Analisis Pengaruh Panjang Serat Abaka Pada Komposit Sebagai Absorber Dengan Pendekatan Teori Semi Empiris Delany-Bazley Dan Miki

Abidah, Diva Ayu (2022) Analisis Pengaruh Panjang Serat Abaka Pada Komposit Sebagai Absorber Dengan Pendekatan Teori Semi Empiris Delany-Bazley Dan Miki. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000055-Undregraduate_thesis.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Penelitian ini menganalisis pengaruh variasi panjang serat dengan resin epoxy sebagai pengikatnya yang kemudian dievaluasi terkait sifat makanik dan sifat akustik. Variasi panjang serat yang digunakan 1 mm, 5 mm, 10 mm, 15 mm, dan 20 mm. Karakterisasi yang dilakukan mencakup FTIR, tarik serat tunggal, gravimetri, densitas, dan morfologi. Karakterisasi tersebut dilakukan untuk mengetahui kemampuan mekanik serat serat memodelkan nilai koefisien absorbsi (α) dengan persamaan semi empiris Delany-Bazley dan Miki yang dibandingkan dengan hasil eksperimen menggunakan tabung impedansi. Hasil dari penelitian menunjukkan perlakuan alkalisasi dan hidrolisis pada serat abaka secara efektif meningkatkan kekuatan mekanisnya. Hal ini ditunjukkan dengan Tensile strength meningkat dari 421,39 MPa menjadi 1,11 GPa dan Modulus Young meningkat dari 17,84 GPa menjadi 39,37 GPa. Pengaruh panjang serat abaka pada komposit resin epoxy terhadap nilai koefisien penyerapan bunyi yang signifikan yaitu semakin bertambahnya panjang serat maka nilai koefisien penyerapan bunyi semakin besar di semua frekuensi dan mencapai nilai maksimum pada panjang serat 20 mm dengan nilai α sebesar 0,92 di frekuensi 4000 Hz dan terendah pada panjang serat 1 mm dengan nilai α sebesar 0,45 di frekuensi 500 Hz. Variasi Panjang serat abaka cukup signifikan yaitu semakin panjang serat, semakin besar pula nilai α yang diperoleh. Hal ini dikarenakan panjang serat berpengaruh terhadap terbentuknya porositas, dimana erat kaitannya dengan nilai α. Variasi serat panjang memiliki penyerapan yang tinggi pada frekuensi ≥ 2000 Hz. Adapun nilai α yang diperoleh berturut – turut 0,69; 0,82; 0,85; 0,86; dan 0,89 pada frekuensi 2000Hz. Perbandingan eksperimen dan Model semi empiris (Delany-Bazley dan Miki) nilai α menunjukkan kurva trend yang sama di semua frekuensi dimana nilai α meningkat seiring bertambahnya panjang serat terhadap frekuensi.
===================================================================================================================================
This study analyzed the effect of variations in fiber length with epoxy resin as a binder which was then evaluated for mechanical and acoustic properties. The variation of fiber length used is 1 mm, 5 mm, 10 mm, 15 mm, and 20 mm. Characterizations carried out included FTIR, single fiber tensile, gravimetry, density, and morphology. The characterization was carried out to determine the mechanical ability of the fiber to model the value of the sound absorption coefficient (SAC) with the semi-empirical equation of Delany-Bazley and Miki which was compared with the experimental results using impedance tubes. The results of the study showed that alkalization and hydrolysis treatment of abaca fiber effectively increased its mechanical strength. This is indicated by the Tensile Strength increased from 421.39 MPa to 1.11 GPa and Young's Modulus increased from 17.84 GPa to 39.37 GPa. The effect of abaca fiber length on epoxy resin composites is significant on the SAC value, namely the longer the fiber length, the greater the sound absorption coefficient value at all frequencies and reaches the maximum value at 20 mm fiber length with a SAC value of 0.92 at 4000 Hz frequency and the lowest at 1 mm fiber length with a SAC value of 0.45 at a frequency of 500 Hz. The variation of abaca fiber length is quite significant, namely the longer the fiber, the greater the SAC value. This is because the length of the fiber affects the formation of porosity, which is closely related to the value of SAC. All fiber length variations have high absorption at a frequency of 2000 Hz. The SAC values obtained are 0.69, 0.82, 0.85, 0.86, and 0.89 at a frequency of 2000Hz. Comparison of experimental and semi-empirical models (Delany-Bazley and Miki) SAC values show the same trend curve at all frequencies where the value increases with increasing fiber length along with the frequency.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Koefisien absorbsi bunyi, Material absorber, Model semi empiris Delany-Bazley dan Miki, Serat abaka, Abaca fiber, Absorber material, Delany-Bazley and Miki semi-empirical model Sound absorption coefficient
Subjects:	Q Science > QC Physics Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	16 Dec 2025 12:16
Last Modified:	16 Dec 2025 12:16
URI:	http://repository.its.ac.id/id/eprint/129011

Actions (login required)

View Item