Sintesis Dan Karakterisasi Komposit Magnetik Lunak Berbasis Besi Nitrida Untuk Komponen Motor Listrik

Syah, Rakhasoni Firman (2022) Sintesis Dan Karakterisasi Komposit Magnetik Lunak Berbasis Besi Nitrida Untuk Komponen Motor Listrik. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6001201015-Master_thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Penelitian yang berjudul "Sintesis dan karakteristik komposit magnetik lunak berbasis besi netrida untuk komponen motor listrik " dilakukan dengan tujuan untuk mengetahui proses dan cara pembuatan SMC dan mengetahui pengaruh komposisi, temperatur sinter, dan tekanan kompaksi pada fabrikasi SMC terhadap karakter magnetnya. Bahan baku yang digunakan pada penelitian ini yaitu besi nitrida (Fe-N) yang berasal dari olahan pasir besi. Adapun metode pembuatan SMC dengan menggunakan metode metalurgi serbuk yang tahap awalnya dimulai dengan serbuk besi nitrida dicampurkan dengan perlakuan phosphate coating dan mixing dari komponen-komponen penyusun SMC. Pada penelitian ini, digunakan data pembanding berupa material somaloy. Phosphate coating dilakukan dengan cara mencampur serbuk besi nitrida ke dalam larutan etanol dan asam fosfat berkonsentrasi 0,016 g/ml. Selanjutnya, dilakukan pengadukan pada temperatur kamar, dengan menggunakan magnetic stirrer pada 500 RPM selama 60 menit. Serbuk yang telah diberi perlakuan phosphate coating akan dibilas dengan larutan etanol selanjutnya dikeringkan pada temperatur 80 C selama 1 jam. Resin phenolic digunakan sebagai binder, sedangkan zinc stearate digunakan sebagai lubricant. Tahap selanjutnya yaitu kompaksi, dimana komponen penyusun SMC yang berupa serbuk dan telah tercampur akan ditekan untuk mencapai sampel dengan geometri dan densitas tertentu. Serbuk penyusun akan ditekan dengan mesin press hidrolik pada tekanan 400 MPa, 500 MPa dan 600 MPa. Proses selanjutnya yaitu sinter, pada proses sinter akan dilakukan pada kisaran temperatur 300-500 C pada lingkungan vakum selama 1 jam. Dan yang terakhir yaitu tahap karakterisasi dengan menggunakan pengujian X-Rays Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive of X-Ray Spectroscopy (EDX), dan Vibrating Sample Magnetometer (VSM).
===================================================================================================================================
The research entitled "Synthesis and Characterization of Iron Nitride-Based Soft Magnetic Composites for Electric Motor Components" was carried out with the aim of knowing the process and method of making SMC and knowing the effect of composition, sintering temperature, and compaction pressure on SMC fabrication on its magnetic character. The raw material used in this research is iron nitride (Fe-N) which is derived from processed iron sand. The method of making SMC is using the powder metallurgy method, which initially starts with iron nitride powder mixed with phosphate coating treatment and mixing of the components that make up SMC. In this study, used comparative data in the form of somaloy material. Phosphate coating is done by mixing iron nitride powder into a solution of ethanol and phosphoric acid with a concentration of 0.016 g/mL. Next, stirred at room temperature, using a magnetic stirrer at 500 RPM for 60 minutes. Powder that has been treated with phosphate coating will be rinsed with ethanol solution and then dried at a temperature of 80°C for 1 hour. Phenolic resin is used as a binder, while zinc stearate is used as a lubricant. The next stage is compaction, where the components that make up the SMC in the form of powder and have been mixed will be pressed to achieve a sample with a certain geometry and density. The constituent powder will be pressed with a hydraulic press at a pressure of 400 MPa, 500 MPa and 600 MPa. The next process is sintering, the sintering process will be carried out at a temperature range of 300-600°C in a vacuum environment for 1 hour. And the last is the characterization stage using X-Rays Diffraction (XRD) testing, Scanning Electron Microscopy (SEM), Energy Dispersive of X-Ray Spectroscopy (EDX), and Vibrating Sample Magnetometer (VSM).

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Besi Nitrida, Komposit Magnetik Lunak, Tekanan Kompaksi, Temperatur Sinter, Iron Nitride, Soft Magnetic Composite, Compaction Pressure, Sintering Temperature
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL440 Motorcycles.
Divisions:	Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	12 Dec 2025 03:30
Last Modified:	12 Dec 2025 03:30
URI:	http://repository.its.ac.id/id/eprint/128946