Analisis Pengaruh Temperatur Dan Waktu Sintering Pada Proses Sintesis BaFe10.2Cu0.6Ni0.6Zn0.6O19 Dengan Metode Kopresitipasi Terhadap Sifat Fisik Dan Magnetik

Serafim, Cristin Charis (2026) Analisis Pengaruh Temperatur Dan Waktu Sintering Pada Proses Sintesis BaFe10.2Cu0.6Ni0.6Zn0.6O19 Dengan Metode Kopresitipasi Terhadap Sifat Fisik Dan Magnetik. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011221164-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Barium M-heksaferrit merupakan material magnet permanen yang banyak dikembangkan karena kestabilan struktur kristal serta sifat magnetiknya yang unggul. Modifikasi sifat BaM dapat dilakukan melalui substitusi ion logam (doping) dan pengaturan kondisi sintering. Pada penelitian ini disintesis barium heksaferrit terdoping Cu, Ni, dan Zn dengan komposisi BaFe₁₀.₂Cu₀.₆Ni₀.₆Zn₀.₆O₁₉ menggunakan metode kopresipitasi. Variasi temperatur sintering yang digunakan adalah 890°C, 990°C, dan 1100°C dengan waktu penahanan 2, 3, dan 4 jam. Karakterisasi dilakukan menggunakan X-ray Diffraction untuk menganalisis struktur kristal dan parameter kristalografi, Scanning Electron Microscopy untuk mengamati morfologi, serta Permagraph untuk menentukan sifat magnetik material. Hasil penelitian menunjukkan bahwa variasi temperatur dan waktu penahanan sintering berpengaruh terhadap densifikasi, keteraturan struktur kristal, dan perkembangan mikrostruktur. Semakin tinggi temperatur sintering (890°C-1100°C) maka akan menghasilkan densitas yang lebih tinggi, porositas yang lebih rendah, serta ukuran kristalit yang lebih besar dibandingkan temperatur yang lebih rendah. Variasi waktu penahanan menunjukkan bahwa waktu 3 jam memberikan kondisi densifikasi dan keteraturan struktur yang paling optimum, sedangkan waktu 2 jam belum cukup untuk pemadatan maksimal dan waktu 4 jam cenderung memicu pertumbuhan butir berlebih. Sifat magnetik menunjukkan bahwa nilai koersivitas terendah sebesar 128,18 Oe diperoleh pada temperatur 1100 °C dan waktu 3 jam dengan tidak ada perubahan sifat magnet yang signifikan pada perbedaan waktu. Kombinasi nilai magnetisasi saturassi (33 emu/g) dan remanensi (10,30 emu/g), dengan nilai Mr/Ms 0,31 yang cukup baik, serta koersivitas yang rendah menunjukkan bahwa BaFe₁₀.₂Cu₀.₆Ni₀.₆Zn₀.₆O₁₉ memiliki potensi yang baik untuk diaplikasikan sebagai material penyerap gelombang radar. ================================================================================================================================
Barium M-hexaferrite is a permanent magnetic material that has been widely developed due to its stable crystal structure and excellent magnetic properties. The properties of BaM can be modified through metal ion substitution (doping) and by controlling the sintering conditions. In this study, Cu-, Ni-, and Zn-doped barium hexaferrite with the composition BaFe₁₀.₂Cu₀.₆Ni₀.₆Zn₀.₆O₁₉ was synthesized using the coprecipitation method. The sintering temperatures were 890°C, 990°C, and 1100°C with holding times of 2, 3, and 4 hours. Characterization was carried out using X-ray Diffraction to analyze the crystal structure and crystallographic parameters, Scanning Electron Microscopy to observe the morphology, and Permagraph to determine the magnetic properties of the material. The results show that variations in sintering temperature and holding time affect densification, crystal structure ordering, and microstructure development. Higher sintering temperatures (890°C–1100°C) produce higher density, lower porosity, and larger crystallite size compared to lower temperatures. The variation in holding time shows that 3 hours gives the most optimal densification and crystal structure ordering, while 2 hours is not sufficient for maximum densification and 4 hours tends to cause excessive grain growth. The magnetic properties show that the lowest coercivity value of 128.18 Oe is obtained at a temperature of 1100°C and a holding time of 3 hours, with no significant change in magnetic properties for different holding times. The combination of saturation magnetization (33 emu/g) and remanence (10.30 emu/g), with a fairly good Mr/Ms ratio of 0.31 and low coercivity, indicates that BaFe₁₀.₂Cu₀.₆Ni₀.₆Zn₀.₆O₁₉ has good potential to be applied as a radar wave absorbing material.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Barium heksaferrit, Dopan, Kopresipitasi, Sintering, Magnetik, Barium hexaferrite, Doping, Coprecipitation, Sintering, Magnetic
Subjects:	Q Science > QC Physics > QC765 Magnetic materials U Military Science > U Military Science (General)
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Cristin Charis Serafim
Date Deposited:	23 Jan 2026 02:32
Last Modified:	23 Jan 2026 02:32
URI:	http://repository.its.ac.id/id/eprint/130191