Sintesis Nanokristal Fe3O4 Dan Fe2O3 Dari Pasir Besi Dengan Kopresipitator

Agustin, Arifa Diana (2022) Sintesis Nanokristal Fe3O4 Dan Fe2O3 Dari Pasir Besi Dengan Kopresipitator. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000007-Undregraduate_thesis.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Pasir besi dapat dijadikan sebagai bahan dasar pembuatan nanokristal Fe3O4 dan Fe2O3. Nanokristal Fe3O4 berhasil disintesis dengan metode kopresipitasi menggunakan kopresipitator semi-otomatis. Kemudian dilanjutkan proses sintering selama 3 jam dengan suhu 600˚C agar diperoleh nanokristal Fe2O3. Variasi yang digunakan pada penelitian ini adalah komposisi pasir besi sebanyak 12, 18, dan 24 gram. Nanokristal Fe3O4 dan Fe2O3 hasil sintesis dikarakterisasi dengan XRD, SEM-EDX, dan VSM. Nanokristal Fe3O4 yang terbentuk memiliki struktur kristal kubik dan orthorombik. Massa Fe3O4 yang dihasilkan berada dalam rentang 7,01 sampai 12,71 gram. Komposisi fasa terbaik dari produk Fe3O4 yaitu 100 %wt yang memiliki rentang ukuran kristal magnetit sebesar 5 – 13 nm. Nanokristal Fe2O3 berhasil diperoleh dari proses sintering nanokristal Fe3O4 pada suhu 600˚C selama 3 jam. Fasa yang terbentuk dari nanokristal Fe2O3 yaitu hematit (α - Fe2O3) dan maghemit (γ - Fe2O3) dengan struktur kristal heksagonal dan tetragonal. Massa produk yang dihasilkan setelah proses sintering berada dalam rentang 3,50 – 7,49 gram. Komposisi fasa terbaik dari sampel hasil sintering yaitu 99,89 %wt fasa hematit, rentang ukuran kristal hematit sebesar 23 – 26 nm. Morfologi nanokristal Fe3O4 dan Fe2O3 berbentuk hampir bulat dengan ukuran partikel (442,56±110,69) dan (505,76±129,56) nm. Sifat magnetik dari nanokristal Fe3O4 dan Fe2O3 masing-masing yaitu ferimagnetik dan superparamagnetik dengan nilai magnetisasi saturasi (Ms) sebesar 8,87 dan 1,54 emu/g, magnetisasi remanen (Mr) sebesar 1,01 dan 0,096 emu/g, serta koersivitas (Hc) sebesar 92,05 dan 115,02 Oe.
===================================================================================================================================
Iron sand can be used as the basic material for the production of Fe3O4 and Fe2O3 nanocrystal. Fe3O4 nanocrystal were successfully synthesized by coprecipitation method using a semi-automatic coprecipitator. Then, the sintering process for 3 hours at a temperature of 600˚C to obtain Fe2O3 nanocrystal. The variation used in this research is the composition of iron sand as much as 12, 18, and 24 gram. The synthesized Fe3O4 and Fe2O3 nanocrystal were characterized by XRD, SEM-EDX, and VSM. The Fe3O4 nanocrystal formed have cubic and orthorhombic crystal structures. The mass of Fe3O4 produced is in the range of 7.01 to 12.71 gram. The best phase composition of Fe3O4 product is 100 %wt which has a magnetite crystal size range of 5 – 13 nm. Fe2O3 nanocrystal were successfully obtained by sintering Fe3O4 nanocrystal at 600˚C for 3 hours. The phases formed from Fe2O3 nanocrystal are hematite (α - Fe2O3) and maghemite (γ - Fe2O3) with hexagonal and tetragonal crystal structures. The mass of the product produced after the sintering process is in the range of 3.50 – 7.49 gram. The best phase composition of the sintered sample is 99.89 %wt hematite phase, hematite crystal size range is 23 – 26 nm. The morphology of Fe3O4 and Fe2O3 nanocrystal is almost spherical with particle sizes (442.56±110.69) and (505.76±129.56) nm, respectively. The magnetic properties of Fe3O4 and Fe2O3 nanocrystal are ferrimagnetic and superparamagnetic, respectively, with saturation magnetization (Ms) of 8.87 and 1.54 emu/g, remanent magnetization (Mr) of 1.01 and 0.096 emu/g, and coercivity (Hc) of 92.05. and 115.02 Oe.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Kopresipitator, Nanokristal Fe2O3, Nanokristal Fe3O4, Pasir besi, Coprecipitator, Iron Sand, Fe2O3 nanocrystal, Fe3O4 nanocrystal
Subjects:	Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	15 Dec 2025 06:35
Last Modified:	15 Dec 2025 06:35
URI:	http://repository.its.ac.id/id/eprint/128971

Actions (login required)

View Item