corrosion rate of 51.8 mpy, for steel experiencing heat treatment at 7500C with a holding time of 30 minutes the corrosion rate of specimen] was 50 mpy, specimen2 was 30 mpy, specimen3 was 76 mpy specimen4 was 68 mpy, specimenS was 67 mpy. For 850°C the corrosion rate of specimen] was 43 mpy, specimen2 was 61 mpy, specimen3 was 46 mpy, specimen4 was 29 mpy, specimen5 was 27 mpy. For 9500C the corrosion rate of specimen] is 82 mpy, specimen2 is 84 mpy, specimen3 is 78 mpy, specimen4 is 75 mpy, specimen5 is 77 mpy

Item Type:	Thesis (Diploma)
Additional Information:	RSM 671.36 Set p-1 2008 (weeding)
Uncontrolled Keywords:	temperatur, laju korosi, laju pendinginan; temperature, corrosion rate, cooling rate
Subjects:	T Technology > TS Manufactures > TS205 Metals--Heat treatment.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	30 Oct 2025 06:05
Last Modified:	30 Oct 2025 06:05
URI:	http://repository.its.ac.id/id/eprint/128701