Efektivitas Lapisan Tipis Emas Dan Perak Sebagai Elektroda Untuk Monitoring Prognosis Kanker Darah

Muliawati, Amastasia Salsabila (2022) Efektivitas Lapisan Tipis Emas Dan Perak Sebagai Elektroda Untuk Monitoring Prognosis Kanker Darah. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000005-Undregraduate_thesis.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Kanker merupakan salah satu penyakit yang menyebabkan kematian yang tinggi di dunia. Berdasarkan data WFO, pada tahun 2015 terdapat 8,8 juta kematian yang diakibatkan oleh penyakit kanker. Berbagai metode telah dikembangkan untuk mengobati kanker, salah satunya dengan menggunakan terapi radiasi atau radioterapi. Logam mulia dalam ilmu kimia merupakan logam yang tahan terhadap korosi maupun oksidasi. Pada penelitian ini dilakukan modifikasi elektroda Ag, Au, Ag/Au, dan Au/Ag dengan menggunakan membran yang berbeda, membran tersebut mempunyai sifat berpori dan stabil terhadap larutan yang akan diuji dengan teknik pembuatan elektroda yang lebih sederhana untuk meningkatkan efektivitas deteksi kanker darah. Maka dari itu, dilakukan penelitian dengan judul “Efektivitas Lapisan Tipis Emas dan Perak sebagai Elektroda Untuk Monitoring Prognosis Kanker Darah”. Penelitian ini berfokus pada pembuatan elektroda lapisan tipis variasi Ag dan Au untuk deteksi kanker darah dengan metode Sputtering DC. Pada penelitian ini menggunakan berbagai metode pengujian karakterisasi yaitu SEM, EDS, XRD, CV, EIS, dan UV-Vis. Pengujian struktur kristal menunjukkan lapisan tipis Ag/Au dan Au/Ag memiliki peak intensitas yang lebih tinggi. Identifikasi pengujian elektrokimia menghasilkan peak reduksi lebih tinggi dan kenaikan resistansi tinggi pada lapisan tipis yang memiliki konsentrasi BSA yang lebih banyak. Nilai sensitivitas dari pengujian elektrokimia ini didapatkan dari slope kurva kalibrasi yang telah diolah menggunakan softaware origin. Pengujian karaktersasi UV-Vis puncak absorbansi maksimum darah normal terdapat panjang gelombang antara 304 nm hingga 310 nm. Sedangkan puncak absorbansi konsentrasi serum albumin 3,0 g/dL sebagai darah kanker pada sampel elektroda terdapat pada panjang gelombang antara 310 nm hingga 314 nm
===================================================================================================================================
Cancer is one of the diseases that causes high mortality in the world. Based on WFO data, in 2015 there were 8.8 million deaths caused by cancer. Various methods have been developed to treat cancer, one of them by using radiation therapy or radiotherapy. Precious metals in chemistry are metals that are resistant to corrosion and oxidation. In this study, modifications of Ag, Au, Ag/Au, and Au/Ag electrodes were carried out using different membranes, these membranes have porous properties and are stable to the solution to be tested with a simpler electrode manufacturing technique to increase the effectiveness of blood cancer detection. Therefore, a study was conducted with the title "The Effectiveness of Gold and Silver Thin Layers as Electrodes for Monitoring Blood Cancer Prognosis". It is hoped that this research can later be used as an illustration for further research and provide information to readers regarding cancer detection using the DC sputtering method, as well as an effective thin layer for cancer detection and the parameters to be considered in conducting research. In this study, various characterization test methods were used, namely SEM, EDS, XRD, CV, EIS, and UV-Vis. The crystal structure test shows that the Ag/Au and Au/Ag thin layers have higher peak intensities. The identification of the electrochemical test resulted in a higher reduction peak and a high resistance increase in the thin film which had a higher concentration of BSA. The sensitivity value of this electrochemical test is obtained from the slope of the calibration curve which has been processed using origin software. The UV-Vis characterization test showed that the maximum absorbance peak of normal blood had a wavelength between 304 nm to 310 nm. Meanwhile, the absorbance peak of serum albumin concentration of 3.0 g/dL as cancer blood in the electrode sample was at a wavelength between 310 nm to 314 nm.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Kanker Darah, Lapisan Tipis, Ag, dan Au, Blood Cancer, Thin Film, Ag and Au
Subjects:	Q Science > QR Microbiology > QR 201.T84 Tumors. Cancer
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	15 Dec 2025 06:22
Last Modified:	15 Dec 2025 06:22
URI:	http://repository.its.ac.id/id/eprint/128970